Conductive resin composition
A conductive resin composition primarily comprising (A) 100 parts by weight of a thermosetting or thermoplastic resin, (B) 5–2,000 parts by weight of a conductive filler, and (C) 0.1–300 parts by weight of organic resin or rubber particulates has a low volume resistivity and stability thereof, and is effectively adherent. When applied to semiconductor packages, the composition can prevent the semiconductor chips from warpage or cracking due to thermal stresses in the semiconductor packages, ensuring the fabrication of semiconductor devices with high reliability.
1. A conductive resin composition comprising:
(A) 100 parts by weight of a thermosetting or thermoplastic resin selected from the group consisting of polyimide resins, polyamic acid resins, polyamide resins, polyamide-imide resins, and phenolic resins,
(B) 5 to 2,000 parts by weight of a conductive filler, and
(C) 0.1 to 300 parts by weight of a particulate organic resin or rubber selected from the group consisting of silicone rubbers, silicone rubbers coated with polyorganosilsesquioxane resins, and mixtures thereof,
wherein said composition has a volume resistivity of 8×10 −5 Ω·cm or less and at the same time a complex elastic modulus of 4.0 GPa or less after curing thereof.
2. The conductive resin composition of claim 1 wherein component (B) is a metal powder, a conductive metal-plated powder, or a mixture thereof.
3. The conductive resin composition of claim 1 wherein component (C) is spherical particulates of silicone rubber having an average particle size of 0.1 to 100 μm, silicone particulates obtained by coating the spherical particulates of silicone rubber with a polyorganosilsesquioxane resin, or a mixture thereof.
4. A conductive epoxy resin composition comprising:
(A) 100 parts by weight of an epoxy resin,
(B) 5 to 2,000 parts by weight of a conductive filler, and
(C) 0.1 to 300 parts by weight of particulates of silicone rubber, silicone rubbers coated with polyorganosilsesquioxane resin, or a mixture thereof,
wherein said composition has a volume resistivity of 5×10 −4 Ω·cm or less and at the same time a complex elastic modulus of 4.1 GPa or less after curing thereof.
5. The conductive resin composition of claim 4 , wherein component (B) is a metal powder, a conductive metal-plated powder, or a mixture thereof.
6. The conductive resin composition of claim 4 wherein component (C) is spherical particulates of silicone rubber having an average particle size of 0.1 to 100 μm, silicone particulates obtained by coating said spherical particulates of silicone rubber with a polyorganosilsesquioxane resin, or a mixture thereof.
7. The conductive resin composition of claim 1 , wherein said composition has a volume resistivity of from 3×10 −5 Ω·cm to 8×10 −5 Ω·cm and at the same time a low complex elastic modulus of from 3.0 GPa to 4.0 GPa after curing thereof.
8. The conductive epoxy resin composition of claim 4 , wherein said composition has a volume resistivity of from 2×10 −4 Ω·cm to 5×10 −4 Ω·cm and at the same time a low complex elastic modulus of from 2.8 GPa to 4.1 GPa after curing thereof.