Underwater immersion block and method to produce the same
It is an object of the invention to effectively absorb and remove CO 2 in an exhaust gas generated during an industrial process for reducing an amount of exhausting CO 2 into the atmospheric air. The exhaust gas containing CO 2 is blown into the agglomerate of solid particles containing CaO and/or Ca(OH) 2 to contact CO 2 to the agglomerate for fixing CO 2 in the exhaust gas as CaCO 3 , thereby to reduce the CO 2 concentration in the exhaust gas. Preferably, the solid particles contain water, and more preferably, the solid particles contain surface adhesive water.
1. An underwater immersion block for rearing algae and water living creatures produced by a method comprising the steps of:
(a) preparing a granular steel making slag mixture, said steel making slag mixture has a basicity in terms of a weight ratio of CaO to SiO 2 of 1.5 or higher; and
(b) producing a carbonate by carbonation of the mixture to agglomerate the mixture by using the carbonate as a binder,
wherein the underwater immersion block has a porosity of 10 to 70%.
2. A method of producing an underwater immersion block for rearing algae and water living creatures, comprising the steps of:
(a) preparing a granular steel making slag mixture, said steel making slag mixture has a basicity in terms of a weight ratio of CaO to SiO 2 of 1.5 or higher;
(b) forming a packed bed of the mixture, the packed bed having a bulk specific gravity/true specific gravity ratio of 0.3 to 0.9; and
(c) carrying out a carbonation of the mixture in the packed bed to agglomerate the mixture.
3. The underwater immersion block according to claim 1 , wherein the block is used for a sea-water immersion.
4. The underwater immersion block according to claim 1 , wherein the block is used for a river immersion.
5. The underwater immersion block according to claim 1 , wherein the mixture comprises granular slag containing CaO, and the carbonate is CaCO 3 .
6. The underwater immersion block according to claim 1 , wherein the mixture comprises granular slag containing CaO and MgO, and the carbonate includes CaCO 3 and MgCO 3 .
7. The underwater immersion block according to claim 1 , wherein the granular steel making slag mixture comprises a water-granulated blast furnace slag.
8. The underwater immersion block according to claim 1 , wherein the granular steel making slag mixture comprises granular slag subjected to a metallic iron removal treatment.
9. The underwater immersion block according to claim 1 , wherein the mixture further comprises a granular additive.
10. The underwater immersion block according to claim 9 , wherein the granular additive comprises oxidized iron.
11. The underwater immersion block according to claim 9 , wherein the granular additive comprises an oxidized iron-containing material.
12. The underwater immersion block according to claim 9 , wherein the granular additive comprises metallic iron.
13. The underwater immersion block according to claim 9 , wherein the granular additive comprises a metallic iron-containing material.
14. The underwater immersion block according to claim 9 , wherein the granular additive comprises a soluble silica.
15. The underwater immersion block according to claim 9 , wherein the granular additive comprises a soluble silica-containing material.
16. The underwater immersion block according to claim 9 , wherein the granular additive comprises CaO.
17. The method of producing the underwater immersion block according to claim 2 , wherein forming the packed bed comprises forming a pile of the mixture.
18. The method of producing the underwater immersion block according to claim 2 , wherein the block is used for a sea-water immersion.
19. The method of producing the underwater immersion block according to claim 2 , wherein the block is used for a river immersion.
20. The method of producing the underwater immersion block according to claim 2 , wherein the granular steel making slag mixture comprises a water-granulated blast furnace slag.
21. The method of producing the underwater immersion block according to claim 2 , wherein the granular steel making slag mixture comprises granular slag subjected to a metal removal treatment.
22. The method of producing the underwater immersion block according to claim 2 , wherein the mixture further comprises a granular additive.
23. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises an oxidized iron.
24. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises an oxidized iron-containing material.
25. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises a metallic iron.
26. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises a metallic iron-containing material.
27. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises a soluble silica.
28. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises a soluble silica-containing material.
29. The method of producing the underwater immersion block according to claim 22 , wherein the granular additive comprises CaO.
30. The method of producing the underwater immersion block according to claim 2 , wherein the step of preparing the mixture comprises mixing (i) the granular steel making slag, and (ii) at least one compound selected from the group consisting of CaO, Ca(OH) 2 , MgO and Mg(OH) 2 .
31. The method of producing the underwater immersion block according to claim 2 , wherein the step of preparing the mixture comprises adjusting a moisture content of the mixture to a degree of a water content value so that an agglomerate formed after the carbonation has a maximum compressive strength.
32. The method of producing the underwater immersion block according to claim 2 , wherein the step of agglomerating the mixture comprises blowing a gas containing carbon dioxide into the mixture in the packed bed.
33. The method of producing the underwater immersion block according to claim 2 , wherein the step of agglomerating the mixture comprises placing the mixture in the packed bed in a gas atmosphere containing carbon dioxide.
34. The method of producing the underwater immersion block according to claim 33 , wherein the carbon dioxide comprises carbon dioxide which is blown into water to saturate the water saturated with H 2 O.
35. The method of producing the underwater immersion block according to claim 2 , further comprising breaking the resultant agglomerated mixture from step (c) into sizes of 80 to 1500 mm.
36. A method for repairing a river bed comprising immersing a plurality of underwater immersion blocks according to claim 1 in a body of water which includes water creatures.
37. The underwater immersion block according to claim 1 , wherein the slag has a grain size of 5 cm or smaller and an iron content of 3 weight % or more.
38. The underwater immersion block according to claim 1 , which provides a pH of 10 or lower.