Bond coat for corrosion resistant EBC for silicon-containing substrate and processes for preparing same
An article comprising a silicon-containing substrate, a silicide-containing bond coat layer overlying the substrate, and an environmental barrier coating (EBC) overlying the bond coat layer, wherein the EBC comprises a corrosion resistant outer layer comprising a corrosion resistant metal silicate. A process is also provided for forming the corrosion resistant outer layer over the silicide-containing bond coat layer.
1. An article comprising:
a silicon-containing substrate;
a silicide-containing bond coat layer overlying the substrate, wherein the bond coat layer comprises a metal silicide selected from the group consisting of a silicide of chromium, tantalum, titanium, tungsten, zirconium, hafnium, a rare earth, and a compatible combination thereof;
an optional silica scale layer overlaying the bond coat layer; and
an environmental barrier coating overlying the bond coat layer, wherein the environmental barrier coating comprises a reaction-generated corrosion resistant metal silicate layer wherein the metal silicate is at least one member of the group consisting of a yttrium silicate, a scandium silicate, a zirconium silicate, a hafnium silicate, a rare earth silicate, and combinations thereof, and wherein a silicon source for the reaction-generated metal silicate includes the silica scale layer, if present, or the silicide-containing bond coat layer in the absence of the silica scale layer.
2. The article of claim 1 wherein the bond coat layer is adjacent to the substrate and has a thickness of from about 0.5 to about 10 mils.
3. The article of claim 2 wherein the bond coat layer has a thickness of from about 1 to about 6 mils.
4. The article of claim 1 wherein the corrosion resistant outer layer has a thickness of up to about 30 mils.
5. The article of claim 4 wherein the corrosion resistant outer layer has a thickness of from about 2 to about 10 mils.
6. The article of claim 4 wherein the corrosion resistant outer layer has a thickness of up to about 5 mils.
7. The article of claim 6 wherein the corrosion resistant outer layer has a thickness of from about 1 to about 2.5 mils.
8. The article of claim 1 which is in the form of a turbine component.
9. The article of claim 8 which is a turbine blade.
10. The article of claim 1 wherein the substrate comprises a silicon-containing ceramic material, a silicon metal alloy, or a combination thereof.
11. The article of claim 10 wherein the substrate comprises a continuous matrix of a silicon-containing material reinforced with fibers.
12. The article of claim 11 wherein the substrate comprises a silicon carbide coated silicon carbide fiber-reinforced silicon carbide particles and a silicon matrix, a carbon fiber-reinforced silicon carbide matrix, or a silicon carbide fiber-reinforced silicon nitride matrix.
13. The article of claim 10 wherein the substrate comprises a silicon-containing ceramic material.
14. The article of claim 13 wherein the silicon-containing ceramic material comprises silicon carbide, silicon nitride, silicon carbide nitride, silicon oxynitride, silicon aluminum oxynitride, or a combination thereof.
15. The article of claim 1 wherein the corrosion resistant outer layer comprises at least about 90% by weight corrosion resistant metal silicate.
16. The article of claim 15 wherein the corrosion resistant outer layer comprises at least about 95% by weight corrosion resistant metal silicate.
17. The article of claim 1 wherein the corrosion resistant metal silicate comprises yttrium silicate, ytterbium silicate, or lutetium silicate.
18. The article of claim 1 which further comprises a thermal barrier coating overlaying the corrosion resistant outer layer.
19. The article according to claim 1 wherein the metal silicide is selected from the group consisting of titanium trisilicide, chromium trisilicide, hafnium disilicide, tantalum trisilicide, tantalum disilicide, tungsten disilicide, zirconium disilicide, gadolinium disilicide, lanthanum disilicide, neodymium silicide, ytterbium trisilicide, and a compatible combination thereof.
20. An article comprising:
a silicon-containing substrate;
a silicide-containing bond coat layer overlying the substrate;
a silica scale layer adjacent to and overlaying the bond coat layer, wherein the silica scale layer is formed by preoxidizing a portion of the bond coat layer and has a thickness of from about 0.5 to about 50 microns; and
an environmental barrier coating overlying the bond coat layer, wherein the environmental barrier coating comprises a corrosion resistant outer layer adjacent to and overlaying the silica scale layer and comprising a corrosion resistant metal silicate, wherein the corrosion resistant metal silicate is formed by reaction of a metal source with the silica scale layer.