Photo-crosslinkable pressure-sensitive adhesive and use thereof
Provided is a photo-crosslinkable PSA comprising a polymer having side-chain benzophenone structures. The photo-crosslinkable PSA is a cured product of a PSA composition comprising an ethylenically unsaturated compound and a benzophenone structure-containing component. The photo-crosslinkable PSA has VOC emissions of 500 μg/g or less. Also provided is a PSA sheet having a PSA layer formed from the photo-crosslinkable PSA.
1 . A photo-crosslinkable pressure-sensitive adhesive
being formed from a pressure-sensitive adhesive composition comprising an ethylenically unsaturated compound and a polymer having side-chain benzophenone structures, and
comprising a polymer having unreacted side-chain benzophenone structures, wherein the pressure-sensitive adhesive composition comprises, as the ethylenically unsaturated compound, a compound having one ethylenically unsaturated group,
wherein, of the entire monomers forming the pressure-sensitive adhesive composition, a compound having two or more ethylenically unsaturated groups has a weight fraction of 1% by weight or lower.
2 . The photo-crosslinkable pressure-sensitive adhesive according to claim 1 , wherein the photo-crosslinkable pressure-sensitive adhesive has a shear storage modulus at 80° C., Gb′ (kPa) and its photo-crosslinked product has a shear storage modulus at 80° C., Gc′ (kPa), satisfying the next relationship Gc′ (kPa)−Gb′ (kPa) ≥2 kPa, with the photo-crosslinked product obtained by UV-irradiating the photo-crosslinkable pressure-sensitive adhesive at a dose of 300 mW/cm 2 to a cumulative dose of 10000 mJ/cm 2 using a high-pressure mercury lamp.
3 . The photo-crosslinkable pressure-sensitive adhesive according to claim 1 , having a shear storage modulus at 80° C., Gc′ (kPa), of 40 kPa or higher, determined with its photo-crosslinked product obtained by UV-irradiating the photo-crosslinkable pressure-sensitive adhesive at a dose of 300 mW/cm 2 to a cumulative dose of 10000 mJ/cm 2 using a high-pressure mercury lamp.
4 . The photo-crosslinkable pressure-sensitive adhesive according to claim 1 , wherein the pressure-sensitive adhesive composition further comprises an organic solvent in an amount of 0.05% by weight to 30% by weight among the components of the pressure-sensitive adhesive composition.
5 . A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer formed from the photo-crosslinkable pressure-sensitive adhesive according to claim 1 .
6 . The pressure-sensitive adhesive sheet according to claim 5 , having a peel strength of 1.0 N/10 mm or greater, determined by the following procedure:
[procedure for measuring peel strength]
the surface of the pressure-sensitive adhesive layer is press-bonded to a glass plate with a 2 kg rubber roller moved back and forth once; the resultant is autoclaved (50° C., 0.5 MPa, 15 min) and then UV-irradiated at a dose of 300 mW/cm 2 to a cumulative dose of 10000 mJ/cm 2 using a high-pressure mercury lamp; subsequently, in the atmosphere at 25° C., at a tensile speed of 300 mm/min at a peel angle of 180°, while the pressure-sensitive adhesive sheet is peeled from the glass plate, the peel strength is measured.
7 . A method for producing a laminate, the method comprising the following steps in the following order:
laminating a member and the photo-crosslinkable pressure-sensitive adhesive according to claim 1 , and
allowing reaction of the benzophenone structures to cause photo-crosslinking of the photo-crosslinkable pressure-sensitive adhesive.
8 . A method for producing a photo-crosslinkable pressure-sensitive adhesive, the method comprising
obtaining a pressure-sensitive adhesive composition comprising a polymer (A) having side-chain benzophenone structures, an ethylenically unsaturated compound (B), and a photoinitiator (C) that absorbs 300 nm to 500 nm wavelength light to generate radicals; and
irradiating the pressure-sensitive adhesive composition with active energy rays;
wherein the pressure-sensitive adhesive composition comprises, as the ethylenically unsaturated compound (B), a compound (B1) having one ethylenically unsaturated group,
wherein, of the entire monomers forming the pressure-sensitive adhesive composition, a compound having two or more ethylenically unsaturated groups has a weight fraction of 1% by weight or lower, and
wherein the active energy rays are irradiated to allow reaction of the ethylenically unsaturated group of the ethylenically unsaturated compound (B) while allowing the benzophenone structures of the polymer (A) to remain.
9 . A pressure-sensitive adhesive composition used for producing a photo-crosslinkable pressure-sensitive adhesive comprising a polymer having benzophenone structures in side chains, the pressure-sensitive adhesive composition comprising
a polymer (A) having benzophenone structures in side chains,
an ethylenically unsaturated compound (B), and
a photoinitiator (C) that absorbs 300 nm to 500 nm wavelength light to generate radicals;
wherein the pressure-sensitive adhesive composition comprises, as the ethylenically unsaturated compound (B), a compound (B1) having one ethylenically unsaturated group, and
wherein, of the entire monomers forming the pressure-sensitive adhesive composition, a compound having two or more ethylenically unsaturated groups has a weight fraction of 1% by weight or lower below 5% by weight.
10 . The pressure-sensitive adhesive composition according to claim 9 , further comprising an organic solvent in an amount of 0.05% by weight to 30% by weight among the components of the pressure-sensitive adhesive composition.