Flame retardant aromatic polycarbonate resin composition
An aromatic polycarbonate resin composition having: 100 parts by weight of a resin component (A) mainly having an aromatic polycarbonate, 0.1 to 200 parts by weight of a solid inorganic compound (B), at least one compound (C) selected from the group consisting of an organic acid, an organic acid ester, and an organic acid anhydride, 0.001 to 1 part by weight of at least one organic acid metal salt (D) selected from the group consisting of an organic acid alkali metal salt and an organic acid alkaline earth metal salt, and 0.01 to 1 part by weight of a fluoropolymer (E), wherein compound (C) is present in an amount wherein a mixture of compounds (B) and (C) exhibits a pH value of from 4 to 8.
1. An aromatic polycarbonate resin composition comprising:
100 parts by weight of a resin component (A) mainly comprising an aromatic polycarbonate,
0.1 to 200 parts by weight of a solid inorganic compound (B),
at least one compound (C) selected from the group consisting of an organic acid, an organic sulfonic acid ester, and an organic monomeric acid anhydride,
0.001 to 1 part by weight of at feast one organic acid metal salt (D) selected from the group consisting of an organic acid alkali metal salt and an organic acid alkaline earth metal salt, and
0.01 to 1 part by weight of a fluoropolymer (E),
wherein said compound (C) is present in an amount wherein a mixture of said inorganic compound (B) and said compound (C) exhibits a pH value of from 4 to 8.
2. The aromatic polycarbonate resin composition according to claim 1 , wherein said solid inorganic compound (B) is at least one silicate compound selected from the group consisting of a plate-shaped silicate compound, a needle-shaped silicate compound and a fibrous silicate compound.
3. The aromatic polycarbonate resin composition according to claim 2 , wherein said at least one silicate compound is selected from the group consisting of talc, mica, a glass flake and a glass fiber.
4. The aromatic polycarbonate resin composition according to claim 3 , wherein said at least one silicate compound is selected from the group consisting of talc and mica.
5. The aromatic polycarbonate resin composition according to claim 1 , wherein said compound (C) is selected from the group consisting of an organic sulfonic acid, an organic sulfonic acid ester, and an organic carboxylic acid.
6. The aromatic polycarbonate resin composition according to claim 1 , wherein the amount of said solid inorganic compound (B) is 1 to 20 parts by weight.
7. An injection molded article comprising the aromatic polycarbonate resin composition of any one of claims 1 to 6 .
8. An extrusion molded article comprising the aromatic polycarbonate resin composition of any one of claims 1 to 6 .
9. The aromatic polycarbonate resin composition according to claim 1 , wherein the amount of said compound (C) is frpm 0.02 to 0.5 part by weight.