Functional coatings for the reduction of oxygen permeation and stress and method of forming the same
View Patent ↗The oxidation behavior of the bond coat is improved using a HVOF nanostructured NiCrAlY coating. NiCrAlY powder is mechanically cryomilled and HVOF sprayed onto Ni-based alloy to form a nanocrystalline bond coat. Oxidation is performed on the coating to form the thermally grown oxide layer (thermally grown oxide). After heat treatment at 1000° C. for 24 and 95 hour, a homogeneous α-Al 2 O 3 layer is formed on top of the bond coat. The nanostructured characteristic of the coating and the presence of Al 2 O 3 within the cryomilled powders (oxidation occurred during cryomilling process) affects the nucleation of the alumina layer on the top of the coating. The formation of a continuous thermally grown oxide layer protects the coating from further oxidation and avoids the formation of mixed oxide protrusions, such as those presented in the coating sprayed using the as-received powder.
1. A method for improving a MCrAlY thermal barrier coating made from MCrAlY powder, where M is a metal or metal alloy, comprising:
providing a MCrAlY bond coat on a substrate; and
providing a nanocrystalline nano-composite metallic powder coating on the MCrAlY bond coat where the nanostructured nano-composite-coating is prepared by refining the microstructure of a metallic alloy system consisting of MCrAlY powder used to make the nanostructure nano-composite coating to nanocrystalline grain size.
2. The method of claim 1 where refining the microstructure of the MCrAlY powder to nanocrystalline grain size comprises cryomilling the MCrAlY powder to nanocrystalline grain size including in-situ formation of oxides, nitrides and/or oxynitrides.
3. A method for improving a MCrAlY thermal barrier coating made from MCrAlY powder, where M is a metal or metal alloy, comprising:
providing a MCrAlY bond coat on a substrate; and
providing a nanocrystalline nano-composite coating on the MCrAlY bond coat where the nanostructured nano-composite-coating is prepared by refining the microstructure of a MCrAlY powder and alumina used to make the nanostructure nanocomposite coating to nanocrystalline grain size, where refining the microstructure of the MCrAlY powder to nanocrystalline grain size comprises cryomilling the MCrAlY powder and refining the microstructure of the MCrAlY powder to nanocrystalline grain size during cryomilling through the introduction of Al 2 O 3 particles added during cryomilling.
4. The method of claim 3 where refining the microstructure of the MCrAlY powder to nanocrystalline grain size achieved after cryomilling comprises introducing nano alumina whiskers during cryomilling.