Particle size control of metallocene catalyst systems in loop slurry polymerization reactors
Catalyst compositions containing a metallocene compound, a solid activator, and a co-catalyst, in which the solid activator or the supported metallocene catalyst has a d50 average particle size of 15 to 50 μm and a particle size distribution of 0.5 to 1.5, can be contacted with an olefin in a loop slurry reactor to produce an olefin polymer. A representative ethylene-based polymer produced using the catalyst composition has excellent dart impact strength and low gels, and can be characterized by a HLMI from 4 to 10 g/10 min, a density from 0.944 to 0.955 g/cm 3 , a higher molecular weight component with a Mn from 280,000 to 440,000 g/mol, and a lower molecular weight component with a Mw from 30,000 to 45,000 g/mol and a ratio of Mz/Mw ranging from 2.3 to 3.4.
1. A catalyst composition comprising:
a metallocene compound;
a solid activator comprising a fluorided solid oxide and/or a sulfated solid oxide; and
optionally, a co-catalyst;
wherein the solid activator has:
a d50 average particle size in a range from 15 to 50 μm; and
a particle size span in a range from 0.5 to 1.5.
2. The catalyst composition of claim 1 , wherein:
the d50 average particle size is from 17 to 27 μm; and
the span is from 0.6 to 1.1.
3. The catalyst composition of claim 1 , wherein the solid activator has:
a d10 particle size from 10 to 18 μm;
a d95 particle size from 25 to 65 μm; and
a ratio of d90/d10 from 1.5 to 5.
4. The catalyst composition of claim 1 , wherein the solid activator has a ratio of d90/d10 from 1.8 to 3.
5. The catalyst composition of claim 1 , wherein an amount of the solid activator having:
a particle size of less than 10 μm is less than or equal to 5 wt %; and
a particle size of greater than 45 μm is less than or equal to 10 wt %.
6. The catalyst composition of claim 1 , wherein an amount of the solid activator having a particle size of less than 50 μm is at least 90 wt %.
7. The catalyst composition of claim 1 , wherein the catalyst composition:
comprises an organoaluminum co-catalyst; and
is substantially free of aluminoxane compounds, organoboron or organoborate compounds, ionizing ionic compounds, or combinations thereof.
8. The catalyst composition of claim 1 , wherein the catalyst composition comprises a single metallocene compound.
9. The catalyst composition of claim 1 , wherein the catalyst composition comprises two metallocene compounds.
10. The catalyst composition of claim 9 , wherein the two metallocene compounds are a bridged metallocene compound and an unbridged metallocene compound.
11. A polymerization process comprising:
contacting the catalyst composition of claim 1 with an olefin monomer and an optional olefin comonomer in a polymerization reactor system comprising a loop slurry reactor under polymerization conditions to produce an olefin polymer.
12. The process of claim 11 , wherein the catalyst composition is contacted with ethylene and an olefin comonomer comprising 1-butene, 1-hexene, 1-octene, or a mixture thereof.
13. The process of claim 12 , wherein the polymerization reactor system comprises only one loop slurry reactor or the loop slurry reactor and one additional reactor.
14. The process of claim 11 , wherein the olefin polymer comprises an ethylene homopolymer, an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, and/or an ethylene/1-octene copolymer.
15. The process of claim 14 , wherein the catalyst composition comprises an organoaluminum co-catalyst.
16. A catalyst composition comprising:
a metallocene compound;
a solid activator comprising fluorided alumina, sulfated alumina, fluorided silica-alumina, sulfated silica-alumina, fluorided silica-coated alumina, fluorided-chlorided silica-coated alumina, sulfated silica-coated alumina, or any combination thereof; and
an organoaluminum co-catalyst;
wherein the solid activator has:
a d50 average particle size in a range from 15 to 50 μm; and
a particle size span in a range from 0.5 to 1.5.
17. The catalyst composition of claim 16 , wherein:
the d50 average particle size is from 17 to 40 μm; and
the span is from 0.6 to 1.3.
18. The catalyst composition of claim 16 , wherein the solid activator has:
a d10 particle size from 10 to 20 μm;
a d95 particle size of less than or equal to 65 μm; and
a ratio of d90/d10 from 1.5 to 5.
19. The catalyst composition of claim 16 , wherein an amount of the solid activator having:
a particle size of less than 10 μm is less than or equal to 8 wt %;
a particle size of greater than 45 μm is less than or equal to 20 wt %; and
a particle size of less than 50 μm is at least 85 wt %.
20. The catalyst composition of claim 16 , wherein the catalyst composition:
is substantially free of aluminoxane compounds, organoboron or organoborate compounds, ionizing ionic compounds, or combinations thereof; and
comprises a single metallocene compound or two metallocene compounds at a weight ratio in a range from 10:1 to 1:10.
21. A polymerization process comprising:
contacting the catalyst composition of claim 16 with an olefin monomer and an optional olefin comonomer in a polymerization reactor system comprising a loop slurry reactor under polymerization conditions to produce an olefin polymer.
22. The process of claim 21 , wherein:
the catalyst composition is contacted with ethylene and an olefin comonomer comprising 1-butene, 1-hexene, 1-octene, or a mixture thereof.
23. The process of claim 22 , wherein the polymerization reactor system comprises only one loop slurry reactor or the loop slurry reactor and one additional reactor.
24. The process of claim 21 , wherein the olefin polymer comprises an ethylene homopolymer, an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, and/or an ethylene/1-octene copolymer.
25. The process of claim 24 , wherein the polymerization reactor system comprises only one loop slurry reactor.
26. The process of claim 24 , wherein:
the catalyst composition is substantially free of aluminoxane compounds, organoboron or organoborate compounds, ionizing ionic compounds, or combinations thereof.