Nickel Hydroxide electrode material with improved microstructure and method for making the same
Nickel hydroxide material comprising particles with a microstructure including crystallites of less than 103 Å as measured in the 101 direction by x-ray diffraction. A method of making positive electrode material for use in an alkaline rechargeable electrochemical cell comprising forming a metal ion solution and increasing the pH to precipitate positive electrode material with a crystallite structure of 120 Å or less in the 101 direction.
1. A process for making nickel hydroxide positive electrode material for use in an alkaline rechargeable electrochemical cell comprising forming a metal ion solution by combining a metal ion solution with nickel, NH 4 OH, and NaOH in a reactor at a pH, agitating the combination and controlling the pH to precipitate positive electrode material with a crystallite structure of 120 Å or less in the 101 direction in a single reactor wherein the metal ion solution includes at least two modifiers selected from the group consisting of Al, Bi, Ca, Co, Cr, Cu, Fe, In, La, rare earth elements, Mg, Mn, Ru, Sb, Sn, Ti, Ba, Si, Sr and Zn.
2. The process of claim 1 , wherein the beginning pH is 8-12.
3. The process of claim 1 wherein the process is controlled to produce a modified nickel hydroxide material with a crystallite structure of 60-103 Å.
4. The process of claim 3 wherein the process is controlled to produce modified nickel hydroxide having a tap density of over 2.2 grams per cubic centimeter.
5. The process of claim 3 wherein the process is controlled to produce modified nickel hydroxide material having a loading over 2.7 grams per cubic centimeter.
6. The process of claim of claim 3 wherein the process is controlled to produce modified nickel hydroxide material having a capacity of over 185 mAh/g.
7. The process of claim 1 wherein the process is controlled to produce a modified nickel hydroxide material with a crystallite structure of 60-100 Å.
8. The process of claim 1 , wherein the process is controlled to produce modified nickel hydroxide material having crystallites that have a strained lattice.
9. The process of claim 1 wherein the process is controlled to produce substantially spherical modified nickel hydroxide material.
10. The process of claim 1 wherein the process is controlled to produce modified nickel hydroxide material selected from the group consisting of Ni—Co—Zn, Ni—Co—Zn—Mg—Ca; Ni—Co—Zn—Mn—Mg—Ca, Ni—Co—Zn—Mg—Ca—Cu—Mn.
11. The process of claim 1 wherein the process is controlled to produce modified nickel hydroxide material having at least three modifiers selected from the group consisting of Al, Bi, Ca, Co, Cr, Cu, Fe, In, La, rare earth elements, Mg, Mn, Ru, Sb, Ti, Ba, Si, Sr, and Zn.
12. The process of claim 1 wherein the process is controlled to produce NiOH material having a full width at half maximum of the 101 peak that is from 0.75 to 1 as measured by XRD with CuKA radiation, diffractional beam curved graphic monochromator, (1) degree divergent (1) degree scattering (0.2) mm receiving slits in theta/2 theta geometry.
13. The process of claim 1 wherein the process further includes controlling a liquid phase and a vapor phase ammonia concentration.
14. The process of claim 1 wherein the process is controlled to produce nickel hydroxide material particles with a microstructure comprising crystallites of less than 103 Å as measured in the 101 direction by x-ray diffraction.