Plating solution for electroless deposition of copper
An electroless copper plating solution is disclosed herein. The solution includes an aqueous copper salt component, an aqueous cobalt salt component, a triamine based complexing agent, and an acidic pH-modifying substance in an amount sufficient to make the electroless copper plating solution acidic. A method of preparing an electroless copper solution is also provided.
1. An electroless copper plating solution, comprising:
an aqueous copper salt component;
an aqueous cobalt salt component;
a complexing agent that is a triamine compound; and
a pH-modifying substance in an amount sufficient to make the electroless copper plating solution acidic, wherein, the pH-modifying substance is selected from a group consisting of sulfuric acid, nitric acid, hydrochloric acid, fluoroboric acid, and acetic acid.
2. The electroless copper plating solution, as recited in claim 1 , wherein,
the aqueous copper salt component is selected from a group of copper salts consisting of copper(II) sulfate, copper(II) nitrate, copper(II) chloride, copper(II) tetrafluoroborate, and copper(II) acetate.
3. The electroless copper plating solution, as recited in claim 1 , wherein,
the aqueous copper salt component is selected from a group of complex copper salts consisting of ethylenediamine copper(II) sulfate, bis(ethylenediamine) copper(II) sulfate, diethylenetriamine copper(II) nitrate, and bis(diethylenetriamine) copper(II) nitrate.
4. The electroless copper plating solution, as recited in claim 1 , wherein,
the aqueous cobalt salt component is selected from a group consisting of cobalt(II) sulfate, cobalt(II) nitrate, cobalt(II) chloride, cobalt(II) tetrafluoroborate, and cobalt(II) acetate.
5. The electroless copper plating solution, as recited in claim 1 , wherein, the triamine compound is selected from a group consisting of diethylenetriamine, dipropylenetriamine, and ethylene propylenetriamine.
6. The electroless copper plating solution, as recited in claim 1 , wherein, a pH of the electroless copper plating solution is between about 4.3 and about 4.6.
7. An electroless copper plating solution, comprising:
an aqueous copper salt component having a concentration between about 0.001 molarity (M) to a solubility limit for the aqueous copper salt component;
an aqueous cobalt salt component;
a complexing agent that is a triamine compound; and
a pH-modifying substance in an amount sufficient to make the electroless copper plating solution acidic, wherein the pH-modifying substance is selected from a group consisting of sulfuric acid, nitric acid, hydrochloric acid, fluoroboric acid, and acetic acid.
8. The electroless copper plating solution, as recited in claim 7 , wherein the pH-modifying substance is a buffer adjusting the electroless copper plating solution to a pH of between about 4.0 and about 6.4.
9. The electroless copper plating solution, as recited in claim 7 , wherein,
the aqueous copper salt component is selected from a group consisting of copper(II) sulfate, copper(II) nitrate, copper(II) chloride, copper(II) tetrafluoroborate, and copper(II) acetate.
10. The electroless copper plating solution, as recited in claim 7 , wherein,
the aqueous cobalt salt component is selected from a group consisting of cobalt(II) sulfate, cobalt(II) nitrate, cobalt(II) chloride, cobalt(II) tetrafluoroborate, and cobalt(II) acetate.
11. An electroless copper plating solution, comprising:
an aqueous copper salt component;
an aqueous cobalt salt component having a concentration between about 0.001 molarity (M) to a solubility limit for the aqueous cobalt salt component;
a complexing agent that is a triamine compound; and
a pH-modifying substance in an amount sufficient to make the electroless copper plating solution acidic, wherein a pH of the electroless copper plating solution is between about 4.0 and about 6.4.
12. The electroless copper plating solution, as recited in claim 11 , wherein, the aqueous copper salt component is selected from a group consisting of copper(II) sulfate, copper(II) nitrate, copper(II) chloride, copper(II) tetrafluoroborate, and copper(II) acetate.
13. The electroless copper plating solution, as recited in claim 11 , wherein, the aqueous cobalt salt component is selected from a group consisting of cobalt(II) sulfate, cobalt(II) nitrate, cobalt(II) chloride, cobalt(II) tetrafluoroborate, and cobalt(II) acetate.
14. An electroless copper plating solution, comprising:
an aqueous copper salt component;
an aqueous cobalt salt component;
a complexing agent that is a triamine compound, wherein the complexing agent has a concentration between about 0.005 molarity (M) to about 10.0M; and
a pH-modifying substance in an amount sufficient to make the electroless copper plating solution acidic, wherein a pH of the electroless copper plating solution is between about 4.0 and about 6.4.
15. The electroless copper plating solution, as recited in claim 14 , wherein, the electroless copper plating solution is prepared by mixing a first mixture with a second mixture, wherein,
the first mixture consists essentially of the aqueous copper salt component, the pH modifying substance, and a portion of the complexing agent; and
the second mixture consists essentially of the aqueous cobalt salt component and a remainder of the complexing agent.
16. The electroless copper plating solution, as recited in claim 14 , wherein, the electroless copper plating solution is prepared by sequentially combining the aqueous copper salt component to a volume of water, then adding the pH-modifying substance to the aqueous copper salt component/water combination, thereafter adding the complexing agent, and lastly adding the aqueous cobalt salt component.
17. A method for preparing an electroless copper plating solution comprising:
combining an aqueous copper salt component, a portion of a complexing agent and an acid as a first component;
combining an aqueous cobalt salt component and a remaining portion of the complexing agent as a second component; and
mixing the first component and the second component prior to use in a deposition operation.
18. The method for preparing an electroless copper plating solution, as recited in claim 17 , wherein,
the aqueous copper salt component is selected from a group consisting of copper(II) sulfate, copper(II) nitrate, copper(II) chloride, copper(II) tetrafluoroborate, and copper(II) acetate.
19. The method for preparing an electroless copper plating solution, as recited in claim 17 , wherein,
the aqueous cobalt salt component is selected from a group consisting of cobalt(II) sulfate, cobalt(II) nitrate, cobalt(II) chloride, cobalt(II) tetrafluoroborate, and cobalt(II) acetate.
20. The method for preparing an electroless copper plating solution, as recited in claim 17 , wherein, the complexing agent is a triamine compound.