DOUBLE-SIDED COPPER CLAD LAMINATE, CAPACITOR ELEMENT AND PRINTED WIRING BOARD WITH BUILT-IN CAPACITOR, AND METHOD FOR MANUFACTURING DOUBLE-SIDED COPPER CLAD LAMINATE
Provided is a double-sided copper clad laminate that can realize not only good capacitor characteristics but also excellent handleability. This double-sided copper clad laminate is a double-sided copper clad laminate having copper foil adhered onto both surfaces of a dielectric layer, wherein the dielectric layer has a thickness of 0.1 μm or more and 2.0 μm or less, and the double-sided copper clad laminate further includes a pair of resin layers arranged in contact with the copper foil between the dielectric layer and the copper foil.
1 . A double-sided copper clad laminate having copper foil adhered onto both surfaces of a dielectric layer,
wherein the dielectric layer has a thickness of 0.1 μm or more and 2.0 μm or less, and
wherein the double-sided copper clad laminate further comprises a pair of resin layers arranged in contact with the copper foil between the dielectric layer and the copper foil.
2 . The double-sided copper clad laminate according to claim 1 , wherein a tensile strength of the resin layers is larger than a tensile strength of the dielectric layer.
3 . The double-sided copper clad laminate according to claim 1 , wherein an overall tensile strength of the dielectric layer and the resin layers is 50 MPa or more and 200 MPa or less.
4 . The double-sided copper clad laminate according to claim 1 , wherein an overall puncture strength of the dielectric layer and the resin layers is 0.6 N or more.
5 . The double-sided copper clad laminate according to claim 1 , wherein at least one of the resin layers and the dielectric layer comprises a dielectric filler.
6 . The double-sided copper clad laminate according to claim 5 , wherein when the dielectric layer comprises the dielectric filler, a content of the dielectric filler in the dielectric layer is 10 parts by weight or more and 90 parts by weight or less relative to 100 parts by weight of the dielectric layer.
7 . The double-sided copper clad laminate according to claim 5 , wherein when the resin layers comprise the dielectric filler, a content of the dielectric filler in the resin layers is 10 parts by weight or more and 80 parts by weight or less relative to 100 parts by weight of the resin layers.
8 . The double-sided copper clad laminate according to claim 5 , wherein a content of the dielectric filler in the resin layers relative to 100 parts by weight of the resin layers is smaller than a content of the dielectric filler in the dielectric layer relative to 100 parts by weight of the dielectric layer.
9 . The double-sided copper clad laminate according to claim 5 , wherein the resin layers are free from the dielectric filler and the dielectric layer comprises the dielectric filler.
10 . The double-sided copper clad laminate according to claim 9 , wherein a content of the dielectric filler in the dielectric layer is 10 parts by weight or more and 90 parts by weight or less relative to 100 parts by weight of the dielectric layer.
11 . The double-sided copper clad laminate according to claim 1 , wherein a glass transition temperature Tg of resin contained in the resin layers is 180° C. or higher.
12 . The double-sided copper clad laminate according to claim 1 , wherein a glass transition temperature Tg of resin contained in the resin layers is higher than a glass transition temperature Tg of resin contained in the dielectric layer.
13 . A capacitor element comprising the double-sided copper clad laminate according to claim 1 .
14 . A printed wiring board with built-in capacitor, comprising the double-sided copper clad laminate according to claim 1 .
15 . A method for manufacturing the double-sided copper clad laminate according to claim 1 , comprising:
(i) applying a resin layer precursor to a copper foil;
(ii) curing the precursor to obtain a copper foil with resin layer;
(iii) arranging a dielectric layer on a surface of the resin layer; and
(iv) pressing the copper foil with resin layer on which the dielectric layer has been arranged and another copper foil with resin layer produced through the above (i) and (ii), so that the dielectric layer is sandwiched by the resin layers from both sides.