Cleaning solution and method of cleaning a semiconductor device using the same
In a cleaning solution and a method of cleaning a semiconductor substrate, the cleaning solution includes about 1 to about 10 percent by weight of sulfuric acid, about 0.5 to about 5 percent by weight of aqueous hydrogen peroxide solution, and about 85 to about 98.5 percent by weight of hydrogen fluoric acid solution. Various polymers attached to a metal wiring formed on a substrate are removed by immersing the substrate into the cleaning solution. The substrate is rinsed to remove the cleaning solution remaining on the substrate. Thus, the polymers can be completely removed without damage to the metal wiring and an underlying oxide film.
1. A method of cleaning a semiconductor device comprising:
removing polymers attached to a metal wiring formed on a substrate by immersing the substrate in a cleaning solution including about 1 to about 10 percent by weight of sulfuric acid, about 0.5 to about 5 percent by weight of an aqueous hydrogen peroxide solution, and about 0.01% to about 0.11% of hydrofluoric acid;
rinsing the substrate to remove the remaining cleaning solution; and
drying the substrate.
2. The method of claim 1 , wherein removing polymers further comprises raising a temperature of the cleaning solution to a temperature of about 20 to about 30° C.
3. The method of claim 2 , wherein immersing the substrate in the cleaning solution comprises immersing the substrate in the cleaning solution for about 1 to about 9 minutes.
4. The method of claim 1 , wherein the metal wiring corresponds to a gate electrode that includes tungsten or a bit line that includes tungsten.
5. The method of claim 1 , wherein the polymers comprise one selected from the group consisting of organic polymers, metallic polymers, and oxygen-containing polymers.
6. A method of cleaning a semiconductor device, comprising:
removing polymers attached to a metal wiring formed on a substrate by immersing the substrate in a cleaning solution, said cleaning solution including:
about 1 to about 10 percent by weight of sulfuric acid,
about 0.5 to about 5 percent by weight of an aqueous hydrogen peroxide solution, and
about 100 ppm to about 1080 ppm hydrofluoric acid;
rinsing the substrate to remove the cleaning solution; and
drying the substrate.
7. The method of claim 6 wherein immersing the substrate in the cleaning solution comprises raising a temperature of the cleaning solution to a temperature of about 20 to about 30° C.
8. The method of claim 6 wherein immersing the substrate in the cleaning solution comprises immersing the substrate in the cleaning solution for about 1 to about 9 minutes.
9. The method of claim 6 wherein the metal wiring corresponds to a gate electrode that includes tungsten or a bit line that includes tungsten.
10. The method of claim 6 wherein the polymers are selected from the group consisting of organic polymers, metallic polymers, and oxygen-containing polymers.
11. A method of forming a structure for a semiconductor device, comprising:
dry etching a polysilicon film, a tungsten film, and a nitride film that are successively disposed on a substrate using a mask pattern formed on the nitride film;
removing the mask pattern;
removing polymers attached to a sidewall of the structure by immersing the substrate in a cleaning solution, wherein the cleaning solution comprises about 1 to about 10 percent by weight of sulfuric acid, about 0.5 to about 5 percent by weight of aqueous hydrogen peroxide solution, and about 100 ppm to about 1100 ppm of hydrofluoric acid;
rinsing the substrate to remove cleaning solution remaining on the substrate; and
drying the substrate.
12. The method of claim 11 , further comprising depositing a barrier layer between the polysilicon film and the tungsten film.
13. The method of claim 11 wherein the structure includes a gate electrode or a bit line.
14. The method of claim 11 wherein immersing the substrate in a cleaning solution comprises immersing the substrate in a cleaning solution with a temperature of about 20 to about 30° C.
15. The method of claim 14 wherein immersing the substrate in a cleaning solution further comprises immersing the substrate in a cleaning solution for about 1 to about 9 minutes.