Powdered niobium, sintered body thereof, capacitor using the sintered body and production method of the capacitor
The present invention relates to a powdered niobium for a capacitor, characterized in that the content of each of the elements such as iron, nickel, cobalt, silicon, sodium, potassium and magnesium is about 100 ppm by weight or less or that the total content thereof is about 350 ppm by weight or less is used, a sintered body thereof, a sintered body comprising niobium monoxide crystal and/or diniobium mononitride crystal, a capacitor using the sintered body and the production method of the capacitor. A capacitor using the above described niobium sintered body has a large capacity per the unit weight, a good specific leakage current value and excellent high temperature property.
1. A powdered niobium for a capacitor comprising at least one of niobium nitride, niobium carbide and niobium boride of 50 ppm by weight to 200,000 ppm by weight and at least one element selected from the group consisting of iron, nickel, cobalt, silicon, sodium, potassium and magnesium in an amount of 100 ppm by weight or less.
2. A powdered niobium for a capacitor comprising at least one of niobium nitride, niobium carbide and niobium boride of 50 ppm by weight to 200,000 ppm by weight and at least one element selected from the group consisting of iron, nickel, cobalt, silicon, sodium, potassium and magnesium in a total amount of 350 ppm by weight or less.
3. A powdered niobium for a capacitor comprising at least one of niobium nitride, niobium carbide and niobium boride of 50 ppm by weight to 200,000 ppm by weight and at least one element selected from the group consisting of iron, nickel, cobalt, silicon, sodium, potassium and magnesium in an amount of 100 ppm by weight or less and in a total amount of 350 ppm by weight or less.
4. The powdered niobium for a capacitor as claimed in claim 1 , wherein the powdered niobium has an average particle size of 0.2 μm to 30 μm.
5. The powdered niobium for a capacitor as claimed in claim 2 , wherein the powdered niobium has an average particle size of 0.2 μm to 30 μm.
6. The powdered niobium for a capacitor as claimed in claim 3 , wherein the powdered niobium has an average particle size of 0.2 μm to 30 μm.
7. A sintered body for a capacitor using the powdered niobium as described in claim 1 .
8. A sintered body for a capacitor using the powdered niobium as described in claim 2 .
9. A sintered body for a capacitor using the powdered niobium as described in claim 3 .
10. A capacitor constructed by one electrode comprising the niobium sintered body as described in claim 7 , a second electrode and a dielectric material interposed between the two electrodes.
11. The capacitor as claimed in claim 10 , wherein the dielectric material is tantalum oxide, niobium oxide or a polymer material, or a ceramic compound.
12. The capacitor as claimed in claim 11 , wherein the dielectric material is niobium oxide formed by chemical forming on a niobium sintered body.
13. A capacitor constructed by one electrode comprising the niobium sintered body as described in claim 8 , a second electrode and a dielectric material interposed between the two electrodes.
14. The capacitor as claimed in claim 13 , wherein the dielectric material is tantalum oxide, niobium oxide or a polymer material, or a ceramic compound.
15. The capacitor as claimed in claim 14 , wherein the dielectric material is niobium oxide formed by chemical forming on a niobium sintered body.
16. A capacitor constructed by one electrode comprising the niobium sintered body as described in claim 9 , a second electrode and a dielectric material interposed between the two electrodes.
17. The capacitor as claimed in claim 16 , wherein the dielectric material is tantalum oxide, niobium oxide or a polymer material, or a ceramic compound.
18. The capacitor as claimed in claim 15 , wherein the dielectric material is niobium oxide formed by chemical forming on a niobium sintered body.
19. A capacitor using a powdered niobium, wherein the capacitor is evaluated by calculating a ratio (C−C 0 )/C 0 where C 0 is an initial capacity at room temperature and C is a capacity after the capacitor was left standing for 2,000 hours in an atmosphere of 105° C., and the ratio as calculated falls within ±20%.
20. The niobium capacitor as described in claim 19 , comprising a niobium sintered body.
21. The niobium capacitor as described in claim 20 , wherein the niobium sintered body comprises at least one of niobium nitride, niobium carbide and niobium boride of 50 ppm by weight to 200,000 ppm by weight and at least one element selected from the group consisting of iron, nickel, cobalt, silicon, sodium, potassium and magnesium in an amount of 100 ppm by weight or less.
22. A capacitor comprising the powdered niobium as claimed in claim 1 or 2 , wherein the leakage current value is 10 [nA/μF·V] or less.