Adhesive, laminate, cell case packaging, cell, high-alkali solution packaging, alcohol-containing solution packaging, and package
An adhesive includes a modified olefin polymer (A) allowing a polymer of a C2 to C20 α-olefin having a structural unit derived from a C4 to C20 α-olefin to be modified with a monomer having a functional group capable of reacting with an isocyanate group and having a heat of fusion measured in accordance with JIS K7122 of 0 J/g or more and 50 J/g or less and a polyisocyanate (B).
1. An adhesive comprising:
a modified olefin polymer (A) obtained by modifying a polymer of a C2 to C20 α-olefin having a structural unit derived from a C4 to C20 α-olefin, with a monomer having a functional group having active hydrogen and having a heat of fusion measured in accordance with JIS K7122 of 0 J/g or more and 50 J/g or less;
a polyisocyanate (B); and
a synthetic hydrocarbon oil (D),
wherein a melting point of the modified olefin polymer (A) is 40° C. or more and 100° C. or less,
the synthetic hydrocarbon oil (D) is an ethylenic copolymer having a structural unit derived from ethylene and a structural unit derived from a C3 to C20 α-olefin,
the modified olefin polymer (A) has an acid value of 10 mgKOH/g or less, and
the synthetic hydrocarbon oil (D) has a kinetic viscosity at 40° C. of 5,000 cSt or more and 300,000 cSt or less.
2. The adhesive according to claim 1 , wherein the polymer has a structural unit derived from propylene.
3. The adhesive according to claim 2 , wherein the content ratio of the structural unit derived from the propylene with respect to 100 mol % of the structural unit derived from the C2 to C20 α-olefin is 40 mol % or more and 95 mol % or less.
4. The adhesive according to claim 2 , wherein in the polymer, the entire structural unit, excluding the structural unit derived from the propylene, is the structural unit derived from the C4 to C20 α-olefin.
5. The adhesive according to claim 4 , wherein the C4 to C20 α-olefin is 1-butene.
6. The adhesive according to claim 1 , wherein the content ratio of the monomer with respect to 100 parts by mass of the modified olefin polymer (A) is 0.1 parts by mass or more and 15 parts by mass or less.
7. The adhesive according to claim 1 , wherein the functional group is a carboxyl group and/or an anhydride group.
8. Cell case packaging comprising:
a substrate,
an inner-side layer adhering to the inner side of the substrate,
an outer-side layer adhering to the outer side of the substrate,
an inner-side adhesive layer interposed between the substrate and the inner-side layer and including a cured material of the adhesive described in claim 1 , and
an outer-side adhesive layer interposed between the substrate and the outer-side layer.
9. A cell comprising:
the cell case packaging described in claim 8 and
an electrolytic solution packaged in the cell case packaging, wherein
at least a part of the inner-side layer of the cell case packaging is in contact with the electrolytic solution.
10. High-alkali solution packaging comprising:
a substrate,
an inner-side layer adhering to the inner side of the substrate, and
an inner-side adhesive layer interposed between the substrate and the inner-side layer and including a cured material of the adhesive described in claim 1 .
11. A package comprising:
the high-alkali solution packaging described in claim 10 and
a solution of pH 9 or more packaged in the high-alkali solution packaging.
12. Alcohol-containing solution packaging comprising:
a substrate,
an inner-side layer adhering to the inner side of the substrate, and
an inner-side adhesive layer interposed between the substrate and the inner-side layer and including a cured material of the adhesive described in claim 1 .
13. A package comprising:
the alcohol-containing solution packaging described in claim 12 and
an alcohol-containing solution packaged in the alcohol-containing solution packaging.
14. A laminate comprising:
a substrate and
an adhesive layer provided at one side of the substrate and formed of an adhesive, wherein the adhesive layer is made of a coating agent including a composition including
a modified olefin polymer (A) obtained by modifying a polymer of a C2 to C20 α-olefin having a structural unit derived from a C4 to C20 α-olefin, with a monomer having a functional group having active hydrogen and having a heat of fusion measured in accordance with JIS K7122 of 0 J/g or more and 50 J/g or less;
a polyisocyanate (B); and
a synthetic hydrocarbon oil (D),
wherein a melting point of the modified olefin polymer (A) is 40° C. or more and 100° C. or less,
the synthetic hydrocarbon oil (D) is an ethylenic copolymer having a structural unit derived from ethylene and a structural unit derived from a C3 to C20 α-olefin,
the modified olefin polymer (A) has an acid value of 10 mgKOH/g or less, and
the synthetic hydrocarbon oil (D) has a kinetic viscosity at 40° C. of 5,000 cSt or more and 300,000 cSt or less.
15. The laminate according to claim 14 , wherein the adhesive layer is directly laminated on one surface of the substrate.
16. The laminate according to claim 14 further comprising:
an adherend adhering to one side of the substrate via the adhesive layer.