Methods to remove an EBC from a substrate and to repair a coated component
A method is provided for removing a bondcoat and an environmental barrier coating from a coated component. The method may include contacting the coated component with an etchant liquid comprising phosphoric acid, 5% by volume to 70% by volume of hydrogen fluoride, and a solvent. The hydrogen fluoride and the phosphoric acid react with a composition in the bondcoat. The bondcoat is positioned within the coated component between a silicon-containing substrate and the environmental barrier coating, and the bondcoat comprises mullite.
1 . A method for removing a coating from a coated component, the method comprising:
contacting the coated component with an etchant liquid, wherein the etchant liquid comprises phosphoric acid, 5% by volume to 70% by volume of hydrogen fluoride, and a solvent, wherein the coated component includes a coating on a silicon-containing substrate, the coating comprising a bondcoat and an environmental barrier coating, wherein the bondcoat comprises mullite, and wherein the phosphoric acid and the hydrogen fluoride react with the coating to weaken chemical bonds therein to form a chemically-weakened coating, and
removing the chemically-weakened coating from the silicon-containing substrate.
2 . The method of claim 1 , wherein the bondcoat comprises at least 50% by weight mullite.
3 . The method of claim 1 , wherein the bondcoat comprises at least 75% by weight mullite.
4 . The method of claim 1 , wherein the environmental barrier coating is directly on the bondcoat prior to contacting the coated component with the etchant liquid.
5 . The method of claim 1 , wherein the coated component is substantially free of a thermally grown oxide layer.
6 . The method of claim 1 , wherein contacting the coated component with the etchant liquid comprises submerging the coated component within the etchant liquid.
7 . The method of claim 1 , wherein the etchant liquid comprises 25% by volume to 49% by volume of the hydrogen fluoride.
8 . The method of claim 1 , wherein the etchant liquid comprises 10% by volume to 60% by volume of the phosphoric acid.
9 . The method of claim 1 , wherein the etchant liquid comprises 30% by volume to 40% by volume of the phosphoric acid.
10 . The method of claim 1 , wherein the solvent comprises water.
11 . The method of claim 1 , wherein the etchant liquid consists essentially of the hydrogen fluoride, the phosphoric acid, and water.
12 . The method of claim 1 , wherein the etchant liquid further comprises hydrogen chloride, nitric acid, fluorosilicic acid, hydrogen peroxide, or a mixture thereof.
13 . The method of claim 1 , wherein the etchant liquid further comprises a wetting agent.
14 . The method of claim 1 , wherein the etchant liquid has a treatment temperature of 20° C. to 60° C. during the contacting.
15 . The method of claim 1 , wherein removing the chemically-weakened coating from the silicon-containing substrate comprises:
contacting the coated component with a mechanical etchant to remove the bondcoat and the environmental barrier coating to expose a surface of the silicon-containing substrate.
16 . The method of claim 15 , wherein contacting the coated component with the mechanical etchant comprises mechanically blasting the environmental barrier coating and the bondcoat with a plurality of particles for removal of the environmental barrier coating and the bondcoat.
17 . A method of repairing a coated component, the method comprising:
forming an intermediate component by removing a bondcoat and an environmental barrier coating from the coated component according to the method of claim 1 to expose a surface of the silicon-containing substrate to define an exposed silicon-containing substrate; and
forming a replacement bondcoat on the exposed silicon-containing substrate.
18 . The method of claim 17 , wherein the replacement bondcoat comprises mullite.
19 . The method of claim 17 , further comprising:
forming a replacement environmental barrier coating on the replacement bondcoat.
20 . The method of claim 19 , wherein the replacement environmental barrier coating is formed directly on the bondcoat without a thermally grown oxide layer therebetween.