Erosion-resistant silicone coatings for protection of fluid-handling parts
Novel uses of compositions of silanol and trifunctional silanes include their application and cure to form erosion-resistant silicone coatings on fluid-handling parts. Methods of application, maintenance, and repair of these coatings are also described.
1. An erosion-resistant fluid-handling part comprising:
a fluid-handling part;
a coating composition disposed on the fluid-handling part at a dry film thickness greater than about 200 μm, wherein the coating composition comprises:
a trifunctional silane ranging from about 0.01% by weight to about 20% by weight of the coating composition;
a silanol fluid having a weight average molecular weight of at least 4000 g/mol and wherein the silanol fluid ranges from about 40% by weight to about 99% by weight of the coating composition; and
fumed silica ranging from about 0.01% by weight to about 25% by weight of the coating composition.
2. An erosion-resistant fluid handling part according to claim 1 , wherein the coating composition has a dry film thickness ranging from about 200 μm to about 3000 μm.
3. An erosion-resistant fluid-handling part according to claim 1 , wherein the silanol fluid has a weight average molecular weight ranging from about 4000 g/mol to about 150,000 g/mol.
4. An erosion-resistant fluid-handling part according to claim 1 , wherein the coated fluid-handling part has a particle-impact erosion rate less than about 13% of the particle-impact erosion rate of uncoated 1100 aluminum.
5. An erosion-resistant fluid-handling part according to claim 1 , further comprising a primer composition disposed on the fluid handling part.
6. An erosion-resistant fluid-handling part according to claim 5 , wherein the primer composition is an epoxy primer composition comprising an epoxy blend, an aliphatic amine, and a silane adhesion promoter.
7. An erosion-resistant fluid-handling part according to claim 6 , wherein the silane adhesion promoter is selected from the group consisting of: a trimethoxysilane, a triethyoxysilane, and 3-glycidoxypropyl trimethoxysilane.
8. An erosion-resistant fluid-handling part according to claim 1 , wherein the fluid-handling part is selected from the group consisting of: hydro turbines, gas turbines, tide mills, windmills, compressors, pumps, blower, impellers, propellers, fans, runners, wheels, rings, stay rings, rotors, buckets, blades, turbine blades, runner blades, fan blades, compressor blades, propeller blades, vanes, stay vanes, helicopter rotors, hydroelectric turbines, marine propellers, housings, jackets, shrouds, hubs, shafts, flanges, tanks, surge vessel; pipes, supply pipes, ducts, intake manifolds, channels, guides, tailraces, headraces, flumes, draft tubes, air intake ducts, combustion engine manifolds, apertures, eyes, nozzles, jets, jet deflectors, valves, check valves, ball valves, globe valves, pin valves, gate valves, valve seats, gates, wicket gates, wicket gate arms, wicket gate links, spear valves, spear tips, penstocks, spiral cases, volutes, strainers, cutwaters, bulkheads, control surfaces, balanced control surfaces, flight control surfaces, wings, slots, flaps, fuselages, fairings, antennae, and domes.
9. An erosion-resistant fluid-handling part according to claim 8 , wherein the fluid-handling part is a hydroelectric turbine.
10. An erosion-resistant fluid-handling part according to claim 1 , wherein the fluid-handling part has a first erosion-resistant coating disposed thereon and wherein a second erosion-resistant coating is disposed on the first erosion-resistant coating.
11. An erosion-resistant fluid-handling part comprising:
hydroelectric turbine;
an epoxy primer composition disposed on the hydroelectric turbine, the epoxy primer composition comprising an epoxy blend, an aliphatic amine, and a silane adhesion promoter;
a coating composition disposed on the epoxy primer composition at a dry film thickness ranging from about 200 μm to about 3000 μm, wherein the coating composition comprises:
a trifunctional silane ranging from about 0.01% by weight to about 20% by weight of the coating composition;
a silanol fluid having a weight average molecular weight ranging from about 4000 g/mol to about 150,000 g/mol and wherein the silanol fluid ranges from about 40% by weight to about 99% by weight of the coating composition; and
fumed silica ranging from about 0.01% by weight to about 25% by weight of the coating composition.
12. An erosion-resistant fluid-handling part according to claim 11 , wherein the coated hydroelectric turbine has a particle-impact erosion rate less tban about 13% of the particle-impact erosion rate of uncoated 1100 aluminum.