Viscoelastic polyurethane foam
The subject invention provides a viscoelastic polyurethane foam having a density of from one to twenty pounds per cubic foot. The foam is formed from a composition that is a reaction product of an isocyanate component (A), a first polyether polyol (B), a second polyether polyol (C), and a chain extender (D). The chain extender (D) has a backbone chain with from two to eight carbon atoms and has a weight-average molecular weight of less than 1,000 and is present in an amount of from 5 to 50 parts by weight based on 100 parts by weight of the composition. The viscoelastic polyurethane foam a first glass transition temperature greater than zero and a second glass transition temperature less than zero and having a tan delta peak ratio of the first glass transition temperature to the second glass transition temperature less than 2.2.
1. A viscoelastic polyurethane foam comprising a reaction product of:
(A) an isocyanate component;
(B) a first polyether polyol having;
(i) a hydroxyl number of from 20 to 60 mg KOH/g,
(ii) a plurality of internal blocks formed from oxyalkylene monomers comprising a random heteric mixture of ethylene oxide and propylene oxide with said internal blocks having at most 20% by weight ethylene oxide based on a total weight of said oxyalkylene monomers in said internal blocks, and
(iii) a plurality of terminal caps attached to said plurality of internal blocks and comprising at most 25% by weight ethylene oxide based on a total weight of said first polyether polyol;
(C) a second polyether polyol having;
(i) a hydroxyl number of from 20 to 200 mg KOH/g,
(ii) a plurality of internal blocks formed from oxyalkylene monomers,
(iii) a plurality of terminal caps attached to said plurality of internal blocks, and
(iv) at least 50% by weight ethylene oxide based on the total weight of the second polyether polyol;
wherein said first polyether polyol (B) is reacted in an amount of from 50 to 65% by weight, and said second polyether polyol (C) is reacted in an amount of from 35 to 50% by weight, both based on the total weight of the first and the second polyether polyols;
(D) a chain extender present in an amount of from 3 to 20 parts by weight based on the total weight of (A), (B), (C), and (D) and having;
(i) a backbone chain with from two to eight carbon atoms, and
(ii) a weight-average molecular weight of from 25 to 250; and
said foam having a density of from 1 to 20 pounds per cubic foot and having a first glass transition temperature greater than zero degrees Celsius and a second glass transition temperature less than zero degrees Celsius and having a tan delta peak ratio of said first glass transition temperature to said second glass transition temperature less than 2.2.
2. A viscoelastic polyurethane foam as set forth in claim 1 wherein said terminal caps of said second polyether polyol (C) comprise at least 30% by weight ethylene oxide based on the total weight of said second polyether polyol (C).
3. A viscoelastic polyurethane foam as set forth in claim 1 wherein said second polyether polyol (C) comprises at least 60% by weight ethylene oxide based on the total weight of the second polyether polyol (C).
4. A viscoelastic polyurethane foam as set forth in claim 1 wherein said first polyether polyol (B) has a hydroxyl number of from 20 to 30 mg KOH/g.
5. A viscoelastic polyurethane foam as set forth in claim 1 wherein said first polyether polyol (B) comprises at most 13% by weight ethylene oxide based on the total weight of said oxyalkylene monomers in said internal blocks.
6. A viscoelastic polyurethane foam as set forth in claim 1 wherein said terminal caps of said first polyether polyol (B) comprise at most 20% by weight ethylene oxide based on the total weight of said first polyether polyol (B).
7. A viscoelastic polyurethane foam as set forth in claim 1 wherein said first glass transition temperature is further defined as from 15 to 70° C.
8. A viscoelastic polyurethane foam as set forth in claim 7 wherein said second glass transition temperature is further defined as from −40 to −60° C.
9. A viscoelastic polyurethane foam as set forth in claim 1 having a density of from 1.8 to 10 pounds per cubic foot.
10. A viscoelastic polyurethane foam as set forth in claim 1 wherein said chain extender (D) has a weight-average molecular weight of less than 100.
11. A viscoelastic polyurethane foam as set forth in claim 1 wherein said chain extender (D) has two isocyanate-reactive groups.
12. A viscoelastic polyurethane foam as set forth in claim 11 wherein said chain extender (D) is selected from at least one of 1,4-butanediol, 1,3-butanediol, 2,3-butanediol, 1,2-butanediol, 1,3-propylene glycol, 1,5-pentanediol, ethylene glycol, diethylene glycol, and polyethylene glycols having a weight-average molecular weight of up to 200.
13. A viscoelastic polyurethane foam as set forth in claim 1 wherein said isocyanate component (A) is further defined as an isocyanate-terminated prepolymer.
14. A viscoelastic polyurethane foam as set forth in claim 13 wherein said prepolymer comprises a reaction product of an isocyanate and a prepolymer polyol having a weight-average molecular weight greater than 1,000, said prepolymer polyol being used in an amount of from 1 to 20 parts by weight based on 100 parts by weight of said isocyanate component (A).
15. A composition for use in forming a viscoelastic polyurethane foam having a density of from 1 to 20 pounds per cubic foot, said composition comprising:
(A) an isocyanate component;
(B) a first polyether polyol having;
(i) a hydroxyl number of from 20 to 60 mg KOH/g,
(ii) a plurality of internal blocks formed from oxyalkylene monomers comprising a random heteric mixture of ethylene oxide and propylene oxide with said internal blocks having at most 20% by weight ethylene oxide based on a total weight of said oxyalkylene monomers in said internal blocks,
(iii) a plurality of terminal caps attached to said plurality of internal blocks and comprising at most 25% by weight ethylene oxide based on a total weight of said first polyether polyol;
(C) a second polyether polyol having;
(i) a hydroxyl number of from 20 to 200 mg KOH/g,
(ii) a plurality of internal blocks formed from oxyalkylene monomers,
(iii) a plurality of terminal caps attached to said plurality of internal blocks,
(iv) at least 50% by weight ethylene oxide based on the total weight of the second polyether polyol (C);
(D) a chain extender having;
(i) a backbone chain with from two to eight carbon atoms,
(ii) a weight-average molecular weight of from 25 to 250, and wherein said chain extender is present in an amount of from 3 to 20 parts by weight based on 100 parts by weight of said composition and wherein said first polyether polyol (B) is present in an amount of from 50 to 65% by weight, and said second polyether polyol (C) is present in an amount of from 35 to 50% by weight, both based on the total weight of the first and the second polyether polyols to produce the viscoelastic polyurethane foam having a first glass transition temperature greater than zero degrees Celsius and a second glass transition temperature less than zero degrees Celsius.
16. A composition as set forth in claim 15 wherein said terminal caps of said second polyether polyol (C) comprise at least 30% by weight ethylene oxide based on the total weight of said second polyether polyol (C).
17. A composition as set forth in claim 15 wherein said second polyether polyol (C) comprises at least 60% by weight ethylene oxide based on the total weight of the second polyether polyol (C).
18. A composition as set forth in claim 15 wherein said first polyether polyol (B) has a hydroxyl number of from 20 to 30 mg KOH/g.
19. A composition as set forth in claim 15 wherein said first polyether polyol (B) comprises at most 13% by weight ethylene oxide based on the total weight of said oxyalkylene monomers in said internal blocks.
20. A composition as set forth in claim 15 wherein said terminal caps of said first polyether polyol (B) comprises at most 20% by weight ethylene oxide based on the total weight of said first polyether polyol (B).
21. A composition as set forth in claim 15 wherein said isocyanate component (A) has an isocyanate index of from 75 to 100.
22. A composition as set forth in claim 15 wherein said isocyanate component (A) has an isocyanate index of from 75 to 90.
23. A composition as set forth in claim 15 wherein said chain extender (D) has a weight-average molecular weight of less than 100.
24. A composition as set forth in claim 15 wherein said chain extender (D) is selected from at least one of 1,4-butanediol, 1,3-butanediol, 2,3-butanediol, 1,2-butanediol, 1,3-propylene glycol, 1,5-pentanediol, and ethylene glycol, diethylene glycol, and polyethylene glycols having a weight-average molecular weight of up to 200.
25. A composition as set forth in claim 15 wherein said isocyanate component (A) comprises an isocyanate-terminated prepolymer.
26. A composition as set forth in claim 25 wherein said prepolymer comprises a reaction product of an isocyanate and a prepolymer polyol having a weight-average molecular weight greater than 1,000, said polyol present in an amount of from 1 to 20 parts by weight based on 100 parts by weight of said isocyanate component (A).
27. A method of forming a viscoelastic polyurethane foam comprising the steps of:
providing an isocyanate component (A);
providing a first polyether polyol (B) having;
(i) a hydroxyl number of from 20 to 60 mg KOH/g,
(ii) a plurality of internal blocks formed from oxyalkylene monomers comprising a random heteric mixture of ethylene oxide and propylene oxide with the internal blocks having at most 20% by weight ethylene oxide based on a total weight of the oxyalkylene monomers in the internal blocks,
(iii) a plurality of terminal caps attached to the plurality of internal blocks and comprising at most 25% by weight ethylene oxide based on the total weight of the first polyether polyol (B);
providing a second polyether polyol (C) having;
(i) a hydroxyl number of from 20 to 200 mg KOH/g,
(ii) a plurality of internal blocks formed from oxyalkylene monomers,
(iii) a plurality of terminal caps attached to the plurality of internal blocks,
(iv) at least 50% by weight ethylene oxide based on the total weight of the second polyether polyol (C);
wherein the first polyether polyol (B) is provided in an amount of from 50 to 65% by weight, and the second polyether polyol (C) is provided in an amount of from 35 to 50% by weight, both based on the total weight of the first and the second polyether polyols;
providing a chain extender (D) having;
(i) a backbone chain with from two to eight carbon atoms,
(ii) a weight-average molecular weight of from 25 to 250,
wherein the chain extender (D) is used in an amount of from 3 to 20 parts by weight based on 100 parts by weight of the foam; and
reacting the isocyanate component (A), the first (B) and the second (C) polyether polyols, and the chain extender (D) to form the foam having a density of from 1 to 20 pounds per cubic foot and having a first glass transition temperature greater than zero degrees Celsius and a second glass transition temperature less than zero degrees Celsius and having a tan delta peak ratio of the first glass transition temperature to the second glass transition temperature less than 2.2.
28. A method as set forth in claim 27 wherein the second polyether polyol (C) has the terminal caps comprising at least 30% by weight ethylene oxide based on the total weight of the second polyether polyol (C).
29. A method as set forth in claim 27 wherein the second polyether polyol (C) comprises at least 60% by weight ethylene oxide based on the total weight of the second polyether polyol (C).
30. A method as set forth in claim 27 wherein the first polyether polyol (B) has a hydroxyl number of from 20 to 30 mg KOH/g.
31. A method as set forth in claim 27 wherein the first polyether polyol (B) comprises at most 13% by weight ethylene oxide based on the total weight of the oxyalkylene monomers in the internal blocks.
32. A method as set forth in claim 27 wherein the terminal caps of the first polyether polyol (B) comprises at most 20% by weight ethylene oxide based on the total weight of the first polyether polyol (B).
33. A method as set forth in claim 27 wherein said chain extender (D) has a weight-average molecular weight of less than 100.
34. A method as set forth in claim 27 wherein said chain extender (D) is selected from at least one of 1,4-butanediol, 1,3-butanediol, 2,3-butanediol, 1,2-butanediol, 1,3-propylene glycol, 1,5-pentanediol, and ethylene glycol, diethylene glycol, and polyethylene glycols having a weight-average molecular weight of up to 200.
35. A method as set forth in claim 27 wherein the first glass transition temperature is further defined as from 15 to 70° C.
36. A method as set forth in claim 35 wherein the second glass transition temperature is further defined as from −40 to −60° C.
37. A method as set forth in claim 27 further comprising the step of spraying the isocyanate component (A), the first (B) and the second (C) polyether polyols, and the chain extender (D) into a mold to form the viscoelastic polyurethane foam.