Method for preparing latex containing pigment copolymerized with a crystalline polymer
A method of preparing a latex that includes pigments copolymerized with a crystalline polymer includes: dispersing a pigment and a dispersing agent in water having an ultra-high purity to obtain a pigment dispersion; dissolving a crystalline monomer in a basic monomer mixture to obtain an organic phase; dissolving while heating the dispersing agent in water having an ultra-high purity, and then mixing the solution with the pigment dispersion to obtain an aqueous phase; mixing and agitating the organic phase and the aqueous phase to obtain a homogenized solution; agitating and heating the homogenized solution; adding a polymerization initiator to the homogenized solution to be reacted; and cooling the reaction solution to room temperature.
1. A method of preparing a latex containing pigments copolymerized with a crystalline polymer comprising:
dispersing a pigment and a dispersing agent in water having an ultra-high purity to obtain a pigment dispersion;
dissolving a crystalline monomer in a basic monomer mixture to obtain an organic phase;
dissolving, while heating, the dispersing agent in water having an ultra-high purity, and then mixing the solution with the pigment dispersion to obtain an aqueous phase;
mixing and agitating the organic phase and the aqueous phase to obtain a homogenized solution;
agitating and heating the homogenized solution;
adding a polymerization initiator to the homogenized solution to be reacted; and
cooling the reaction solution to room temperature.
2. The method of preparing a latex of claim 1 , wherein a dispersing agent is an anionic surfactant selected from the group consisting of a carboxylate, an ester sulfate and a sulfonate; or a non-ionic surfactant selected from the group consisting of a polyoxyethylene alkylether, a polyoxyethylene alkylphenylether, a polyoxyethylene fatty acid ester, a sorbitan fatty acid ester, a polyoxysorbitan fatty acid ester, a polyoxyethylene alkylamine and an oxyethyleneoxypropylene block copolymer.
3. The method of preparing a latex of claim 1 , wherein the pigment dispersion is prepared by agitating at a speed of 2,000 to 10,000 rpm for 1 to 5 hours.
4. The method of preparing a latex of claim 1 , wherein the basic monomer mixture is a mixture of an aromatic-based vinyl monomer selected from the group consisting of a styrene, an o-methyl styrene, an m-methyl styrene, a p-methyl styrene, a p-methoxy styrene, a p-phenyl styrene, a p-chloro styrene, a p-ethyl styrene, a p-n-butyl styrene, a p-tert-butyl styrene, a p-n-hexyl styrene, a p-n-octyl styrene, a p-n-nonyl styrene, a p-n-decyl styrene, a p-n-dodecyl styrene, a 2,4-dimethyl styrene, a 3,4-dichloro styrene and their derivatives; a (meth)acrylic acid ester-based monomer selected from the group consisting of an acrylic acid methyl, an acrylic acid ethyl, an acrylic acid butyl, an acrylic acid-2-ethyl hexyl, an acrylic acid cyclohexyl, an acrylic acid phenyl, a methacrylic acid methyl, a methacrylic acid ethyl, a methacrylic acid butyl, a methacrylic acid hexyl, a methacrylic acid-2-ethyl hexyl, β-hydroxy acrylic acid ethyl, γ-amino acrylic acid propyl, a methacrylic acid stearyl, a methacrylic acid dimethyl amino ethyl, a methacrylic acid diethyl amino ethyl and their derivatives; a vinyl ester-based monomer selected from the group consisting of an acetic acid vinyl, a propionic acid vinyl, a benzoic acid vinyl and their derivatives; a vinyl ether-based monomer selected from the group consisting of a vinyl methyl ether, a vinyl ethyl ether, a vinyl isobutyl ether, a vinyl phenyl ether and their derivatives; a monoolefine-based monomer selected from the group consisting of an ethylene, a propylene, an isobutylene, a 1-butene, a 1-pentene, a 4-methyl-1-pentene and their derivatives; a diolefine-based monomer selected from the group consisting of a butadiene, an isoprene, a chloroprene and their derivatives; and a halogenated olefine-based monomer selected from the group consisting of a vinyl chloride, a vinylidene chloride, a vinyl fluoride and their derivatives.
5. The method of preparing a latex of claim 1 , wherein the crystalline monomer has 18 to 32 carbon atoms, and a melting point of 30° C. to 70° C.
6. The method of preparing a latex of claim 1 , wherein the crystalline monomer forms a crystalline polymer by copolymerization with the basic monomer, and the amount of the crystalline polymer in the latex is 1 to 50 parts by weight based on 100 parts by weight of the latex.
7. The method of preparing a latex of claim 1 , wherein the basic monomer forms a polymer material having a glass transition temperature of 40° C. to 100° C. by polymerization, and the crystalline monomer forms a crystalline polymer material having a melting point of 30° C. to 80° C. by copolymerization with the basic monomer.
8. The method of preparing a latex of claim 1 , wherein the dispersing agent is a non-ionic surfactant selected from the group consisting of a polyoxyethylene alkyl ether, a polyoxyethylene alkyl phenyl ether, a polyoxyethylene fatty acid ester, a sorbitan fatty acid ester, a polyoxy sorbitan fatty acid ester, a polyoxyethylene alkyl amine and an oxyethyleneoxypropylene block copolymer.
9. The method of preparing a latex of claim 1 , wherein the homogenization is carried out at an agitation speed of 1,000 to 7,000 rpm for 1 to 60 min.
10. The method of preparing a latex of claim 1 , wherein the agitation speed is 100 to 800 rpm, and the heating temperature is 50° C. to 80° C.
11. The method of preparing a latex of claim 1 , wherein the polymerization initiator is a water-soluble polymerization initiator selected from the group consisting of a persulfate, an azo based compound and a peroxide compound.
12. The method of preparing a latex of claim 1 , wherein the polymerization initiator is used in 1 to 5 parts by weight based on 100 parts by weight of the homogenized solution.
13. The method of preparing a latex of claim 1 , wherein a reaction time is 5 to 24 hours.
14. The method of of preparing a latex of claim 1 , wherein the pigment is a cyan pigment.
15. The method of of preparing a latex of claim 3 , wherein the organic phase comprises an octadecyl acrylate as a crystalline monomer and a basic monomer mixture comprising a styrene, a butyl acrylate and an acrylic acid in a mixed weight ratio of 7:2:1 to 7.5:1:0.5.
16. The method of of preparing a latex of claim 15 , wherein the aqueous phase comprises the pigment dispersion, an anionic surfactant, and a non-ionic surfactant in water having an ultra-high purity.
17. The method of of preparing a latex of claim 16 , wherein the aqueous phase and the organic phase are homogenized at approximately 7,000 rpm for approximately 30 min to form a homogenized solution, and the homogenized solution is poured into a reaction bath, and heated to a temperature of 75° C. while agitating at 100 rpm.
18. The method of preparing a latex of claim 17 , wherein, when the temperature within the reaction bath reaches 75° C., potassium persulfate is added as a polymerization initiator, and an inside of the reactor is purged with nitrogen gas, a polymerization reaction is carried out for approximately 24 hours, and after completion of the polymerization reaction, the reaction solution is cooled to room temperature.