The present disclosure relates to a laminate film including a water resistant or oxygen resistant base layer, and co-extrusion layer. The co-extrusion layer may include a tie layer and a contact layer, and the contact layer may include a polymer such as cyclic olefin copolymer, a polyamide, or an ethylene vinyl alcohol. A total loading of the tie layer may be in the range of 3-9 g/m 2 and wherein a loading of the contact layer is: loading contact =x*loading tie , wherein loading contact is the loading of the contact layer, loading tie is the total loading of the tie layer, and x is in the range of 0.8 to 3.
1. A packaging for packing a composition, comprising:
a first outer layer made of a mechanically wear-resistant material;
an aggressive chemical-resistant laminate film comprising a base layer and a coextrusion layer, wherein:
the base layer is one or more of water-resistant or oxygen-resistant;
the coextrusion layer comprises a tie layer and a contact layer, wherein the contact layer comprises a polymer selected from the group consisting of: a polyamide, an ethylene vinyl alcohol, or any combination thereof, and wherein a total loading of the tie layer is between 3 g/m 2 and 9 g/m 2 and a loading of the contact layer is equal to x times the total loading of the tie layer, wherein x is in a range of 1 to 3, and
the base layer side of the film faces the first outer layer;
wherein the aggressive chemical-resistant laminate film is resistant to a chemical selected from nicotine, fentanyl, rivastigmine, or lidocaine.
2. The packaging of claim 1 , wherein the aggressive chemical-resistant laminate film encloses the composition.
3. The packaging of claim 1 , wherein the base layer is selected from aluminum, polyvinylidene chloride, a silicon oxide-coated polyester, an aluminum oxide-coated polyester, an aluminum oxide polyethylene terephthalate-coated (PET) film, a silicon oxide-coated PET film, or any combination thereof.
4. The packaging of claim 1 , wherein the composition is a patch.
5. The packaging of claim 1 , wherein the composition is in a liquid state.
6. A method for providing an aggressive chemical-resistant laminate film, comprising:
providing a base layer, wherein the base layer is one or more of water-resistant or oxygen-resistant;
coextruding a tie layer and a contact layer to provide a coextrusion layer;
coating the coextrusion layer to the base layer; and
curing the coextrusion layer coated to the base layer, wherein:
the contact layer comprises a polymer selected from the group consisting of: a polyamide, an ethylene vinyl alcohol, or any combination thereof, and
a total loading of the tie layer is between 3 g/m 2 and 9 g/m 2 and a loading of the contact layer is equal to x times the total loading of the tie layer, wherein x is in a range of 1 to 3;
wherein the aggressive chemical-resistant laminate film is resistant to a chemical selected from nicotine, fentanyl, rivastigmine, or lidocaine.
7. The method of claim 6 , wherein:
the tie layer comprises a plurality of layers,
each layer of the plurality of layers of the tie layer are coextruded with the contact layer.
8. The method of claim 6 , wherein the tie layer and the contact layer are coextruded at a temperature between 240° C. and 330° C.
9. The method of claim 6 , wherein the base layer is selected from aluminum, polyvinylidene chloride, a silicon oxide coated polyester, an aluminum oxide coated polyester, an aluminum oxide polyethylene terephthalate (PET) film, a silicon oxide coated PET film, or any combination thereof.
10. A method for providing a packaging for packing a compound or a composition, comprising:
providing a first outer layer made of a mechanically wear-resistant material;
providing an aggressive chemical-resistant laminate film comprising a base layer and a coextrusion layer, wherein providing the aggressive chemical-resistant laminate film comprises:
providing the base layer, wherein the base layer is one or more of water-resistant or oxygen-resistant,
coextruding a tie layer and a contact layer to provide the coextrusion layer,
coating the coextrusion layer to the base layer, and
curing the coextrusion layer coated to the base layer, wherein:
the contact layer comprises a polymer selected from the group consisting of: a polyamide, an ethylene vinyl alcohol, or any combination thereof, and
a total loading of the tie layer is between 3 g/m 2 and 9 g/m 2 and the loading of the contact layer is equal to x times the total loading of the tie layer, wherein x is in a range of 1 to 3,
wherein the aggressive chemical-resistant laminate film is resistant to a chemical selected from nicotine, fentanyl, rivastigmine, or lidocaine; and
attaching the aggressive chemical-resistant laminate film to the first outer layer, wherein the base layer side of the aggressive chemical-resistant laminate film faces the first outer layer.
11. The method of claim 10 , further comprising:
providing the compound or the composition;
sealing the packaging around the compound or the composition to be packed so that the contact layer side of the coextrusion layer faces the interior side and the compound or the composition.
12. The method of claim 10 , wherein the base layer is selected from aluminum, polyvinylidene chloride, a silicon oxide coated polyester, an aluminum oxide coated polyester, an aluminum oxide polyethylene terephthalate (PET) film, a silicon oxide coated PET film, or any combination thereof.
13. The method of claim 10 , wherein the compound or the composition is a patch.
14. The method of claim 10 , wherein the compound or the composition is in a liquid state.