Ferritic stainless steel alloy and its use as a substrate for catalytic converters
A ferritic stainless steel alloy useful as a substrate for catalytic converter material consists of, by weight: 15-21% Cr, 8-12% Al, 0.01-0.09% Ce, 0.02-0.1% total of REM, and possible minor amounts of further elements, other than the ones mentioned, the balance being Fe with normally occurring impurities. These alloys have managed to combine a high content of Al with a good hot and cold workability.
1. A method of making a thin foil from a ferritic stainless steel alloy, the method comprising:
(i) forming a melt of the alloy with a composition comprising 19-21% Cr, 9-12% Al, 0.02-0.1% total of Ce plus additional amounts of other REM, the balance essentially being Fe;
(ii) casting the melt to form an ingot; and
(iii) hot and cold rolling the ingot to an extent sufficient to produce a foil having a thickness on the order of 20 to 50 μm.
2. The method of claim 1 , wherein the alloy contains 9% to 11.5% Al.