IP Library Granted Patent US 12,469,851
Granted Patent B2
US 12,469,851 · App. 17/709,156 · Granted Nov 11, 2025

Anode protective layer for lithium-sulfur cells

Inventors: Elena Rogojina (San Jose, CA); Jerzy Gazda (Austin, TX); You Li (Sunnyvale, CA); Jesse Baucom (Sunnyvale, CA); Chandra B. KC (San Jose, CA); Jingning Shan (San Jose, CA); Ratnakumar Bugga (Arcadia, CA)
Assignee: Lyten, Inc.
H01M4/62H01M4/13H01M10/052H01M2004/027H01M2300/0065
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,469,851
App. No.
17/709,156
Granted
Nov 11, 2025
Kind
B2
Abstract

A lithium-sulfur battery may include a cathode, an anode structure positioned opposite to the cathode, a separator, and an electrolyte. In some instances, the anode structure may include an artificial solid-electrolyte interphase (A-SEI) that may form on and within the anode structure. A protective layer may form within and on the A-SEI, and may include exposed carbon surfaces formed by coalescence of several wrinkled graphene nanoplatelets with one another. Metal-containing substances may be decorated on and/or attached with at least some exposed carbon surfaces and regulate flow of lithium (Li + ) cations within the lithium-sulfur battery and correspondingly moderate one or more of a plating rate or a de-plating rate of lithium onto the anode structure. The separator may be positioned between the anode structure and the cathode. The electrolyte may be dispersed throughout the cathode and in contact with the anode structure.

Claims (58)

1 . A lithium-sulfur battery comprising:

a cathode;

an anode structure positioned opposite to the cathode, the anode structure comprising:

an artificial solid-electrolyte interphase;

a protective layer at least partially formed on and within the artificial solid-electrolyte interphase, the protective layer comprising:

a plurality of exposed carbon surfaces formed by a coalescence of wrinkled graphene nanoplatelets with one another; and

one or more metal-containing substances decorated on or attached with one or more exposed carbon surfaces, the one or more metal-containing substances configured to adjust one or more of a plating rate of lithium onto the anode structure or a de-plating rate of lithium from the anode structure by regulating a flow of lithium (Li + ) cations within the lithium-sulfur battery;

a separator positioned between the anode structure and the cathode; and

an electrolyte dispersed throughout the cathode and in contact with the anode structure.

2 . The lithium-sulfur battery of claim 1 , wherein the anode structure further comprises one or more of a cavity, a foil of lithium, or a lithium-containing substance configured to receive lithium from the cathode during operational discharge-charge cycling of the lithium-sulfur battery.

3 . The lithium-sulfur battery of claim 1 , wherein the protective layer has a cross-linking density configured to swell between 10%-50% by controlling absorption of at least some solvents contained in the electrolyte.

4 . The lithium-sulfur battery of claim 1 , wherein the protective layer has a cross-linking density configured to swell no more than 10% by preventing absorption of one or more solvents in the electrolyte.

5 . The lithium-sulfur battery of claim 1 , wherein the protective layer further comprises a first polymeric chain and a second polymeric chain positioned opposite one another.

6 . The lithium-sulfur battery of claim 5 , wherein the protective layer further comprises a lithium fluoride (LiF) layer based on a combination of lithium cations (Li + ) output from the anode structure and fluorine anions (F) grafted onto the first polymeric chain or the second polymeric chain.

7 . The lithium-sulfur battery of claim 5 , wherein the first polymeric chain is formed from a first plurality of interconnected monomer units, and the second polymeric chain is formed from a second plurality of interconnected monomer units.

8 . The lithium-sulfur battery of claim 7 , wherein the first plurality of interconnected monomer units and the second plurality of interconnected monomer units are identical to one another.

9 . The lithium-sulfur battery of claim 7 , wherein the first plurality of interconnected monomer units and the second plurality of interconnected monomer units are distinct from one other.

10 . The lithium-sulfur battery of claim 5 , wherein the first polymeric chain and the second polymeric chain are configured to cross-link with each other based on exposure to one or more nitrogen-containing groups cured in an epoxy.

11 . The lithium-sulfur battery of claim 5 , wherein the first polymeric chain and the second polymeric chain each comprise exposed carbon atoms grafted to one or more of oxide anions (O 2− ), fluorine anions (F − ), or nitrate anions (NO 3 − ) uniformly dispersed throughout the protective layer.

12 . The lithium-sulfur battery of claim 5 , wherein each of the first polymeric chain and the second polymeric chain is configured to form carbon-carbon bonds with one another responsive to exposure to an energy provided by an energetic environment.

13 . The lithium-sulfur battery of claim 5 , wherein each of the first polymeric chain and the second polymeric chain each is configured to at least partially cross-link with one another responsive to exposure to an energy provided by an energetic environment.

14 . The lithium-sulfur battery of claim 13 , wherein the energy is an ultraviolet (UV) energy.

15 . The lithium-sulfur battery of claim 13 , wherein the energy is a thermal energy.

16 . The lithium-sulfur battery of claim 13 , wherein the cross-linked first and second polymeric chains are configured to form the protective layer as a three-dimensional lattice having a cross-linking density defined by a number of cross-link points per-unit volume.

17 . The lithium-sulfur battery of claim 16 , wherein the number of cross-link points per-unit volume are configured to restrict re-dissolution of lithium-containing additives in the protective layer toward the electrolyte.

18 . The lithium-sulfur battery of claim 16 , wherein the three-dimensional lattice is configured to at least partially trap TFSI − anions produced upon dissociation of LiTFSI.

19 . The lithium-sulfur battery of claim 5 , wherein the first polymeric chain and the second polymeric chain are configured to form the protective layer by participating in one or more cross-linking polymerization reactions with each other responsive to exposure to one or more cationic photo initiators.

20 . The lithium-sulfur battery of claim 19 , wherein the one or more cross-linking polymerization reactions includes ring-opening polymerization (ROP).

21 . The lithium-sulfur battery of claim 5 , wherein the first polymeric chain or the second polymeric chain includes one or more of liquid bisphenol A epichlorohydrin-based epoxy resin or polyoxyethylene bis(glycidyl ether) having an average M n of 500 (PEG-DEG-500).

22 . The lithium-sulfur battery of claim 21 , wherein the protective layer comprises:

between 2 wt. %-5 wt. %; of difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin;

between 15 wt. %-25 wt. % of polyoxyethylene bis(glycidyl ether) (PEG-DEG-500) having an average M n of 500;

between 20 wt. %-25 wt. % of diaminopolypropylene glycol;

between 5 wt. %-15 wt. % of poly(propylene glycol) bis(2-aminopropyl ether);

between 5 wt. %-15 wt. % of lithium bis(trifluoromethanesulfonyl)imide (LiTFSI); and

between 40 wt. %-60 wt. % of lithium lanthanum zirconium oxide (LLZO).

23 . The lithium-sulfur battery of claim 1 , wherein the protective layer further comprises one or more lithium-containing salts including at least lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) dispersed throughout the protective layer and configured to dissociate into lithium (Li + ) cations and TFSI − anions.

24 . The lithium-sulfur battery of claim 1 , wherein the protective layer is devoid of pinholes.

25 . The lithium-sulfur battery of claim 1 , wherein the electrolyte comprises one or more solvents including dimethoxyethane (DME).

26 . The lithium-sulfur battery of claim 1 , wherein the protective layer has a modulus of elasticity between 3 gigapascals (GPa) and 100 GPa.

27 . The lithium-sulfur battery of claim 1 , wherein the protective layer has a glass transition temperature of between 60° C. and 81° C.

28 . The lithium-sulfur battery of claim 1 , wherein at least some lithium cations (Li + ) are involved in one or more of a dissociation reaction or a combination reaction during operational discharge cycling of the lithium-sulfur battery.

29 . The lithium-sulfur battery of claim 1 , wherein the protective layer further comprises a layer of lithium fluoride (LiF) formed responsive to a combination of fluorine anions (F−) and lithium cations (Li + ).

30 . The lithium-sulfur battery of claim 29 , wherein the combination of fluorine anions (F−) and lithium cations (Li + ) is associated with generation of a lithium oxide (Li 2 O), a lithium nitrate (LiNO 3 ) or a plurality of nitrogen-oxygen containing compounds.

31 . The lithium-sulfur battery of claim 30 , wherein one or more of the lithium fluoride (LiF), the lithium oxide (Li 2 O), the lithium nitrate (LiNO 3 ), or the plurality of nitrogen-oxygen containing additives form one or more regions extending across one or more of the anode structure or the artificial solid-electrolyte interphase.

32 . The lithium-sulfur battery of claim 1 , wherein the protective layer further comprises one or more of lithium lanthanum zirconium oxide (LLZO), NASICON-type oxide Li 1+x Al x Ti 2−x (PO 4 ) 3 (LATP) or lithium tin phosphorus sulfide (LSPS).

33 . The lithium-sulfur battery of claim 32 , wherein at least some of the plurality of additives dispersed throughout the protective layer are configured to dissociate and produce a plurality of lithium cations (Li + ).

34 . The lithium-sulfur battery of claim 33 , wherein a presence of at least some of the plurality of additives within the protective layer is configured to increase one or more of a charging rate, a discharging rate, or an energy density of the lithium-sulfur battery.

35 . The lithium-sulfur battery of claim 1 , wherein the protective layer comprises:

between 2 wt. %-5 wt. % of difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin;

between 15 wt. %-25 wt. % of polyoxyethylene bis(glycidyl ether) having an average M n of 500;

between 5 wt. %-15 wt. % of 3,4-epoxy cyclohexyl methyl-3,4-epoxy cyclohexane carboxylate (ECC);

between 15 wt. %-20 wt. % of lithium bis(trifluoromethanesulfonyl)imide (LiTFSI);

between 40 wt. %-60 wt. % of lithium lanthanum zirconium oxide (LLZO); and

between 1 wt. %-5 wt. % of diphenyliodonium hexafluorophosphate (DPIHFP).

36 . The lithium-sulfur battery of claim 1 , wherein the protective layer is coated or deposited onto the anode structure by a roll-to-roll apparatus.

37 . The lithium-sulfur battery of claim 1 , wherein the protective layer is spray coated, gravure coated, micro gravure coated, slot-die coated, doctor-blade coated, Mayer's rod spiral-coated onto the anode structure.

38 . The lithium-sulfur battery of claim 1 , wherein the artificial solid-electrolyte interphase is configured to form one or more compounds on the anode structure based on one or more oxidation-reduction reactions involving lithium cations (Li + ) and one or more solvents.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Apr 6, 2022
From: ROGOJINA, ELENA; GAZDA, JERZY; LI, YOU; BAUCOM, JESSE; KC, CHANDRA B.; SHAN, JINGNING; BUGGA, RATNAKUMAR
To: LYTEN, INC.
Reel/Frame 059515/0887 →
Continuity (10)
Continuation In Part 17694407 · Mar 14, 2022
Continuation In Part 17672960 · Feb 16, 2022
Continuation In Part 17666753 · Feb 8, 2022
Continuation In Part 17584666 · Jan 26, 2022
Continuation In Part 17578240 · Jan 18, 2022
Continuation In Part 17563183 · Dec 28, 2021
Continuation In Part 17383803 · Jul 23, 2021
Provisional Application 63235892 · Aug 23, 2021
Provisional Application 63169754 · Apr 1, 2021
Related Publication 20220320515A1 · Oct 6, 2022
References Cited (113)
US 5595837A · Olsen et al. · 1997 [cited by applicant]
US 6060184A · Gan et al. · 2000 [cited by applicant]
US 6136477A · Gan et al. · 2000 [cited by applicant]
US 6210839B1 · Gan et al. · 2001 [cited by applicant]
US 6955866B2 · Nimon et al. · 2005 [cited by applicant]
US 7354680B2 · Mikhaylik · 2008 [cited by applicant]
US 7745047B2 · Zhamu et al. · 2010 [cited by applicant]
US 7842421B2 · Mikhaylik · 2010 [cited by applicant]
US 8119288B2 · Zhamu et al. · 2012 [cited by applicant]
US 8241793B2 · Zhamu et al. · 2012 [cited by applicant]
US 8415054B2 · Skotheim et al. · 2013 [cited by applicant]
US 8617748B2 · Mikhaylik et al. · 2013 [cited by applicant]
US 8748043B2 · Mikhaylik · 2014 [cited by applicant]
US 8936870B2 · Affinito et al. · 2015 [cited by applicant]
US 8968924B2 · Bosnyak et al. · 2015 [cited by applicant]
US 9005809B2 · Wilkening et al. · 2015 [cited by applicant]
US 9034421B2 · Mikhaylik et al. · 2015 [cited by applicant]
US 9040201B2 · Affinito et al. · 2015 [cited by applicant]
US 9171679B2 · Gogotsi et al. · 2015 [cited by applicant]
US 9190667B2 · Zhamu et al. · 2015 [cited by applicant]
US 9419274B2 · Wilkening et al. · 2016 [cited by applicant]
US 9437344B2 · Zhamu et al. · 2016 [cited by applicant]
US 9577243B2 · Schmidt et al. · 2017 [cited by applicant]
US 9666899B2 · He et al. · 2017 [cited by applicant]
US 9994960B2 · Laramie et al. · 2018 [cited by applicant]
US 10530011B1 · MacKenzie et al. · 2020 [cited by applicant]
US 10734653B2 · Lanning et al. · 2020 [cited by applicant]
US 10862129B2 · Pan et al. · 2020 [cited by applicant]
US 10998552B2 · Lanning et al. · 2021 [cited by applicant]
US 20050042515A1 · Hwang · 2005 [cited by examiner]
US 20090208836A1 · Fuhr et al. · 2009 [cited by applicant]
US 20100190056A1 · Turner et al. · 2010 [cited by applicant]
US 20100330423A1 · Cui et al. · 2010 [cited by applicant]
US 20110052966A1 · Lampe-Onnerud · 2011 [cited by applicant]
US 20110165466A1 · Zhamu et al. · 2011 [cited by applicant]
US 20130141050A1 · Visco et al. · 2013 [cited by applicant]
US 20140023936A1 · Belharouak et al. · 2014 [cited by applicant]
US 20140057179A1 · Yushin et al. · 2014 [cited by applicant]
US 20140315100A1 · Wang et al. · 2014 [cited by applicant]
US 20140342209A1 · He et al. · 2014 [cited by applicant]
US 20150155549A1 · Moganty · 2015 [cited by examiner]
US 20150188106A1 · Takeshi et al. · 2015 [cited by applicant]
US 20150349380A1 · Manthiram et al. · 2015 [cited by applicant]
US 20160028063A1 · Visco · 2016 [cited by examiner]
US 20160093916A1 · Moon et al. · 2016 [cited by applicant]
US 20160104882A1 · Yushin · 2016 [cited by examiner]
US 20160164102A1 · Moganty · 2016 [cited by examiner]
US 20160248084A1 · Cairns et al. · 2016 [cited by applicant]
US 20160294000A1 · He et al. · 2016 [cited by applicant]
US 20160336615A1 · Thillaiyan · 2016 [cited by examiner]
US 20170033406A1 · Zhang et al. · 2017 [cited by applicant]
US 20170077490A1 · Zhang et al. · 2017 [cited by applicant]
US 20170092950A1 · Xiao et al. · 2017 [cited by applicant]
US 20170207484A1 · Zhamu et al. · 2017 [cited by applicant]
US 20170324097A1 · Lee · 2017 [cited by examiner]
US 20170331150A1 · Park et al. · 2017 [cited by applicant]
US 20180019471A1 · Wu et al. · 2018 [cited by applicant]
US 20180233784A1 · Zhamu et al. · 2018 [cited by applicant]
US 20180251681A1 · Zhang · 2018 [cited by examiner]
US 20190097270A1 · Park et al. · 2019 [cited by applicant]
US 20190123390A1 · Xu · 2019 [cited by examiner]
US 20190348672A1 · Wang · 2019 [cited by examiner]
US 20190348719A1 · Batson et al. · 2019 [cited by applicant]
US 20190393541A1 · Jang · 2019 [cited by examiner]
US 20200052325A1 · Zhamu et al. · 2020 [cited by applicant]
US 20200161706A1 · Cao · 2020 [cited by examiner]
US 20200287245A1 · Ryu · 2020 [cited by examiner]
US 20210013550A1 · Wang et al. · 2021 [cited by applicant]
US 20210057751A1 · Lanning et al. · 2021 [cited by applicant]
US 20210057753A1 · Viner et al. · 2021 [cited by applicant]
US 20210066687A1 · Que et al. · 2021 [cited by applicant]
US 20210167399A1 · Hu · 2021 [cited by applicant]
US 20210210753A1 · Gazda et al. · 2021 [cited by applicant]
US 20210336251A1 · Venkatachalam et al. · 2021 [cited by applicant]
US 20210359305A1 · Rogojina · 2021 [cited by examiner]
US 20220263111A1 · Li · 2022 [cited by examiner]
US 20220376253A1 · Kim · 2022 [cited by examiner]
CA 2032137A · 1990 [cited by applicant]
CN 100541870A · 2009 [cited by applicant]
CN 101997120A · 2011 [cited by applicant]
EP 3340346A1 · 2018 [cited by applicant]
JP 2010095390A · 2010 [cited by applicant]
JP 2016532566A · 2016 [cited by applicant]
JP 2020194792A · 2020 [cited by applicant]
KR 101785064B1 · 2017 [cited by applicant]
WO 2014048390A1 · 2014 [cited by applicant]
WO 2015058057A1 · 2015 [cited by applicant]
WO 2015084945A1 · 2015 [cited by applicant]
WO 2016027583A1 · 2016 [cited by applicant]
WO 2016061216A1 · 2016 [cited by applicant]
WO 2016201101A1 · 2016 [cited by applicant]
WO 2017127674A1 · 2017 [cited by applicant]
International Search Report and Written Opinion dated Mar. 14, 2023, for PCT Appl. No. PCT/US2022/037905; 17 pages. [cited by applicant]
International Search Report and Written Opinion dated Jul. 18, 2022, for PCT Application No. PCT/US2022/022755; 11 pages. [cited by applicant]
Shi, Jia-Le et al.; “Template growth of porous graphene microspheres on layered double oxide catalysts and their applications in lithium-sulfur batteries”, Carbon, vol. 92; Mar. 17, 2015; pp. 96-105. [cited by applicant]
Wang, J., et al., “Self-assembly of Fe2O3 nanotubes on graphene as an anode material for lithium ion batteries”, Journal of Alloys and Compounds; vol. 750; Apr. 9, 2018; pp. 871-877. [cited by applicant]
Song, Y. et al., “Macro-Sized All-Graphene 3D Structures via Layer-by-Layer Covalent Growth for Micro-to-Macro Inheritable Electrical Performances”, Advanced Functional Materials, No. 202305191; Jun. 19, 2023; Abstract. [cited by applicant]
Sun, K. et al., “Metal Nanoclusters as a Superior Polysulfides Immobilizer toward Highly Stable Lithium-Sulfur Batteries”, Small, No. 2304210, Published by Wiley-VCH GmbH; Aug. 25, 2023; 11 pages. [cited by applicant]
Choudhury et al.; “Carbon onion-sulfur hybrid cathodes for lithium-sulfur batteries”, Sustainable Energy Fuels; vol. 1; pp. 84-94; Jan. 2017. [cited by applicant]
Final Report Summary—LISSEN (Lithium Sulfur Superbattery Exploitating Nanotechnology), CORDIS, Record No. 181634; Apr. 4, 2016. [cited by applicant]
Gao, Y. et al., “Polymer-inorganic solid-electrolyte interphase for stable lithium metal batteries under lean electrolyte conditions”, Nature Materials; vol. 18, No. 4; Mar. 11, 2019; pp. 384-389. [cited by applicant]
International Search Report and Written Opinion dated May 28, 2018 for PCT Patent Application Serial No. PCT/US2018/019772. [cited by applicant]
International Search Report and Written Opinion dated Aug. 7, 2019, for PCT Patent Application Serial No. PCT/US2019/029445; 10 pages. [cited by applicant]
Kang, H. et al., “Thirty-minute synthesis of hierarchically ordered sulfur particles enables high-energy, flexible lithium-sulfur batteries”, Nano Energy, vol. 89; Aug. 25, 2021; 10 pages. [cited by applicant]
Lu, H. et al., “Application of Partially Fluorinated Ether for Improving Performance of Lithium/Sulfur Batteries”, Journal of the Electrochemical Society; vol. 162, No. 8; May 12, 2015; pp. A1460-A1465. [cited by applicant]
Lu, Z. et al.; “Improving Li anode performance by a porous 3D carbon paper host with plasma assisted sponge carbon coating”; Energy Storage Materials; vol. 11; pp. 47-56; 2018. [cited by applicant]
Meini et al., “The Use of Redox Mediators for Enhancing Utilization of Li2S Cathodes for Advanced Li-S Battery Systems”, J. Phys. Chem. Lett.; vol. 5; pp. 915-918; Feb. 2014. [cited by applicant]
Park, J. et al., “Formation of Stable Solid-Electrolyte Interphase Layter on Few-Layer Graphene-Coated Silicon Nanoparticles for High-Capacity Li-Ion Battery Anodes”, The Journal of Physical Chemistry C, vol. 121; pp. 2… [cited by applicant]
Son, I. et al., “Graphene balls for lithium rechargeable batteries with fast charging and high volumetric energy densities”, Nature Communications; 8(1); pp. 1-11; Nov. 16, 2017. [cited by applicant]
Zeng, F. et al., “Enhanced Li-S batteries using cation-functionalized pigment nanocarbon in core-shell structured composite cathodes”, J. Mater. Chem. A, vol. 5, 2017; pp. 5559-5567. [cited by applicant]
Zhang, S.; “Liquid electrolyte lithium/sulfur battery: Fundamental chemistry, problems, and solutions”; Science Direct. Journal of Power Sources; vol. 231; pp. 153-162; Jun. 1, 2013. [cited by applicant]
Zhou, H. et al., “Protective coatings for lithium metal anodes: Recent progress and future perspectives”, Journal of Power Sources; vol. 450; Jan. 2020; 18 pages. [cited by applicant]
Diez, N. et al., “Dense (Non-Hollow) Carbon Nanospheres: Synthesis and Electrochemical Energy Applications”, Materials Today Nano; vol. 16; No. 100147; Oct. 6, 2021; 32 pages. [cited by applicant]