Method and device for producing laminated composite
A polyolefin resin drawn sheet 4 is laminated on at least one face of a sheet-form core material 6 having a density of 30 to 300 kgf/m 3 . At this time, a sheet or film 5 made of a bonding synthetic resin or rubber having a flow starting temperature lower than the thermal deformation temperature of the core material 6 and the melting point of the drawn sheet 4 is interposed between the core material 6 and the drawn sheet 4 . The resultant stack product is heated to not less than the flow starting temperature of the synthetic resin or the rubber and not more than the thermal deformation temperature of the core material 6 and the melting point of the drawn sheet 4 . At the same time of or after the heating, the stack product is pressed to apply a compression strain of 0.01 to 10% to the core material 6.
1. A method for producing a laminated composite by laminating a polyolefin resin drawn sheet on at least one face of a sheet-form core material having a density of 30 to 300 kg/m 3 , comprising:
interposing, between the core material and the drawn sheet, a bonding synthetic resin or rubber having a flow starting temperature lower than the thermal deformation temperature of the core material and the melting point of the drawn sheet; heating the synthetic resin or the rubber to not less than the flow starting temperature and not more than the thermal deformation temperature of the core material and the melting point of the drawn sheet before or after the three materials are stacked into a stack product; and pressing the stack product to apply a compression strain of 0.01 to 10% to the core material at the same time of or after the heating.
2. A method for producing a laminated composite by laminating a polyolefin resin drawn sheet on at least one face of a sheet-form core material having a density of 30 to 300 kg/m 3 , comprising:
coating or impregnating a face to be bonded of the core material and/or the drawn sheet with a bonding synthetic resin or rubber having a flow starting temperature lower than the thermal deformation temperature of the core material and the melting point of the drawn sheet; heating the synthetic resin or the rubber to not less than the flow starting temperature thereof and not more than the thermal deformation temperature of the core material and the melting point of the drawn sheet before or after the core material and the drawn sheet are stacked into a stack product; and pressing the stack product to apply a compression strain of 0.01 to 10% to the core material at the same time of or after the heating.
3. A method for producing a laminated composite by laminating a polyolefin resin drawn sheet on at least one face of a sheet-form core material having a density of 30 to 300 kg/m 3 , comprising:
coating or impregnating a face to be bonded of the core material and/or the drawn sheet with a bonding synthetic resin or rubber having a flow starting temperature lower than the thermal deformation temperature of the core material and the melting point of the drawn sheet; stacking the core material and the drawn sheet into a stack product so as to contact each other in the coated face or impregnated face; heating the resultant stack product to not less than the flow starting temperature of the synthetic resin or the rubber and not more than the thermal deformation temperature of the core material and the melting point of the drawn sheet; and pressing the stack product to apply a compression strain of 0.01 to 10% to the core material at the same time of or after the heating.
4. The method for producing a laminated composite according to any of claims 1 , 2 or 3 , wherein when the shrinkage starting temperature of the drawn sheet at the time of the heating is lower than the heating temperature at the time of the laminating, the laminating is performed while a tension of 0.1 to 3 kgf/1 cm-width is applied to the sheet in the orientation direction of the sheet.
5. The method for producing a laminated composite according to any of claims 1 , 2 or 3 , wherein the draw magnification of the sheet is from 5 to 40 times.
6. The method for producing a laminated composite according to any of claims 1 , 2 or 3 , wherein the core material is a resin foamed body in which the average of aspect ratios (Dz/Dxy) of cells is from 1.1 to 4.0.
7. The method for producing a laminated composite according to any of claims 1 , 2 or 3 , wherein as the polyolefin resin drawn sheet, there is used a drawn sheet having a face to be bonded being at least locally heated and melted at a temperature higher than the melting point of the resin by 10° C. or more or being roughened.
8. A method for producing a laminated composite by laminating a polyolefin resin drawn sheet on at least one face of a sheet-form core material having a density of 30 to 300 kg/m 3 , comprising:
interposing, between the core material and the drawn sheet, a bonding layer having a flow starting temperature lower than the thermal deformation temperature of the core material and the melting point of the drawn sheet;
heating the bonding layer to not less than the flow starting temperature and not more than the thermal deformation temperature of the core material and the melting point of the drawn sheet;
stacking the three materials into a stack product; and
pressing the stack product to apply a compression strain of 0.01 to 10% to the core material.