Al-Mg-Si alloy sheet excellent in surface properties, manufacturing method thereof, and intermediate material in the manufacturing thereof
The present invention provides an Al—Mg—Si alloy sheet in which the production of ridging marks during press forming is noticeably inhibited, and in addition, provides a manufacturing method capable of providing such an aluminum alloy sheet, and an intermediate material in the manufacture thereof. The Al—Mg—Si alloy sheet in accordance with the present invention is characterized by having a prescribed composition, and characterized in that respective textures are present therein with a good balance. Further, in accordance with the manufacturing method, and the intermediate material in the manufacture thereof of the present invention, it is possible to manufacture the alloy with high efficiency.
1. An Al—Mg—Si alloy sheet, comprising Mg in an amount of 0.4 to 1.9 mass % and Si in an amount of 0.2 to 1.9 mass %,
wherein respective textures of Cube orientation, CR orientation, RW orientation, Goss orientation, Brass orientation, S orientation, Cu orientation, and PP orientation satisfy the conditions of the following expression (1):
([Cube]+[CR]+[RW]+[Goss]+[Brass]+[S]+[Cu]+[PP])/8≦1.0 (%) (1)
(where [x] denotes the standard deviation (%) of the area ratio of an orientation x in a sheet cross section every 500 μm along the sheet width direction); and
wherein the Al—Mg—Si alloy sheet is produced by a process comprising cold rolling an intermediate material, which comprises Mg in an amount of 0.4 to 1.9 mass % and Si in an amount of 0.2 to 1.9 mass %, which is in shape of a sheet, and in which the average value of the crystal sizes along the sheet thickness direction of textures of respective orientations is 50 μm or less.
2. The Al—Mg—Si alloy sheet according to claim 1 , further comprising at least one selected from the group consisting of 1.0 mass % or less of Fe, 0.3 mass % or less of Mn, 0.3 mass % or less of Cr, 0.3 mass % or less of Zr, 0.3 mass % or less of V, and 0.1 mass % or less of Ti.
3. The Al—Mg—Si alloy sheet according to claim 1 , further comprising at least one of 1.0 mass % or less of Cu and 1.0 mass % or less of Zn.
4. A method for manufacturing the Al—Mg—Si alloy sheet according to claim 1 , comprising: subjecting an aluminum alloy containing Mg in an amount of 0.4 to 1.9 mass % and Si in an amount of 0.2 to 1.9 mass % to hot rolling and cold rolling; and subjecting the aluminum alloy to intermediate annealing immediately before the cold rolling or during the cold rolling, wherein the intermediate annealing conditions are set such that the annealing temperature is 150 to 320° C. and the annealing time is 20 hours or more.
5. The method according to claim 4 , wherein the starting temperature of the hot rolling is set at 500° C. or less, and the finishing temperature of the hot rolling is set at 250° C. or less.
6. The method according to claim 4 , wherein the cold rolling reduction in the cold rolling is set at 70% or more.