Fuel cell, electrode for fuel cell and a method of manufacturing the same
An electrode for a fuel cell, including a porous catalytic carrier including conductive fibers having two particle diameter distribution peaks of a first particle diameter distribution peak existing at a small particle diameter side and a second particle diameter distribution peak existing at a large particle diameter side, wherein said conducting fibers are carbon nano-fibers formed from a catalyst for formation prepared by preparing a mixed powder including one or more of a reducible metallic oxide powder and a non-reducible metallic oxide powder, mixing and pulverizing the mixed powder, and heating the mixed powder under reducing atmosphere; catalyst to be carried on said conductive fibers belonging to the first particle diameter distribution peak; and a proton conductive material adhered on surface of at least the conducive fibers belonging to the first particle diameter distribution peak, so as to come into contact with the catalyst.
1. An electrode for a fuel cell comprising:
a film including:
carbon nano-fibers having particle diameters of 5–1000 nm and an aspect ratio of particle diameter to particle length of from 1:10 to 1:1000;
aluminum oxide powder;
fuel cell catalyst carried on a surface of said carbon nano-fibers; and
ion conductive material.
2. An electrode for a fuel cell comprising:
a film formed on a current collector, the film including:
carbon nano-fibers having a particle diameter of 5–1000 nm and an aspect ratio of particle diameter to particle length of from 1:10 to 1:1000;
aluminum oxide powder;
fuel cell catalyst carried on the surface of said carbon nano-fibers; and
ion conductive material.
3. An electrode for a fuel cell comprising:
a proton electrolyte layer;
an electrode including a film, the film including:
carbon nano-fibers formed on opposing surfaces of said proton electrolyte layer, the carbon nano-fibers having a particle diameter of 5–1000 nm and an aspect ratio of particle diameter to particle length of from 1:10 to 1:1000;
aluminum oxide particles;
fuel cell catalyst carried on a surface of said carbon nano-fibers; and
ion conductive material.
4. An electrode for a fuel cell according to claim 1 ,
wherein said carbon nano-fibers have two particle diameter distribution peaks of a first particle diameter distribution peak existing at a small particle diameter side and a second particle diameter distribution peak existing at a large particle diameter side, and are formed from the catalyst for formation prepared by process comprising the steps of, preparing a mixed powder comprising one or more reducible metallic oxide power and aluminum oxide powder, mixing and pulverizing said mixed powder, and heating said mixed powder under reducing atmosphere;
said fuel cell catalyst are carried on said carbon nano-fibers belonging to said first particle diameter distribution peak; and
said ion conductive material is a proton conductive material adhered on surface of at least said carbon nano-fibers belonging to said first particle diameter distribution peak, so as to come into contact with said fuel cell catalyst.
5. An electrode for a fuel cell according to claim 2 , further comprising:
wherein said carbon nano-fibers have two particle diameter distribution peaks of a first particle diameter distribution peak existing at a small particle diameter side and a second particle diameter distribution peak existing at a large particle diameter side, and are formed from the catalyst for formation prepared by process comprising the steps of, preparing a mixed powder comprising one or more reducible metallic oxide powder and aluminum oxide powder, mixing and pulverizing said mixed powder, and heating said mixed powder under reducing atmosphere;
said fuel cell catalyst are carried on said carbon nano-fibers belonging to said first particle diameter distribution peak; and
said ion conductive material is a proton conductive material adhered on surface of at least said carbon nano-fibers belonging to said first particle diameter distribution peak, so as to come into contact with said fuel cell catalyst.
6. An electrode for a fuel cell according to claim 3 , further comprising:
wherein said carbon nano-fibers have two particle diameter distribution peaks of a first particle diameter distribution peak existing at a small particle diameter side and a second particle diameter distribution peak existing at a large particle diameter side, and are formed from the catalyst for formation prepared by process comprising the steps of, preparing a mixed powder comprising one or more reducible metallic oxide powder and aluminum oxide powder, mixing and pulverizing said mixed powder, and heating said mixed powder under reducing atmosphere;
said fuel cell catalyst are carried on said carbon nano-fibers belonging to said first particle diameter distribution peak; and
said ion conductive material is a proton conductive material adhered on surface of at least said carbon nano-fibers belonging to said first particle diameter distribution peak, so as to come into contact with said fuel cell catalyst.
7. An electrode for a fuel cell according to claim 3 , further comprising:
transition metal powder and/or alloy powder;
wherein said transition metal is at least one selected from the group consisting of nickel, copper, and ion;
said alloy is at least one selected from an alloy of one metal chosen from the group consisting of nickel, copper and iron and the other metal chosen from the group consisting of copper, silver and manganese.