Moisture curable sealer and adhesive composition
A low cost moisture curable sealer and adhesive composition containing a polymer having reactive silyl groups and a bituminous material and having many advantages over conventional moisture cure sealer compositions, including greater elastomeric properties, improved flexibility and pliability, lower durometer, faster and deeper cure, low temperature cure. The composition is also free of carcinogens such as coal tar, toxic isocyanates, and volatile solvents.
1. A moisture curable composition, comprising:
a polymer having reactive silyl groups; and an asphalt material, wherein the polymer having reactive silyl groups is a polyester having silyl groups, a polyether having reactive silyl groups, or a polyurethane having reactive silyl groups.
2. A moisture curable adhesive composition, comprising:
a polyurethane having reactive silyl groups; and an asphalt material.
3. A moisture curable composition, comprising:
a polymer having reactive silyl groups; and
an asphalt material, wherein the polymer having reactive silyl groups is an α, ω-telechelic silyl-terminated polymer.
4. The moisture curable composition of claim 3 , wherein the polymer having reactive silyl groups is a polyacrylate having reactive silyl groups or a polyether having reactive silyl groups.
5. A moisture curable composition, comprising:
a polymer having reactive silyl groups; and
an asphalt material, wherein the polymer having reactive silyl groups is a silyl-terminated oxyalkylene polymer.
6. A moisture curable composition, comprising;
a polymer having reactive silyl groups;
an asphalt material; and
a compatibilizing plasticizer in an amount effective to wet and help disperse the asphalt material in the polymer having reactive silyl groups.
7. The moisture curable composition of claim 6 , wherein the compatibilizing plasticizer is an ester of a polyol with a fatty acid, the condensation product of a polycarboxylic acid and an alkanol, or a polyester polyol having repeating units derived from acrylic or methacrylic acid and a polyol.
8. The moisture curable composition of claim 1 , further comprising a catalyst for promoting fast reaction among the reactive silyl groups of the polymer having reactive silyl groups.
9. The moisture curable composition of claim 1 , wherein the asphalt material is present in an amount of from about 20 to about 175 parts by weight per 100 parts by weight of the polymer having reactive silyl groups.
10. The moisture curable composition of claim 1 , wherein the asphalt material is present in an amount of from about 75 to about 150 parts by weight per 100 parts by weight of the polymer having reactive silyl groups.
11. The moisture curable composition of claim 1 , wherein the composition is substantially free of volatile organic compounds.
12. The moisture curable composition of claim 1 , wherein the composition is substantially free of isocyanate groups.
13. A moisture curable composition consisting essentially of:
a polymer selected from the group consisting of polyesters having reactive silyl groups, polyethers having reactive silyl groups, and polyurethanes having reactive silyl groups;
an asphalt material;
a compatibilizer in an amount effective to wet and help disperse the asphalt material in the polymer having reactive silyl groups;
optionally, a catalyst for promoting fast reaction among the reactive silyl groups of the polymer having reactive silyl groups; and
optionally, one or more additives selected from the group consisting of dehydrating agents, tactifiers, physical property modifiers, storage stability improving agents, antioxidants, adhesion promoters, ultraviolet light absorbers, metal deactivators, antiozonants, light stabilizers, amine type radial chain inhibitors, phosphorous-containing peroxide decomposers, lubricants, pigments, foaming agents, flame retardants and antistatic agents.
14. The moisture curable composition of claim 13 , wherein the polymer having reactive silyl groups is an α, ω-telechelic silyl-terminated polymer.
15. The moisture curable composition of claim 13 , wherein the compatibilizer is an ester of a polyol with a fatty acid, the condensation product of a polycarboxylic acid and an alkanol, or a polyester polyol having repeating units derived from acrylic or methacrylic acid and a polyol.
16. The moisture curable composition of claim 13 , wherein the asphalt material is present in an amount of from about 20 to about 175 parts by weight per 100 parts by weight of the polymer having reactive silyl groups.
17. The moisture curable composition of claim 13 , wherein the asphalt material is present in an amount of from about 75 to about 150 parts by weight per 100 parts by weight of the polymer having reactive silyl groups.
18. The moisture curable composition of claim 13 , wherein the composition is substantially free of volatile organic compounds.
19. The moisture curable composition of claim 13 , wherein the composition is substantially free of isocyanate groups.
20. The moisture curable composition of claim 1 , which has been applied to a substrate and cured to form a film having a water permeability rating less than 0.1.
21. The moisture curable composition of claim 1 , that is free of volatile organic compounds.
22. A composite waterproofing system comprising:
a moisture curable composition of claim 1 disposed between or on at least one side of one or more sheets of reinforcement scrim.
23. A roof membrane system comprising:
at least two plies of a polymer modified bitumen membrane adhered to each other and to a roof structure by a moisture curable composition of claim 1 .
24. A roofing system comprising:
a plurality of asphalt impregnated fiberglass felt layers adhered to each other and to a roof structure by a moisture curable composition of claim 1 .
25. A highway, parking structure or airport runway, comprising:
a plurality of concrete slabs arranged proximately to each other and defining at least one gap between the slabs, and a moisture curable composition of claim 1 deposited in the gap to form a horizontal joint seal.
26. A solvent-free, moisture curable composition for waterproofing automotive body components or for automotive underbody coating, comprising:
“a polymer selected from the group consisting of polyesters having reactive silyl groups, polyethers having reactive silyl groups and polyurethanes having reactive silyl groups; and
an asphalt material”.
27. A roofing system comprising:
a fleece- or felt-backed polymer membrane adhered to a roof structure by a moisture curable composition of claim 1 .
28. A concrete structure comprising:
a plurality of concrete slabs; and
a moisture curable composition of claim 1 coated onto surfaces of the concrete slabs and/or deposited in gaps defined between adjacent slabs of the structure.
29. The moisture curable composition of claim 1 , wherein the reactive silyl group is represented by the formula: —[Si(R 2 ) 2−a (X) a O] p —Si(R 3 ) 3−b (X) b wherein R 2 and R 3 are the same or different and each represents an alkyl group containing 1 to 20 carbon atoms, an aryl groups containing 6 to 20 carbon atoms, an aralkyl group containing 7 to 20 carbon atoms or a triorganosiloxy group of the formula (R 4 ) 3 SiO—, wherein R 4 independently represents a hydrocarbon group containing 1 to 20 carbon atoms, and, when two or more R 2 and/or R 3 groups are present, they may be the same or different; X represents a hydrolyzable group or a hydroxyl group and, when two or more X groups are present, they may be the same or different; a represents an integer of 0 to 2; b represents an integer of 0 to 3; and p represents an integer of 0 to 19 and, when p 2 or more, the —[Si(R 2 ) 2−a (X) a O]groups may be the same or different, with the proviso that the reactive silyl group includes at least one hydrolyzable group or hydroxyl group represented by X.