Ceramics comprising Al
Ceramics comprising (i) at least one of Nb 2 O 5 or Ta 2 O 5 and (ii) at least two of (a) Al 2 O 3 , (b) REO, or (c) at least one of ZrO 2 or HfO 2 . Embodiments of ceramics according to the present invention can be made, formed as, or converted into optical waveguides, glass beads, articles (e.g., plates), fibers, particles (e.g., abrasive particles), and thin coatings.
1. Glass collectively comprising at least 80 percent by weight of (i) at least one of Nb 2 O 5 or Ta 2 O 5 ,(ii) at least one of ZrO 2 or HfO 2 , and (iii) at least one of Al 2 O 3 or REO, and the glass containing not more than 20 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , with the proviso that the glass does not comprise 35.73 percent by weight Al 2 O 3 , 42.17 percent by weight La 2 O 3 , 17.1 percent by weight ZrO 2 , and 5 percent by weight of one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
2. The glass according to claim 1 , wherein if Al 2 O 3 , REO, and at least one of ZrO 2 or HfO 2 are present, the glass comprises either not greater than 4 or at least 6 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
3. The glass according to claim 1 , wherein if Al 2 O 3 , REO, and at least one of ZrO 2 or HfO 2 are present, the glass comprises at least 6 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
4. The glass according to claim 3 collectively comprising at least 90 percent by weight of (i) at least one of Nb 2 O 5 or Ta 2 O 5 , (ii) at least one of ZrO 2 or HfO 2 , and (iii) at least one of Al 2 O 3 or REO, based on the total weight of the glass.
5. The glass according to claim 3 collectively comprising at least 99 percent by weight of (i) at least one of Nb 2 O 5 or Ta 2 O 5 , (ii) at least one of ZrO 2 or HfO 2 , and (iii) at least one of Al 2 O 3 or REO, based on the total weight of the glass.
6. The glass according to claim 3 collectively having 100 percent by weight of (i) at least one of Nb 2 O 5 or Ta 2 O 5 , (ii) at least one of ZrO 2 or HfO 2 , and (iii) at least one of Al 2 O 3 or REO, based on the total weight of the glass.
7. The glass according to claim 3 collectively comprising at least 70 percent by weight of Al 2 O 3 , REO, and at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
8. The glass according to claim 3 , wherein the at least one of Nb 2 O 5 or Ta 2 O 5 is present in an amount of at least 10 percent by weight, based on the total weight of the glass.
9. The glass according to claim 3 collectively comprising at least 70 percent by weight of REO, at least one of ZrO 2 or HfO 2 , and at least one of Nb 2 O 5 or Ta 2 O 5 .
10. The glass according to claim 9 , wherein the at least one of Nb 2 O 5 or Ta 2 O 5 is present in an amount greater than 5 percent by weight, based on the total weight of the glass.
11. The glass according to claim 9 , wherein the at least one of Nb 2 O 5 or Ta 2 O 5 is present in an amount of at least 10 percent by weight, based on the total weight of the glass.
12. The glass according to claim 3 comprising greater than 5 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight or the glass.
13. The glass according to claim 3 comprising at least 10 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
14. The glass according to claim 3 comprising at least 15 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
15. The glass according to claim 3 comprising at least 20 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
16. The glass according to claim 3 comprising at least 25 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
17. The glass according to claim 3 comprising the at least one of Nb 2 O 5 or Ta 2 O 5 , in a range from 10 to 40 percent by weight, based on the total weight of the glass.
18. The glass according to claim 3 collectively comprising at least 80 percent by weight of Al 2 O 3 , REO, at least one of ZrO 2 or HfO 2 , and at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
19. The glass according to claim 18 , wherein the at least one of ZrO 2 or HfO 2 is present in an amount of at least 5 percent by weight, based on the total weight of the glass.
20. The glass according to claim 18 , wherein the at least one of ZrO 2 or HfO 2 is present in an amount of at least 10 percent by weight, based on the total weight of the glass.
21. A method for making the glass according to claim 3 , the method comprising:
melting sources of (i) at least one of Nb 2 O 5 or Ta 2 O 5 , (ii) at least one of ZrO 2 or HfO 2 , and (iii) at least one of Al 2 O 3 or REO, to provide a melt; and
cooling the melt to provide the glass.
22. An optical waveguide comprising:
a substrate; and
a glass according to claim 3 on a surface of the substrate.
23. The optical waveguide according to claim 22 , wherein the glass is doped with a rare earth dopant.
24. The optical waveguide according to claim 22 wherein the rare earth dopant is selected from the group consisting of cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, or their other compounds and mixtures thereof.
25. An optical waveguide comprising a glass fiber having a core material and a cladding surrounding the core material, wherein the core material comprises a glass according to claim 3 .
26. The optical waveguide according to claim 25 , wherein the glass is doped with a rare earth dopant.
27. The optical waveguide according to claim 23 , wherein the rare earth dopant is selected from the group consisting of cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, or their other compounds, and mixtures thereof.
28. An optical amplifier comprising:
an optical pump source which provides optical pump light; and
an optical waveguide coupled to receive the optical pump light from the optical pump source, wherein the optical waveguide comprises a glass according to claim 3 .
29. The optical amplifier according to claim 28 , wherein the glass is doped with a rare earth dopant.
30. The optical amplifier according to claim 29 , wherein the rare earth dopant is selected from the group consisting of cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, or their other compounds, and mixtures thereof.
31. The glass according to claim 1 in the form of an IR window.
32. Glass collectively comprising at least 97 percent by weight of (i) at least one of Nb 2 O 5 or Ta 2 O 5 and (ii) at least two of (a) Al 2 O 3 , (b) REO, or (c) at least one of ZrO 2 or HfO 2 , and the glass containing not more than 3 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , with the proviso that the glass does not comprise 35.73percent by weight Al 2 O 3 , 42.17 percent by weight La 2 O 3 , 17.1 percent by weight ZrO 2 , and 5 percent by weight of one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.
33. The glass according to claim 32 , wherein if A 2 O 3 , REO, and at least one of ZrO 2 or HfO 2 are present, the glass comprises either not greater than 4 or at least 6 percent by weight of the at least one of Nb 2 O 5 or Ta 2 O 5 , based on the total weight of the glass.