Polyolefin-based adhesive composition
The present invention provides an adhesive composition that shows good adhesion to a polyolefin resin substrate and a metal substrate, and good electrolyte solution resistance, and also exhibits excellent heat resistance. The present invention also provides a laminate including an adhesive layer comprising the adhesive composition, a packaging material using the laminate for which heat resistance and electrolyte solution resistance are required, and a packaging material for a lithium-ion battery comprising the laminate as a constituent member. The adhesive composition comprises an acid-modified polyolefin (A), an isocyanate curing agent (B), and an acid anhydride group-containing compound (C), the acid anhydride group-containing compound (C) being present in an amount of 0.1 parts by mass or more and 20 parts by mass or less based on 100 parts by mass of the acid-modified polyolefin (A).
1. An adhesive composition comprising an acid-modified polyolefin (A), an isocyanate curing agent (B), and an acid anhydride group-containing compound (C),
the acid anhydride group-containing compound (C) is contained in an amount of 0.1 parts by mass or more and 20 parts by mass or less based on 100 parts by mass of the acid-modified polyolefin (A),
wherein the acid anhydride group-containing compound (C) contains a hydrocarbon group having 11 or more and 20 or less carbon atoms, and
the isocyanate curing agent (B) is contained in an amount of 15 to 70 parts by mass based on 100 parts by mass of the acid-modified polyolefin (A).
2. The adhesive composition according to claim 1 , wherein the acid-modified polyolefin (A) has an acid value of 2 to 50 mgKOH/g.
3. The adhesive composition according to claim 1 , further comprising an organic solvent (D) contained in an amount of 80 to 2000 parts by mass based on 100 parts by mass of the acid-modified polyolefin (A).
4. The adhesive composition according to claim 3 , wherein the organic solvent (D) is a mixture of a solvent (D1) and a solvent (D2),
the solvent (D1) is at least one solvent selected from the group consisting of an aromatic hydrocarbon, an aliphatic hydrocarbon, an alicyclic hydrocarbon, and a halogenated hydrocarbon,
the solvent (D2) is at least one oxygen-containing organic solvent, and
the mass ratio of solvent (D1) to solvent (D2) is 50 to 97/50 to 3.
5. The adhesive composition according to claim 1 , wherein the acid anhydride group-containing compound (C) has a molecular weight of 100 g/mol or more and 500 g/mol or less.
6. The adhesive composition according to claim 1 , wherein the acid anhydride group-containing compound (C) has an acid value of 150 mgKOH/g or more and 800 mgKOH/g or less.
7. The adhesive composition according to claim 1 for use in bonding a polyolefin resin substrate and a metal substrate.
8. A laminate comprising a polyolefin resin substrate and a metal substrate bonded with the adhesive composition according to claim 1 .
9. A packaging material for a battery, comprising the laminate according to claim 8 as a constituent member.
10. A packaging material for a lithium-ion battery, comprising the laminate according to claim 8 as a constituent member.
11. A method of bonding substrates, comprising applying the adhesive composition according to claim 1 to a metal substrate and bonding a polyolefin resin substrate to the metal substrate.
12. A method for preparing a laminate, comprising applying the adhesive composition according to claim 1 to a metal substrate and bonding a polyolefin resin substrate to the metal substrate.