Stretchable conductive fluoroelastomer paste composition
The invention relates to a polymer thick film (PTF) conductive paste composition comprising a conductive powder, a fluoroelastomer, a silane coupling agent, and one or solvents. The PTF conductive paste composition can be used to form a printed conductor and to form an electrically conductive adhesive on various articles. The PTF conductive paste composition is provides a stretchable electrical conductor for wearables.
1. A wearable garment comprising a printed conductor formed from a polymer thick film conductive paste composition wherein the polymer thick film conductive paste composition comprises:
a) 45-65 wt % conductive powder;
b) 10-20 wt % fluoroelastomer;
c) 0.1-3 wt % silane coupling agent;
d) at least one solvent comprising:
(i) 1-35 wt % of one or more solvents selected from the group consisting of 2-(2-ethoxyethoxy)ethyl acetate, diethylene glycol monobutyl ether acetate, ethylene glycol diacetate, and dibasic esters; and
(ii) 1-35 wt % of one or more solvents selected from the group consisting of triethyl phosphate, acetone, 4-methyl-2-pentanone, 2,6-dimethyl-4-heptanone and cyclohexane, wherein the wt % are based on a total weight of the polymer thick film conductive paste composition.
2. The wearable garment of claim 1 , wherein the fluoroelastomer is a vinylidene fluoride containing fluoroelastomer copolymer.
3. The wearable garment of claim 2 , wherein the fluoroelastomer is a terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethlyene.
4. The wearable garment of claim 2 , wherein the fluoroelastomer is a dipolymer of vinylidene fluoride and hexafluoropropylene.
5. The wearable garment of claim 1 , wherein the conductive powder is an electrically conductive powder of one or more of Ag, Cu, Au, Pd, Pt, Sn, Al, Ni, C, alloys thereof and mixtures thereof.
6. The wearable garment of claim 5 , wherein the conductive powder is silver powder.
7. The wearable garment of claim 6 , wherein the silver powder is in the form of silver flakes.
8. The wearable garment of claim 1 , wherein the silane coupling agent is selected from the group consisting of [3-(2,3-epoxypropoxy)propyl] trimethoxysilane (3-glycidyloxypropyltrimethoxysilane), (am inopropyl)trimethoxysilane, (methacryloxypropyl) trimethoxysilane, (vinyl)trimethoxysilane and (mercaptopropyl)trimethoxysilane.
9. The wearable garment of claim 8 , wherein the silane coupling agent is [3-(2,3epoxypropoxy)propyl]trimethoxysilane.
10. The wearable garment of claim 1 , wherein the polymer thick film conductive paste composition comprises 1-35 wt % of 2-(2-ethoxyethoxy) ethyl acetate and 1-35 wt % of triethyl phosphate.
11. The wearable wearable garment of claim 1 , wherein the printed conductor is printed on a substrate which has been subsequently laminated to the garment.
12. The wearable garment of claim 1 , wherein a weight ratio of the at least one solvent to the silane coupling agent is 1:60.
13. The wearable garment of claim 1 , wherein the polymer thick film conductive paste composition comprises 1-35 wt % of 2-(2-ethoxyethoxy) ethyl acetate and less than 5 wt % of triethyl phosphate.
14. The wearable garment of claim 1 , wherein the polymer thick film conductive paste composition consists essentially of:
a) 45-65 wt % conductive powder;
b) 10-20 wt % fluoroelastomer;
c) 0.1-3 wt % silane coupling agent comprising [3-(2,3epoxypropoxy)propyl]trimethoxysilane;
d) 1-35 wt % 2-(2-ethoxyethoxy)ethyl acetate; and
e) 1-35 wt % of triethyl phosphate, wherein the wt % are based on the total weight of the polymer thick film conductive paste composition.
15. The wearable garment of claim 1 , wherein the at least one solvent is added such that the composition has a viscosity of between 30-90 Pa·S.