Hot melt adhesive composition based on a random copolymer of isotactic polypropylene

1. A hot melt adhesive composition comprising a blend of the following components:

(a) about 4% to 50% by weight of an isotactic polypropylene random RCP copolymer of propylene and at least one α-olefin comonomer having the following molecular structure:

R—CH═CH 2

where R is hydrogen or a C 2 to C 10 alkyl group, and said α-olefin comprises about 1.5% by weight to about 20% by weight of the said RCP copolymer; wherein said RCP copolymer has a density of about 0.88 g/cc to 0.905 g/cc and a melt flow rate of 1 to 500 g/10 mm and an a melting point equal to or less than 145° C.;

(b) about 20% to 65% by weight of a tackifier;

(c) about 0% to 60% by weight of an atactic poly-α-olefin (APAO) polymer;

(d) about 0% to 40% by weight of a plasticizer;

(e) about 0% to 40% by weight of a wax;

(f) about 0% to 3% by weight of a stabilizer; and

(g) about 0% to 60% by weight of a filler;

the components totaling 100% by weight of the composition.

2. The composition of claim 1 wherein said RCP copolymer is an mRCP copolymer of propylene and at least one α-olefin prepared by using a metallocene catalyst system.

3. The composition of claim 1 wherein said APAO polymer has a density of about 0.85 g/cc to 0.89 g/cc and a glass transition temperature (Tg) of from about −5 to −40° C. and a weight average molecular weight (Mw) of from about 4,000 g/mol to about 150,000 g/mol.

4. The composition of claim 1 wherein the α-olefin comonomer is selected from the group consisting of ethylene, butene-1 and hexene-1.

5. The composition of claim 1 wherein the APAO polymer is a homopolymer or a copolymer of propylene and at least one α-olefin comonomer having the following molecular structure:

R—CH═CH 2

where R is hydrogen, or an alkyl or an aryl radical.

6. The composition of claim 5 wherein the α-olefin comonomer is selected from the group consisting of ethylene, butene-1 and hexene-1.

7. The composition of claim 1 wherein the tackifier is selected from the group consisting of aliphatic and cycloaliphatic hydrocarbon resins and their hydrogenated derivatives, aromatic and hydrogenated aromatic hydrocarbon resins, aromatically modified aliphatic or cycloaliphatic resins and their hydrogenated derivatives, polyterpene and styrenated polyterpene resins.

8. The composition of claim 7 wherein the tackifier has a R&B softening point equal to or greater than 80° C.

9. The composition of claim 8 wherein the tackifier is a C-5 aliphatic hydrocarbon resin.

10. The composition of claim 1 wherein the plasticizer is selected from the group consisting of mineral oil and liquid polybutene.

11. The composition of claim 10 wherein the mineral oil has less than 30% aromatic carbon atoms.

12. The composition of claim 1 wherein said wax is selected from the group consisting of petroleum waxes, low molecular weight polyethylene and polypropylene, synthetic waxes and polyolefin waxes.

13. The composition of claim 12 wherein the said wax is a low molecular weight polyethylene having a number average molecular weight of about 400 to about 6,000 g/mol.

14. The composition of claim 1 further including 0.1% to about 30% by weight of a surfactant.

15. The composition of claim 14 wherein the surfactant has an HLB of less than 15.

16. The composition of claim 14 wherein the surfactant is selected from the group consisting of fatty acid esters, nonionic ethoxylates and ethylene oxide/propylene oxide copolymers.

17. The composition of claim 1 wherein said filler is selected from the group consisting of talc, calcium carbonate, clay, silica, mica, wollastonite, feldspar, aluminum silicate, alumina, hydrated alumina, glass microsphere, ceramic microsphere, thermoplastic microsphere, baryte and wood flour.

18. The composition of claim 1 wherein the adhesive composition further includes a colorant.