Copper polishing cleaning solution
View Patent ↗A cleaning solution for removing copper complex residues from the surface of polishing pads and wafer substrates includes an amine pH-adjusting agent, which can be a unidentate or bidentate amine compound or a quartnary ammonium hydroxide compound or an amine including an alcohol group. The cleaning solution also includes an amino acid complexing agent and an inhibitor. In a preferred embodiment, the cleaning solution has a basic pH.
1. A method useful for removing copper(I)-BTA complex precipitate from substrates and polishing pads comprising the steps of:
polishing a microelectronic substrate in a manner wherein the concentration of copper ions exceeds the solubility constant (K sp ) and copper ions react with BTA to form the copper(I)-BTA complex precipitate on the microelectronic substrate;
introducing a copper polishing cleaning solution to dissolve the copper(I)-BTA complex precipitate and form copper(I) ions in the cleaning solution, the copper polishing cleaning solution having an amino acid complexing agent, the complexing agent having a dipole ion structure;
forming a complex between the copper ions and the complexing agent; and
maintaining the copper ions in solution with the complexing agent to prevent the copper ions from redepositing on the microelectronic substrate.
2. The method of claim 1 wherein the complexing agent is selected from glycine, lysine, valine or alanine to maintain the copper ions in solution.
3. The method of claim 1 wherein the cleaning solution has a pH of at least 10.
4. The method of claim 1 wherein the complexing agent is glycine to maintain the copper ions in solution.
5. The method of claim 1 wherein the cleaning solution comprises a quartnary ammonium hydroxide compound for adjusting the pH of the cleaning solution.
6. A method useful for removing copper(I)-BTA complex precipitate from substrates and polishing pads comprising the steps of:
polishing a microelectronic substrate in a manner wherein the concentration of copper ions exceeds the solubility constant (K sp ) and copper ions react with BTA to form the copper(I)-BTA complex precipitate on the microelectronic substrate;
introducing a copper polishing cleaning solution to dissolve the copper(I)-BTA complex precipitate and form copper (I) ions in the cleaning solution, the copper polishing cleaning solution having an amino acid complexing agent, a basic pH and an azole inhibitor, the complexing agent having a dipole structure;
forming a complex between the copper ions and the complexing agent; and
maintaining the copper ions in solution with the complexing agent to prevent the copper ions from redepositing on the microelectronic substrate.
7. The method of claim 6 wherein the complexing agent is selected from glycine, lysine, valine or alanine to maintain the copper ions in solution.
8. The method of claim 6 wherein the cleaning solution has a pH of 10.5 to 11.9.
9. The method of claim 6 wherein the complexing agent is glycine to maintain the copper ions in solution.
10. The method of claim 6 wherein the cleaning solution comprises a quartnary ammonium hydroxide compound for adjusting the pH of the cleaning solution.