Elastomer laminate
An elastomer laminate comprises at least two adjacent layers, the first layer consisting of a composition based on 20 to 100 phr of at least one copolymer comprising ethylene units and units of a formula CH 2 ═CR—CH═CH 2 , the ethylene units in the copolymer representing more than 50 mol % of the monomer units, R representing a hydrocarbon chain having 3 to 20 carbon atoms, 0 to 80 phr of at least one diene elastomer having a weight content of diene units of greater than 50%, 10 to 100 phr of a plasticizing system comprising at least one plasticizing resin having a glass transition temperature above 20° C. and/or at least one plasticizer that is liquid at 23° C., a reinforcing filler, and a crosslinking system, and the second layer consisting of a composition based on a diene elastomer having a weight content of diene units of greater than 50% and a crosslinking system.
1 . An elastomer laminate comprising at least two adjacent layers, the first layer consisting of a rubber composition based on:
20 to 100 phr of at least one copolymer comprising ethylene units and units of a 1,3-diene of formula (I), the ethylene units in the copolymer representing more than 50 mol % of monomer units of the copolymer,
CH 2 —CR—CH—CH 2 (I),
R representing a hydrocarbon chain having 3 to 20 carbon atoms;
0 to 80 phr of at least one diene elastomer having a weight content of diene units of greater than 50%;
35 to 100 phr of a plasticizing system comprising at least one plasticizing resin having a glass transition temperature above 20° C. and/or at least one plasticizer that is liquid at 23° C.;
a reinforcing filler; and
a crosslinking system, and
the second layer consisting of a rubber composition based on a diene elastomer having a weight content of diene units of greater than 50% and a crosslinking system.
2 . The elastomer laminate according to claim 1 , wherein the 1,3-diene of formula (I) of the copolymer of the first layer is myrcene, β-farnesene or a mixture of myrcene and β-farnesene.
3 . The elastomer laminate according to claim 1 , wherein the copolymer further comprises a second 1,3-diene selected from 1,3-butadiene, isoprene or a mixture thereof.
4 . The elastomer laminate according to claim 1 , wherein the content of the copolymer of ethylene and of a 1,3-diene of formula (I) in the rubber composition of the first layer is within a range extending from 20 to 90 phr, and
wherein the diene elastomer having a weight content of diene units of greater than 50% is present in the rubber composition of the first layer at a content within a range extending from 10 to 80 phr.
5 . The elastomer laminate according to claim 1 , wherein the diene elastomer having a weight content of diene units of greater than 50% of the rubber composition of the first layer is selected from the group consisting of polybutadienes (BRs), natural rubber (NR), synthetic polyisoprenes (IRs), butadiene copolymers, isoprene copolymers and mixtures thereof.
6 . The elastomer laminate according to claim 1 , wherein the plasticizer that is liquid at 23° C. of the rubber composition of the first layer is selected from the group consisting of liquid diene polymers, polyolefin oils, naphthenic oils, paraffinic oils, Distillate Aromatic Extract (DAE) oils, Medium Extracted Solvate (MES) oils, Treated Distillate Aromatic Extract (TDAE) oils, Residual Aromatic Extract (RAE) oils, Treated Residual Aromatic Extract (TRAE) oils, Safety Residual Aromatic Extract (SRAE) oils, mineral oils, vegetable oils, ether plasticizers, ester plasticizers, phosphate plasticizers, sulfonate plasticizers and mixtures thereof.
7 . The elastomer laminate according to claim 1 , wherein the content of plasticizer that is liquid at 23° C., in the rubber composition of the first layer, is within a range extending from 1 to 49 phr.
8 . The elastomer laminate according to claim 1 , wherein the plasticizing resin having a glass transition temperature above 20° C. of the rubber composition of the first layer is selected from the group consisting of cyclopentadiene homopolymer or copolymer resins, dicyclopentadiene homopolymer or copolymer resins, terpene homopolymer or copolymer resins, C 5 fraction homopolymer or copolymer resins, C9 fraction homopolymer or copolymer resins, α-methylstyrene homopolymer or copolymer resins and mixtures thereof.
9 . The elastomer laminate according to claim 1 , wherein the content of plasticizing resin having a glass transition temperature above 20° C., in the rubber composition of the first layer, is within a range extending from 1 to 99 phr.
10 . The elastomer laminate according to claim 1 , wherein the content of reinforcing filler in the rubber composition of the first layer is within a range extending from 30 to 200 phr.
11 . The elastomer laminate according to claim 1 , wherein the diene elastomer having a weight content of diene units of greater than 50% of the rubber composition of the second layer is selected from the group consisting of polybutadienes (BRs), natural rubber (NR), synthetic polyisoprenes (IRs), butadiene copolymers, isoprene copolymers and mixtures thereof.
12 . The elastomer laminate according to claim 1 , wherein the diene elastomer having a weight content of diene units of greater than 50% of the first layer and the diene elastomer having a weight content of diene units of greater than 50% of the second layer are polyisoprenes comprising a weight content of 1,4-cis bonds of at least 90% of the weight of the polyisoprene.
13 . The elastomer laminate according to claim 1 , wherein the first layer has a thickness within a range extending from 0.2 to 120 mm, and
wherein the second layer has a thickness within a range extending from 0.2 to 10 mm.
14 . A rubber article comprising the elastomer laminate according to claim 1 .
15 . The rubber article according to claim 14 , wherein the rubber article is selected from the group consisting of pneumatic tires, non-pneumatic tires, caterpillar tracks, conveyor belts and anti-vibratory articles.