Holey optical fibres of non-silica based glass
To overcome problems of fabricating conventional core-clad optical fibre from non-silica based (compound) glass, it is proposed to fabricate non-silica based (compound) glass optical fibre as holey fibre i.e. one contining Longitudinal holes in the cladding. This removes the conventional problems associated with mismatch of the physical properties of the core and clad compound glasses, since a holey fibre can be made of a single glass composition. With a holey fibre, it is not necessary to have different glasses for the core and cladding, since the necessary refractive index modulation between core and cladding is provided by the microstructure of the clad, i.e. its holes, rather than by a difference in materials properties between the clad and core glasses. Specifically, the conventional thermal mismatch problems between core and clad are circumvented. A variety of fibre types can be fabricated from non-silica based (compounds) glasses, for example: single-mode fibre; photonic band gap fibre; highly non-linear fibre; fibre with photosensitivity written gratings and other refractive index profile structures; and rare-earth doped fibres (e.g. Er, Nd, Pr) to provide gain media for fibre amplifiers and lasers.
1. A method of fabricating compound glass fibre, comprising:
(a) making a holey preform of compound glass; and
(b) drawing the preform in a drawing tower to produce a fibre,
wherein the holey preform is made by stacking together a plurality of compound glass tubes, wherein the tubes are stacked within a larger tube which forms an outer jacket, and wherein the outer jacket is coated with a coating material prior to drawing with a material for stripping cladding modes and/or providing mechanical strength.
2. A method according to claim 1 , wherein the coating material is graphite.
3. A method according to claim 1 , wherein the coating material is a polymer doped with at least one of: graphite, a transition metal selected from the group Ti, V, Cr, Mn, Fe, Co, Ni and Cu; and a rare earth ion selected from the group Pr, Nd, Sm, Tb, Dy, Ho, Er, Tm and Yb.
4. A method according to claim 1 , wherein the coating material is doped with a dopant that exhibits absorption at a transmission wavelength of the compound glass fibre which it is desired to be stripped from the cladding.
5. A method of fabricating compound glass fibre, comprising:
(a) making a holey preform of compound glass; and
(b) drawing the preform in a drawing tower to produce a fibre,
wherein the holey preform is supported by a wiring structure retained for the drawing.
6. A compound glass fiber fabricated according to the method of claim 1 .
7. A compound glass fiber fabricated according to the method of claim 5 .
8. A method according to claim 1 , wherein the drawing tower has a hot zone of at least 2 cm.
9. A method according to claim 5 , wherein the drawing tower has a hot zone of at least 2 cm.
10. A method according to claim 1 , wherein the drawing temperature is less than 1800° C.
11. A method according to claim 5 , wherein the drawing temperature is less than 1800° C.