Process and apparatus for production of water-absorbent resin
There is disclosed a process to uniformly and rapidly carry out the mixing of a monomer liquid and a polymerization initiator and thus for the resulting polymer not to adhere to the inner surface of the piping or the inside of the apparatus in an art of producing a water-absorbent resin by continuously mixing the monomer liquid and the polymerization initiator together and thereby carrying out polymerization. This process comprises the steps of: (a) continuously supplying a monomer liquid 20 to such as a supply pipe 10 to continuously stir the monomer liquid 20 in the supply pipe 10 with such as a stirring apparatus 12 ; (b) causing a polymerization initiator 30 to join into a flow of the monomer liquid 20 being in a stirred state, thereby obtaining a mixed liquid 40 of the monomer liquid 20 and the polymerization initiator 30 ; and (c) continuously supplying the mixed liquid 40 from the supply pipe line 10 to a polymerization apparatus to cause the mixed liquid 40 to run a polymerization reaction.
1. A process for production of a water-absorbent resin, which comprises the steps of mixing a monomer liquid with a polymerization initiator and then polymerizing the resultant mixture, thereby producing the water-absorbent resin; with the process further comprising the steps of:
(a) continuously supplying the monomer liquid to a supply pipe line having a flow path to continuously stir a flow of the monomer liquid in the supply pipe line by continuously passing the flow of the monomer liquid through a static mixer in the flow path of the supply pipe line so that the flow of the monomer liquid is in a stirred state downstream of the static mixer while continuously passing through the supply pipe line;
(b) causing the polymerization initiator to join into a flow of the monomer liquid being in a stirred state, thereby obtaining a mixed liquid of the monomer liquid and the polymerization initiator downstream of the static mixer; and
(c) continuously supplying the mixed liquid from the supply pipe line to a polymerization apparatus to cause the mixed liquid to run a polymerization reaction.
2. A process for production of a water-absorbent resin according to claim 1 , wherein, in the step (a), a monomer liquid having a concentration of not less than 40 weight % is used as the monomer liquid.
3. A process for production of a water-absorbent resin according to claim 1 , wherein, in the step (a), a monomer liquid having a liquid temperature of not lower than 50° C. is used as the monomer liquid.
4. A process for production of a water-absorbent resin according to claim 1 , wherein, in the step (a), the monomer liquid is stirred until its stirring Reynolds number reaches not smaller than 50.
5. The process of claim 1 , wherein said supply pipe line has an inlet end and an outlet end, and wherein said static mixer is positioned between said inlet end and said outlet end, said process comprising passing the monomer liquid through the static mixer to produce a vortical flow downstream of the static mixer sufficient to mix with the polymerization initiator.
6. The process of claim 5 , further comprising continuously supplying the monomer liquid in a vortical flow to the polymerization apparatus.
7. The process of claim 5 , further comprising introducing the polymerization initiator in a center portion of the supply pipe line.
8. The process of claim 5 , further comprising introducing the polymerization initiator in a peripheral portion of the supply pipe line.
9. The process of claim 1 , further comprising an initiator feed pipe positioned within the supply pipe line and having an outlet end facing an outlet end of the supply pipe line, the process comprising introducing the polymerization initiator into the monomer liquid in the direction of the flow of the monomer liquid.
10. The process of claim 1 , wherein said static mixer is an inline structure having fixed spiral stirring blades, said process comprising continuously passing the monomer liquid through the static mixer to produce the stirred state, and thereafter introducing the polymerization initiator into the monomer liquid.