Laminated polyester resin container and method of molding such a container
A multiplayer perform having at least a medium or intermediate gas barrier layer is prepared in advance by the injection molding of this perform in a predetermined shape that corresponds to the shape of a finished molded product. The body portion of this perform is heated to a blow moldable temperature. The heated perform is set in a primary blow mold ( 12 ), and is blow molded in the biaxial orientation to give a primary molded intermediate ( 5 ). The primary intermediate ( 5 ) is then heated to deform it forcibly by thermal shrinkage and thereby to give the secondary molded intermediate ( 6 ). The shrunken secondary intermediate ( 6 ) is set in a secondary blow mold ( 13 ), and is subjected to the secondary blow molding in the biaxial orientation to obtain a finished molded product, which is fixed thermally to give heat history to the PET resin. As a result, the PET resin layers are given a high degree of crystallization, which serves to complement the function of the gas barrier layer or layers in such a way that the container has high and effective gas barrier properties.
1. A method for molding a laminated polyester resin container, comprising:
(a) Preparing in advance a multilayer preform by injection-molding said preform in a predetermined shape that corresponds to the shape of a finished molded product, wherein the mouth/neck portion consists of a single layer of the polyester resin and wherein the body portion, including trunk and bottom but excluding said mouth/neck portion, comprises an outer and an inner layer of the polyester resin and at least a medium or intermediate layer of a gas barrier resin;
(b) heating the body portion of said preform to a blow moldable temperature within the range of 90° to 120° C.;
(c) setting said heated preform in a primary blow mold that has been heated to a temperature within the range of 70° to 180° C. and blow molding said preform in the biaxial orientation to form a primary molded intermediate;
(d) heating said primary intermediate to a temperature within the range of 130° to 200° C. to deform it forcibly by thermal shrinkage and thereby to form a secondary molded intermediate; and
(e) setting the shrunken secondary intermediate in a secondary blow mold that has been heated to a temperature within the range of 80° to 150° C., and subjecting said secondary intermediate to secondary blow molding with biaxial orientation to obtain a finished molded product.
2. The method of claim 1 , wherein the mouth/neck portion has been treated for whitening.
3. The method of claim 1 , wherein said multilayer preform is obtained by extrusion molding of resins into the multilayer structure of 3 layers of more, including inner and outer layers of polyethylene terephthalate and a middle gas barrier layer of a polyamide resin containing meta-xylyl radicals or an ethylene vinyl alcohol copolymer resin.
4. The method of claim 1 , wherein the multilayer preform is obtained by extrusion molding of resins into a 5-layer structure, including inner and outer layers of polyethylene terephthalate as well as a PET center core, plus two intermediate layers of a polyamide resin containing meta-xylyl radicals or the ethylene vinyl alcohol copolymer resin.
5. The method of claim 1 for molding a laminated polyester resin container, wherein the secondary molded intermediate is subjected to the secondary blow molding at a blow ratio smaller than used in the primary blow molding.
6. A method for molding a laminated polyester resin container, comprising:
(a) preparing in advance a multilayer preform by injection-molding said preform in a predetermined shape that corresponds to the shape of a finished molded product, wherein the body portion, including the mouth/neck portion and the trunk and bottom portions, comprises an outer and an inner layer of the polyester resin and at least a medium or intermediate layer of a gas barrier resin;
(b) heating the body portion of said preform to a blow moldable temperature within the range of 90° to 120° C.;
(c) setting said heated preform in a primary blow mold that has been heated to a temperature within the range of 70° to 180° C. and blow molding said preform in the biaxial orientation to form a primary molded intermediate;
(d) heating said primary intermediate to a temperature within the range of 130° to 200° C. to deform it forcibly by thermal shrinkage and thereby to form a secondary molded intermediate; and
(e) setting the shrunken secondary intermediate in a secondary blow mold that has been heated to a temperature within the range of 80° to 150° C., and subjecting said secondary intermediate to secondary blow molding with biaxial orientation to obtain a finished molded product.