POLISHING PAD AND PREPARATION METHOD THEREOF
The embodiment relates to a polishing pad for use in a chemical mechanical planarization process of semiconductor devices. The polishing pad comprises a top pad layer, wherein the polishing pad has a total biomass content of 1 to 50% by weight as measured according to the ASTM D 6866 standard; thus, it can be environmentally friendly.
1 . A polishing pad, which comprises a top pad layer prepared from a biomass-containing composition and has a total biomass content of 1 to 50% by weight as measured by the ASTM D 6866 standard.
2 . The polishing pad of claim 1 , wherein the biomass content of the top pad layer is 2 to 70% by weight based on the total weight of the top pad layer.
3 . The polishing pad of claim 1 , wherein the composition comprises a biomass-containing urethane prepolymer, and the biomass-containing urethane prepolymer is prepared from a urethane prepolymer composition comprising an isocyanate material; and a polyol material comprising a bio-polyol.
4 . The polishing pad of claim 3 , wherein the biomass content of the biomass-containing urethane prepolymer is 4 to 80% by weight based on the total weight of the biomass-containing urethane prepolymer.
5 . The polishing pad of claim 3 , wherein the bio-polyol comprises at least one selected from the group consisting of a bio-polymer polyol and a bio-monomer polyol.
6 . The polishing pad of claim 5 , wherein the bio-polymer polyol comprises at least one selected from the group consisting of a bio-polyether polyol, a bio-polyester polyol, a bio-polycarbonate polyol, and a bio-polycaprolactam polyol.
7 . The polishing pad of claim 5 , wherein the bio-monomer polyol comprises at least one selected from the group consisting of bio-ethylene glycol, bio-diethylene glycol, bio-1,2-propylene glycol, bio-1,3-propanediol, bio-2-methyl-1,3-propanediol, bio-1,3-butanediol, bio-1,4-butanediol, bio-2,3-butanediol, bio-n-butanol, bio-isobutanol, bio-1,5-pentanediol, bio-2-octanol, bio-1,9-nonediol, bio-1,10-decanediol, bio-diethylene glycol, and bio-isosorbide.
8 . The polishing pad of claim 3 , wherein the isocyanate raw material comprises at least one selected from the group consisting of toluene diisocyanate (TDI) and 4,4′-methylenedicyclohexyl diisocyanate (H12MDI).
9 . The polishing pad of claim 3 , wherein the isocyanate raw material comprises a bio-isocyanate.
10 . The polishing pad of claim 1 , wherein the total biomass content of the polishing pad is 8 to 50% by weight.
11 . A process for preparing a polishing pad, which comprises:
preparing a biomass-containing urethane prepolymer from a urethane prepolymer composition comprising an isocyanate raw material and a polyol raw material comprising a bio-polyol;
preparing a biomass-containing composition comprising the biomass-containing urethane prepolymer, a curing agent, and a foaming agent; and
curing the biomass-containing composition to prepare a top pad layer,
wherein the polishing pad has a total biomass content of 1 to 50% by weight as measured by the ASTM D 6866 standard.