The invention is directed to compositions comprising a CO to CO 2 combustion promoter at least one porous particle having a diameter of less than 1 mm and comprising: a) one or more of silica, alumina, zeolite, silica sol, alumina sol, pseudo-boehmite alumina, and/or a clay-based matrix; and b) one or more Group VIII noble metals distributed in the porous particle such that at least 60% of the one or more Group VIII noble metals is present in an outer region of the porous particle; and method of using the same.
1. A CO to CO 2 combustion promoter comprising:
a porous particle having a diameter of less than 1 mm and comprising:
a) one or more of silica, alumina, zeolite, silica sol, alumina sol, pseudo-boehmite alumina, and/or a clay-based matrix; and
b) one or more Group VIII noble metals distributed in the porous particle such that at least 60% of the one or more Group VIII noble metals is present in an outer region of the porous particle.
2. The CO to CO 2 combustion promoter according to claim 1 , wherein the outer region comprises a depth from the outer surface towards the interior of the particle of at least 1 micron.
3. The CO to CO 2 combustion promoter according to claim 1 , wherein the outer region comprises a depth from the outer surface towards the interior of the particle of up to 10 microns.
4. The CO to CO 2 combustion promoter according to claim 1 , wherein the outer region comprises a depth from the outer surface towards the interior of the particle of between 1 to 10 microns.
5. A CO to CO 2 combustion promoter comprising a first plurality of porous particles, each porous particle of the first plurality of porous particles being a porous particle of claim 1 .
6. The CO to CO 2 combustion promoter according to claim 5 , wherein the average content of Group VIII noble metal per grams of CO to CO 2 combustion promoter is between 100 and 1500 ppm.
7. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles comprises silica.
8. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles comprise silica; and
the CO to CO 2 combustion promoter further comprises a second plurality of porous particles, each of the second plurality of porous particles having a diameter of less than 1 mm and comprising:
a) alumina; and
b) one or more Group VIII noble metals distributed in the porous particle such that at least 60% of the one or more Group VIII noble metals is present in an outer region of the porous particle.
9. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles collectively have an average (D50) size of between 60 and 90 microns as measured by laser diffraction.
10. The CO to CO 2 combustion promoter according to claim 5 , wherein an attrition index as measured according to ASTM D-5757 of the CO to CO 2 combustion promoter for a sieve fraction of porous particles of between 40 and 105 microns is between 5 and 25.
11. A composition, inventory, or mixture comprising at least:
the CO to CO 2 combustion promoter of claim 5 ; and
a second plurality of particles comprising FCC catalyst particles.
12. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles comprises alumina.
13. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles comprises silica and alumina.
14. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles collectively have an average (D50) size of between 60 and 90 microns as measured by laser diffraction; and
wherein the outer region comprises a depth from the outer surface towards the interior of the particle of up to 10 microns.
15. The CO to CO 2 combustion promoter according to claim 5 , wherein the first plurality of porous particles collectively have an average (D50) size of between 60 and 90 microns as measured by laser diffraction; and
wherein the outer region comprises a depth from the outer surface towards the interior of the particle of between 1 to 10 microns.
16. The CO to CO 2 combustion promoter according to claim 1 , wherein the zeolite is faujasite, Type Y zeolite, and/or ZSM-5.
17. The CO to CO 2 combustion promoter according to claim 1 , wherein the zeolite is ZSM-5.
18. The CO to CO 2 combustion promoter according to claim 1 , wherein the porous particle has a surface area (BET) of between 50 and 300 m 2 /g in the absence of the one or more Group VIII noble metals.
19. The CO to CO 2 combustion promoter according to claim 1 , wherein the porous particle is a gamma alumina particle.
20. The CO to CO 2 combustion promoter according to claim 1 , wherein the porous particle is a theta alumina particle.
21. The CO to CO 2 combustion promoter according to claim 1 , wherein the porous particle is a spray dried silica particle; or is an equilibrium or spent catalyst as obtained from a fluidized catalytic cracking (FCC) process.
22. The CO to CO 2 combustion promoter according to claim 1 , wherein the one or more Group VIII noble metals comprises one or more of platinum, palladium, iridium, ruthenium, and rhodium.
23. The CO to CO 2 combustion promoter according to claim 22 , wherein the one or more Group VIII noble metals comprises platinum.
24. The CO to CO 2 combustion promoter according to claim 22 , wherein the one or more Group VIII noble metals comprises palladium.
25. The CO to CO 2 combustion promoter according to claim 22 , wherein the one or more Group VIII noble metals comprises platinum and palladium.
26. The CO to CO 2 combustion promoter according to claim 1 , wherein the porous particles further comprise at least one of cerium oxide and copper oxide.
27. The CO to CO 2 combustion promoter according to claim 26 , wherein the at least one of cerium oxide and copper oxide is distributed in the porous particles such that a higher concentration of the at least one of cerium oxide and copper oxide is present in the outer region of the porous particle as compared to the concentration of the at least one of cerium oxide and copper oxide in the centre of the porous particle.
28. A method of fluid catalytic cracking, the method comprising contacting a CO to CO 2 combustion promoter of claim 1 with CO in a fluidized bed of an FCC unit.
29. A method of CO to CO 2 combustion, the method comprising contacting a CO to CO 2 combustion promoter of claim 1 with CO in a fluidized bed.
30. The CO to CO 2 combustion promoter according to claim 1 , wherein the porous particle has a pore volume of between 0.05 and 0.50 mL/g as measured by the water pore volume in the absence of the one or more Group VIII noble metals.