Formulation for the manufacture of carbon-carbon composite materials
Method for manufacturing a carbonized carbon-carbon composite preform, by: mixing (a) chopped carbon fiber, chopped stabilized pitch fiber, or chopped oxidized polyacrylonitrile (PAN) fiber, (b) thermoplastic pitch binder powder, and (c) activated carbon powder to form a mixture of 15-60 parts by weight of chopped carbon fiber or chopped stabilized pitch fiber or chopped oxidized PAN, 28-83 parts by weight of thermoplastic pitch binder powder, and 1-12 parts by weight of activated carbon powder; depositing this mixture into a mold; pressing/heating the materials in the mold to form a preform by compaction; removing the compacted preform from the mold; and carbonizing the compacted preform. The preform is preferably configured in the form of an aircraft landing system brake disc.
1. A method for manufacturing a carbonized carbon-carbon composite preform, comprising the steps of:
(i) mixing (a) chopped carbon fiber, chopped stabilized pitch fiber, or chopped oxidized polyacrylonitrile (PAN) fiber, (b) thermoplastic pitch binder powder, and (c) activated carbon powder to form a mixture of 15-60 parts by weight of chopped carbon fiber or chopped stabilized pitch fiber or chopped oxidized PAN, 28-83 parts by weight of thermoplastic pitch binder powder, and 1-12 parts by weight of activated carbon powder;
(ii) depositing said mixture into a mold;
(iii) compression molding the materials in the mold at a temperature of from 180 to 300° C. and at a pressure of from 1600 to 2400 psi to form a preform by compaction;
(iv) removing the compacted preform from the mold; and
(v) carbonizing the compacted preform.
2. The method of claim 1 , wherein the carbonized preform weighs at least 3% more than does a carbonized preform made by an otherwise identical process in which said activated carbon powder is replaced by thermoplastic binder powder.
3. The method of claim 1 , wherein carbonization step (v) is conducted in an inert atmosphere at a temperature of from 750 to 1200° C. for from 1/2 to 2 hours.
4. The method of claim 1 , which comprises the further step (vi) of densifying the carbonized preform by CVI/CVD processing.
5. An aircraft landing system brake disc made by the method of claim 4 .
6. A composition suitable for manufacturing a carbon-carbon composite preform, said comprising a mixture of: (a) 15-60 parts by weight of chopped carbon fiber or carbon fiber precursor, (b) 28-83 parts by weight of thermoplastic pitch binder powder, and 1-12 parts by weight of (c) activated carbon powder.
7. The composition of claim 6 , comprising 50 weight-% chopped carbon fiber, 45 weight-% thermoplastic pitch binder powder, and 5 weight-% activated carbon powder.
8. A compacted carbon-carbon composite preform comprising a molded mixture of: (a) 15-60 weight-% chopped carbon fiber or chopped stabilized pitch fiber or chopped oxidized PAN fiber, (b) 28-83 weight-% thermoplastic pitch binder powder, and (c) 1-12 weight-% activated carbon powder, wherein at least 2 weight-% of said thermoplastic binder is adsorbed to said activated carbon.
9. A carbonized carbon-carbon composite preform comprising a compacted, molded mixture of: (a) 15-60 weight-% carbon fiber or carbonized stabilized pitch fiber or carbonized oxidized PAN fiber, (b) 28-83 weight-% carbonized pitch powder, and (c) 1-12 weight-% activated carbon.
10. The carbonized carbon-carbon composite preform of claim 9 , said preform being configured as a brake disc for an aircraft landing system.
11. The carbonized carbon-carbon composite preform of claim 9 , comprising 50 weight-% carbon fiber, 45 weight-% carbonized pitch, and 5 weight-% activated carbon.
12. The carbonized carbon-carbon composite preform of claim 11 , said preform being configured in the form of an annular ring having the shape of a brake disc for an aircraft landing system, said annular ring having an outside diameter of 20 inches, an inner diameter of 10 inches, and a thickness of 2.5 inches.