Polyester resin emulsion and two-component aqueous paint
The present invention relates to a hydroxy-functional polyester resin, which is obtainable by reaction of a composition, which contains (i) a low-molecular polyvalent alcohol having at least two hydroxyl groups per molecule, (ii) a polyether polyol, (iii) a monofunctional saturated aliphatic, cycloaliphatic or aromatic carboxylic acid, and (iv) a polycarboxylic acid having at least two carboxyl groups. The invention further relates to a resin emulsion and a mother paint comprising an aqueous emulsion of the polyester resin, a two-component water-based paint system, comprising the resin emulsion or the mother paint and an isocyanate component as well as a method for the preparation of the water-based paint system.
1. A two-component water-based paint system, comprising:
a polyester resin component (A) that is an aqueous emulsion of a hydroxy-functional polyester resin, which does not contain any ethylenically unsaturated monofunctional carboxylic acid moieties, and which is obtained by reaction of a composition, which comprises
(i) at least one low-molecular polyvalent alcohol having at least two hydroxyl groups per molecule,
(ii) at least one polyether polyol,
(iii) at least one monofunctional saturated aliphatic, cycloaliphatic or aromatic carboxylic acid, and
(iv) at least one polycarboxylic acid having at least two carboxyl groups; and
an isocyanate component (B);
the polyester resin component (A) and the isocyanate component (B) being provided as separate components suitable for mixing together by an applicator for application to a substrate, the resulting mixture having a pot life such that the mixture must be applied to the substrate before the hydroxy-functional polyester resin and the isocyanate component have fully reacted, wherein the resin is additionally modified by reaction with isocyanate prior to mixing the polyester resin component (A) and the isocyanate component (B) to form a mixed paint system.
2. The two-component water-based paint system according to claim 1 , wherein said component (i) is a mixture of at least two different polyols each having at least two hydroxyl groups per molecule and the average functionality is at least 2.0.
3. The two-component water-based paint system according to claim 1 , wherein said component (iii) is selected from compounds of the general formula
R 2 —COOR′
wherein R 2 is an aromatic, optionally substituted by straight-chain or branched alkyl groups, hydrocarbon group or a straight-chain or branched saturated aliphatic or cycloaliphatic hydrocarbon group, and R′ is a hydrogen atom, a straight-chain or branched C 1 -C 4 alkyl group or a —(CO)R 2 group.
4. The two-component water-based paint system according to claim 1 , wherein said component (iii) is a mixture of at least two different saturated monocarboxylic acids.
5. The two-component water-based paint system according to claim 1 , wherein said component (iv) is a mixture of at least two different polycarboxylic acids having each at least two carboxyl groups per molecule, and the average functionallity is at least 2.0.
6. The two-component water-based paint system according to claim 1 , wherein the composition has 10 to 40 wt % of component (i), 3 to 15 wt % of component (ii), 10 to 40 wt % of component (iii) and 10 to 40 wt of component (iv).
7. The two-component water-based paint system according to claim 1 , wherein the amount of hydroxyl of the resin is in the range of 1 to 8 wt %.
8. A method of painting a substrate comprising
a) providing an aqueous emulsion of a hydroxy-functional polyester resin, which does not contain any ethylenically unsaturated monofunctional carboxylic avid moieties which contains
(i) at least one low-molecular polyvalent alcohol having at least two hydroxyl groups per molecule,
(ii) at least one polyether polyol,
(iii) at least one monofunctional saturated aliphatic, cycloaliphatic or aromatic carboxylic acid, and
(iv) at least one polycarboxylic acid having at least two carboxyl groups;
b) providing an isocyanate component;
c) mixing die aqueous emulsion with the isocyanate component to form a mixed paint system; and
d) applying the mixed paint system to a substrate before the hydroxy-functional polyester resin and the isocyanate component have fully reacted.
9. The method according to claim 8 , wherein said component (i) is a mixture of at least two different polyols each having at least two hydroxyl groups per molecule and the average functionality is at least 2.0.
10. The method according to claim 8 , wherein said component (iii) is selected from compounds of the general formula
R 2 —COOR′
wherein R 2 is an aromatic, optionally substituted by straight-chain or branched alkyl groups, hydrocarbon group or a straight-chain or branched saturated aliphatic or cycloaliphatic hydrocarbon group, and R′ is a hydrogen atom, a straight-chain or branched C 1 -C 4 alkyl group or a —(CO)R 2 group.
11. The method according to claim 8 , wherein said component (iii) is a mixture of at least two different saturated monocarboxylic acids.
12. The method according to claim 8 , wherein said component (iv) is a mixture of at least two different polycarboxylic acids having each at least two carboxyl groups per molecule, and the average functionality is at least 2.0.
13. The method according to claim 8 , wherein the composition has 10 to 40 wt % of component (i), 3 to 15 wt % of component (ii), 10 to 40 wt % of component (iii) and 10 to 40 wt % of component (iv).
14. The method according to claim 8 , wherein the amount of hydroxyl of the resin is in the range of 1 to 8 wt %.
15. The method according to claim 8 , wherein the hydroxy-functional polyester resin is additionally modified by reaction with isocyanate prior to mixing the aqueous emulsion with the isocyanate component to form a mixed paint system.