Radiation resistant single-mode optical fiber and method of manufacturing thereof
A radiation resistant single-mode optical fiber has a core and a cladding, each made of fluorine-doped silica glass, in which a chlorine concentration of the core is at least 0.01 ppm, a relative refractive index difference of the core based on the refractive index for silica is between −0.30% and −0.10%, a relative refractive index difference of the core based on the refractive index for the cladding is between 0.3% and 0.5%, a cutoff wavelength is 1.27 μm or below, and a bending loss at a wavelength of 1.3 μm and a bending diameter of 20 mm is 0.5 dB/m or less.
1. A radiation resistant single-mode optical fiber comprising a core and a cladding, wherein:
the core and the cladding comprise fluorine-doped silica glass,
a chlorine concentration of the core is between 0.01 ppm and 0.05 ppm,
a flourine concentration of the core between 0.8 wt % and 1.2 wt %,
a relative refractive index difference of the core based on a refractive index for the cladding is between 0.3% and 0.5%, a cutoff wavelength is not greater than 1.27 μm, and
a bending loss at a wavelength of 1.3 μm and a bending diameter of 20 mm is not greater than 0.5 dB/m.
2. The radiation resistant single-mode optical fiber according to claim 1 , wherein r 1 is a core radius and r 2 is a cladding radius, a cladding to core diameter ratio r 2 /r 1 is between 12 and 17, a transmission loss at a wavelength of 1.3 μm is not greater than 1.0 dB/km, and a mode field diameter (MFD) at a wavelength of 1.3 μm is not less than 8.0 μm.
3. The radiation resistant single-mode optical fiber according to claim 2 , wherein if the optical fiber is irradiated for 60 minutes at an exposure dose rate of 1.0×10 6 R/h, a transmission loss increase is not greater than 10.0 dB/km at a wavelength of 1.3 μm.
4. A method of manufacturing the radiation resistant single-mode optical fiber according to claim 2 , the method comprising drawing an optical fiber preform comprising a core and a cladding at a fiber drawing tension between 0.10 N and 0.40 N and a fiber drawing speed between 10 m/min and 100 m/min, wherein:
the core and the cladding of the optical fiber preform comprise fluorine-doped silica glass,
a chlorine concentration of the core of the optical fiber preform is between 0.01 ppm and 0.05 ppm,
a flourine concentration of core is between 0.8 wt % and 1.2 wt %, and
a relative refractive index difference of the core of the optical fiber preform based on a refractive index of the cladding of the optical fiber preform is between 0.3% and 0.5%.
5. The radiation resistant single-mode optical fiber according to claim 1 , wherein, if the optical fiber is irradiated for 60 minutes at an exposure dose rate of 1.0×10 6 R/h, a transmission loss increase is not greater than 10.0 dB/km at a wavelength of 1.3 μm.
6. A method of manufacturing the radiation resistant single-mode optical fiber according to claim 5 , the method comprising drawing an optical fiber preform comprising a core and a cladding at a fiber drawing tension between 0.10 N and 0.40 N and a fiber drawing speed between 10 m/min and 100 m/min, wherein:
the core and the cladding of the optical fiber preform comprise fluorine-doped silica glass,
a chlorine concentration of the core of the optical fiber preform is between 0.01 ppm and 0.05 ppm,
a flourine concentration of core is between 0.8 wt % and 1.2 wt %, and
a relative refractive index difference of the core of the optical fiber preform based on a refractive index of the cladding of the optical fiber preform is between 0.3% and 0.5%.
7. A method of manufacturing the radiation resistant single-mode optical fiber according to claim 1 , the method comprising drawing an optical fiber preform comprising a core and a cladding at a fiber drawing tension between 0.10 N and 0.40 N and a fiber drawing speed between 10 m/min and 100 m/min, wherein:
the core and the cladding of the optical fiber preform comprise fluorine-doped silica glass,
a chlorine concentration of the core of the optical fiber preform is between 0.01 ppm and 0.05 ppm,
a flourine concentration of core is between 0.8 wt % and 1.2 wt %, and
a relative refractive index difference of the core of the optical fiber preform based on a refractive index of the cladding of the optical fiber preform is between 0.3% and 0.5%.