Method of producing a hollow glass cylinder with suspension during sintering
The invention relates to a method for producing a silica glass tube which is characterized by depositing SiO 2 particles on an elongate support that rotates about its longitudinal axis, thereby producing a porous with a cylindrical inner bore. Said blank is vertically aligned, suspended in a furnace using a suspension that engages with a constriction in the upper zone of the inner bore of the blank, and vitrified. The aim of the invention is to provided a method with which also heavy blanks can be secured safely and substantially without any danger of contaminations of the inner bore without using complicated securing devices. To this end, the constriction ( 6 b ) is generated by shaping the inner bore ( 7 ) when the SiO 2 particles are deposited. For vitrification a suspension ( 8; 9; 10 ) is used that supports itself on the constriction ( 6 b ) and that otherwise projects into the cylindrical inner bore ( 7 ) without having any contact therewith.
1. A method for producing a hollow cylinder from silica glass, said method comprising:
depositing SiO 2 particles onto an elongate support that rotates about a longitudinal axis thereof, said support having a first longitudinal section with a first outer diameter and a second longitudinal section with a second outer diameter, the first outer diameter being larger than the second outer diameter, so as to produce a porous blank with an inner bore defined by a first cylindrical surface extending over a first length of the blank and having a first inner diameter, and by a second cylindrical surface extending over a second length of the blank and having a second inner diameter, and an area therebetween, the first inner diameter being larger than the second inner diameter so that said area between the first longitudinal section and the second longitudinal section has a constriction in said inner bore of said blank, said constriction being formed by said support by shaping the inner bore during said SiO 2 deposition, and
vitrifying the blank suspended in vertical orientation in a furnace using a suspension that engages with said constriction,
said constriction being in an upper region of the blank;
said suspension having an upper portion and a lower portion, said upper portion being smaller than the second inner diameter, and said lower portion having a size between the first inner diameter and the second inner diameter, and
wherein during said vitrification said suspension extends into the inner bore and supports the blank by engagement with said blank in said area of said constriction, said suspension having no contact with said first cylindrical surface of the inner bore of the blank during said vitrification.
2. The method according to claim 1 , wherein the support has a reduction in diameter between the first and second longitudinal sections that is rotationally symmetrical relative to a longitudinal axis of said support.
3. The method according to claim 2 , wherein the reduction in diameter of the support comprises a surrounding shoulder.
4. The method according to claim 3 , wherein said suspension projects from above into the inner bore, so that said suspension is secured behind said constriction.
5. The method according to claim 2 , wherein said suspension projects from above into the inner bore, so that said suspension is secured behind said constriction.
6. The method according to claim 1 , wherein said suspension projects from above into the inner bore, so that said suspension is secured behind said constriction.
7. The method according to claim 1 , wherein at least part of said suspension is formed of silica glass.
8. The method according to claim 7 , wherein said suspension is fused with said blank during vitrification.
9. The method according to claim 1 , wherein said suspension is fused with said blank during vitrification.
10. A method for producing a hollow cylinder from silica glass, said method comprising:
depositing SiO 2 particles onto an elongate support that rotates about a longitudinal axis thereof, said support having a first longitudinal section with a first outer diameter and a second longitudinal section, the first outer diameter being larger than a largest radial dimension of the second longitudinal section so that said depositing step produces a porous blank with a wall defining an inner bore extending through said porous blank,
the wall including a cylindrical surface that has an inner diameter extending over a partial length of the blank up to an upper region of the porous blank
the wall also including an area wherein there is a constriction in the inner bore in said upper region, and
suspending the blank in a vertical orientation on a suspension structure,
said suspension structure extending downwardly through the inner bore in an upper end of the blank, and having a thickened portion, said thickened portion being sized so as to pass through said partial length of the blank and the cylindrical surface, and being so large that said thickened portion cannot pass through the inner bore at the constriction, and engages the wall and supports the porous blank in said upper region of the blank, and
vitrifying the blank suspended in said vertical orientation in a furnace,
during said vitrifieation said suspension structure having no contact with the cylindrical surface.
11. The method according to claim 10 , wherein the support has a reduction in diameter between the first and second longitudinal sections that is rotationally symmetrical relative to a longitudinal axis of said support.
12. The method according to claim 11 , wherein the reduction in diameter of the support comprises a surrounding shoulder.
13. The method according to claim 12 , wherein at least part of said suspension structure is formed of silica glass.
14. The method according to claim 13 , wherein said suspension structure is fused with said blank during the vitrification.
15. The method according to claim 11 , wherein at least part of said suspension structure is formed of silica glass.
16. The method according to claim 15 , wherein said suspension structure is fused with said blank during the vitrification.
17. The method according to claim 10 , wherein at least part of said suspension structure is formed of silica glass.
18. The method according to claim 17 , wherein said suspension structure is fused with said blank during the vitrification.
19. The method according to claim 10 wherein said suspension structure is fused with said blank during vitrification.