Method for welding sheets with coatings comprising an alloy of aluminum and silicon
A method of welding two metal sheets includes providing a first sheet having a first weld surface and a second sheet having a second weld surface. The first sheet has a coating includes an alloy of aluminum and silicon on the first weld surface. The method further includes irradiating the first weld surface and the second weld surface with a laser beam. The laser beam has an inner core and an outer ring with different intensity profiles. The laser beam is moved with a wobbling motion in a feed direction along an imaginary feed line and perpendicular to the imaginary feed line. A path of the laser beam along the imaginary feed line is of a periodic shape. A width of the path perpendicular to the imaginary feed line is greater than a length of a period of the path along the imaginary feed line.
1. A method of welding two metal sheets, the method comprising:
providing a first sheet having a first weld surface and a second sheet having a second weld surface, the first sheet having a coating comprising an alloy of aluminum and silicon on the first weld surface; and
irradiating the first weld surface and the second weld surface with a laser beam, the laser beam having an inner core and an outer ring with different intensity profiles,
wherein the laser beam is moved with a wobbling motion in a feed direction along an imaginary feed line and perpendicular to the imaginary feed line, and
wherein a path of the laser beam along the imaginary feed line is of a periodic shape, a width of the path perpendicular to the imaginary feed line being greater than a length of a period of the path along the imaginary feed line.
2. The method according to claim 1 , wherein the second weld surface is coated with the alloy of aluminum and silicon.
3. The method according to claim 1 , wherein the wobbling motion has a same amplitude on both sides of the imaginary feed line, and wherein the amplitude is greater than the period of the path of the laser beam.
4. The method according to claim 1 , wherein the first sheet and the second sheet are arranged as a lap joint.
5. The method according to claim 1 , wherein the first sheet and the second sheet are joined by a fillet weld or by an I-weld.
6. The method according to claim 1 , wherein the path of the laser beam is in a form of a sinusoidal function, a meander, or a zigzag function.
7. The method according to claim 1 , wherein the path of the laser beam is in a form of successive eights or infinity symbols.
8. The method according to claim 1 , wherein a power of the laser beam is varied along the path of the laser beam.
9. The method of claim 8 , wherein the power of the laser beam is increased or decreased during a welding process in a predetermined section at an end of the path of the laser beam in the feed direction of the laser beam compared to an averaged power of the laser beam on the path of the laser beam.
10. The method according to claim 1 , wherein the laser beam is guided multiple passes along a same segment of the imaginary feed line, and wherein an amplitude of the wobbling motion in a direction perpendicular to the imaginary feed line is set differently for each pass of the segment.
11. The method according to claim 1 , wherein the first sheet and/or the second sheet comprises a steel that contains ferrite, martensite, bainite and/or austenite.
12. The method according to claim 11 , wherein the steel is a multiphase steel.
13. The method according to claim 1 , wherein the imaginary feed line has a sinusoidal, circular, spiral, or zig-zag shape, or a C-shape.
14. The method according to claim 1 , wherein the first weld surface and the second weld surface are arranged such that the first weld surface and the second weld surface face each other, with a gap between the first weld surface and the second weld surface.
15. The method according to claim 14 , wherein a width of the gap between the first weld surface and the second weld surface is in a range from 0.05 mm to 0.3 mm.
16. The method according to claim 15 , wherein the width of the gap between the first weld surface and the second weld surface is in a range from 0.1 mm to 0.2 mm.
17. The method according to claim 1 , wherein a proportion of the power of the inner core of the laser beam is in a range from 20% to 80% of a total power of the inner core and the outer ring of the laser beam.
18. The method according to claim 17 , wherein the proportion of the power of the inner core of the laser beam is in a range from 59% to 61% of the total power.
19. The method according to claim 1 , wherein a speed of the laser beam along the imaginary feed line during the wobbling motion is in a range from 2 m/min to 8 m/min.
20. The method according to claim 19 , wherein the speed of the laser beam along the imaginary feed line during the wobbling motion is in a range from 3 m/min to 5 m/min.