Non-white construction surface
Provides a non-white construction surface comprising a substrate, a first reflective coating on at least a portion of an outer surface of the substrate, the coated substrate exhibiting a minimum direct solar reflectance value of at least about 25%, and a second reflective coating on at least a portion of the first reflective coating, wherein the combination of the first reflective coating and the second reflective coating provide the substrate with at least one of (i) a reflectivity of at least about 20% at substantially all points in the wavelength range between 770 and 2500 nm, and (ii) a summed reflectance value of at least 7000 as measured in the range between 770 and 2500 nm inclusive. Also provided are various substrates having the coatings described as well as methods of providing the described construction surfaces.
1. A non-white roofing shingle granule comprising:
a substrate comprising a granule;
a first white reflective coating on at least a portion of an outer surface of the substrate,
the coated substrate exhibiting a minimum direct solar reflectance value of at least about 25%,
the first white reflective coating comprising at least 50 vol % of an inorganic binder; and
a second reflective coating comprising a colored pigment having enhanced NIR reflectivity on at least a portion of the first white reflective coating, wherein the combination of the first white reflective coating and the second reflective coating provide the substrate with a reflectivity of at least about 20% at substantially all points in the wavelength range between 770 and 2500 nm;
wherein the second reflective coating has a non-metallic appearance.
2. The non-white roofing shingle granule of claim 1 wherein the second reflective coating has an inorganic binder.
3. A non-white roofing shingle granule comprising:
a substrate comprising a granule;
a first white reflective coating on at least a portion of an outer surface of the substrate, the coating substrate exhibiting a minimum direct solar reflectance value of at least about 25%, the first white reflective coating comprising at least 50 vol % of an inorganic binder; and
a second reflective coating comprising a colored pigment having enhanced NIR reflectivity on at least a portion of the first white reflective coating, wherein the combination of the first white reflective coating and the second reflective coating provide the substrate with a summed reflectance value of at least about 7,000 as measured in the range between 770 and 2500 nm inclusive;
wherein the second reflective coating has a non-metallic appearance.
4. The non-white roofing shingle granule of claim 3 wherein the second reflective coating comprises an inorganic binder.
5. A method of producing a non-white roofing shingle granule surface comprising:
applying a first coating solution to at least a portion of an outer surface of a substrate comprising a granule;
curing the first coating solution to form a first white reflective coating to form a coated substrate, the first white reflective coating exhibiting a minimum direct solar reflectance value of at least about 25, % and the first white reflective coating comprising at least 50 vol % of an inorganic binder;
applying a second coating solution comprising a colored pigment having enhanced NIR reflectivity over at least a portion of the coated substrate; and
curing the second coating solution to form second reflective coating wherein the combination of the first white reflective coating and the second reflective coating provide at least one of
(i) a reflectivity of at least about 20 % at substantially all points in the wavelength range between 770 and 2500 nm, and
(ii) a summed reflectance value of at least 7000 as measured in the range between 770 and 2500 nm inclusive;
wherein the second reflective coating has a non-metallic appearance.
6. A non-white roofing shingle granule comprising:
an inorganic, non-metallic substrate comprising a granule;
a first white reflective coating on at least a portion of an outer surface of the substrate, the coated substrate exhibiting a minimum direct solar reflectance value of at least about 25%, the first white reflective coating comprising at least 50 vol % of an inorganic binder; and
a second reflective coating comprising a colored pigment having enhanced NIR reflectivity on at least a portion of the first reflective coating, wherein the combination of the first white reflective coating and the second reflective coating provide the substrate with at least one of (i) a reflectivity of at least about 20 % at substantially all points in the wavelength range between 770 and 2500 nm, and (ii) a summed reflectance value of at least 7000 as measured in the range between 770 and 2500 nm inclusive;
wherein the second reflective coating has a non-metallic appearance.
7. The non-white roofing shingle granule of claim 6 wherein the second reflective coating has an inorganic binder.
8. The non-white roofing shingle granule of claim 1 wherein the colored pigment having enhanced NIR reflectivity is selected from the group consisting of a black colored pigment, a brown colored pigment, a green colored pigment, and combinations thereof.
9. The non-white roofing shingle granule of claim 1 wherein the colored pigment having enhanced NIR reflectivity is selected from the group consisting of a yellow colored pigment, a blue colored pigment, a red colored pigment, and combinations thereof.
10. The non-white roofing shingle granule of claim 3 wherein the colored pigment having enhanced NIR reflectivity is selected from the group consisting of a black colored pigment, a brown colored pigment, and combinations thereof.
11. The non-white roofing shingle granule of claim 3 wherein the colored pigment having enhanced NIR reflectivity is selected from the group consisting of a yellow colored pigment, a blue colored pigment, a red colored pigment, a green colored pigment, and combinations thereof.
12. The method of claim 5 , wherein the applying a second coating solution step comprises applying a second coating solution over at least a portion of the coated substrate, the second coating solution comprising a colored pigment having enhanced NIR reflectivity selected from the group consisting of a black colored pigment, a brown colored pigment, a red colored pigment, and combinations thereof.
13. The method of claim 5 , wherein the applying a second coating solution step comprises applying a second coating solution over at least a portion of the coated substrate, the second coating solution comprising a colored pigment having enhanced NIR reflectivity selected from the group consisting of a blue colored pigment, a yellow colored pigment, a green colored pigment, and combinations thereof.