Methods for depositing dielectric films with increased stability
Embodiments include semiconductor processing methods to form dielectric films on semiconductor substrates are described. The methods may include providing a silicon-containing precursor and a nitrogen-containing precursor to a processing region of a semiconductor processing chamber. A substrate may be disposed within the processing region. The methods may include providing an inert precursor to the processing region of the semiconductor processing chamber. The methods may include generating plasma effluents of the silicon-containing precursor, the nitrogen-containing precursor, and the inert precursor. The methods may include depositing a silicon-containing material on the substrate.
1 . A semiconductor processing method comprising:
providing a silicon-containing precursor, a nitrogen-containing precursor, and an inert gas to a processing region of a semiconductor processing chamber, wherein a substrate is disposed within the processing region;
generating plasma effluents of the silicon-containing precursor, the nitrogen-containing precursor, and the inert gas; and
depositing a silicon-containing material on the substrate.
2 . The semiconductor processing method of claim 1 , wherein the silicon-containing precursor comprises trimethylsilane (TMS).
3 . The semiconductor processing method of claim 1 , wherein the nitrogen-containing precursor comprises ammonia (NH 3 ).
4 . The semiconductor processing method of claim 1 , wherein the inert gas comprises argon.
5 . The semiconductor processing method of claim 1 , wherein a flow rate ratio of the inert gas compared to the silicon-containing precursor is greater than or about 3:1.
6 . The semiconductor processing method of claim 1 , wherein the plasma effluents of the silicon-containing precursor, the nitrogen-containing precursor, and the inert gas are generated at a plasma power of greater than or about 250 W.
7 . The semiconductor processing method of claim 1 , wherein the silicon-containing material is characterized by a carbon content of greater than or about 20 at. %.
8 . The semiconductor processing method of claim 1 , further comprising:
subsequent to the depositing the silicon-containing material, performing a post-deposition plasma treatment on the silicon-containing material.
9 . The semiconductor processing method of claim 8 , further comprising:
halting a flow of the silicon-containing precursor prior to performing the post-deposition plasma treatment on the silicon-containing material.
10 . The semiconductor processing method of claim 8 , further comprising:
bonding the silicon-containing material on the substrate to an exposed silicon-and-carbon-containing material on a second substrate.
11 . A semiconductor processing method comprising:
providing a silicon-containing precursor, a nitrogen-containing precursor, and argon to a processing region of a semiconductor processing chamber, wherein a substrate is disposed within the processing region;
generating plasma effluents of the silicon-containing precursor, the nitrogen-containing precursor, and argon; and
depositing a silicon-carbon-and-nitrogen-containing material on the substrate, wherein the silicon-carbon-and-nitrogen-containing material is deposited at a rate of less than or about 5,000 Å/min.
12 . The semiconductor processing method of claim 11 , wherein a flow rate of argon is greater than or about 1,000 sccm.
13 . The semiconductor processing method of claim 11 , wherein a temperature within the semiconductor processing chamber is maintained at less than or about 300° C.
14 . The semiconductor processing method of claim 11 , wherein a pressure within the semiconductor processing chamber is maintained at less than or about 10 Torr.
15 . The semiconductor processing method of claim 11 , wherein the silicon-carbon-and-nitrogen-containing material is characterized by an oxygen content of less than or about 2.0 at. %.
16 . The semiconductor processing method of claim 15 , wherein, subsequent a period of aging, the oxygen content in the silicon-carbon-and-nitrogen-containing material does not increase above about 3.0 at. %.
17 . The semiconductor processing method of claim 11 , wherein the silicon-carbon-and-nitrogen-containing material is characterized by a Young's modulus of greater than or about 30 GPa, a hardness greater than or about 5 GPa, or both.
18 . A semiconductor processing method comprising:
providing a silicon-containing precursor, a nitrogen-containing precursor, and an inert gas to a processing region of a semiconductor processing chamber, wherein a substrate is disposed within the processing region, and wherein the silicon-containing precursor, the nitrogen-containing precursor, or both comprise carbon;
generating plasma effluents of the silicon-containing precursor, the nitrogen-containing precursor, and the inert gas;
depositing a silicon-containing material on the substrate, wherein the silicon-containing material is characterized by a carbon content of greater than 30 at. %;
halting a flow rate of the silicon-containing precursor; and
performing a post-deposition plasma treatment on the silicon-containing material.
19 . The semiconductor processing method of claim 18 , wherein the post-deposition plasma treatment reduces the carbon content at an exposed surface of the silicon-containing material.
20 . The semiconductor processing method of claim 18 , wherein a plasma power during the post-deposition plasma treatment is maintained at less than or about 1,500 W.