Waterborne composition for forming protective coatings
A waterborne composition for forming protective coatings to provide, by a simple method comprising coating and drying onto a metal surface, a coating that is uniform with little unevenness and that has an excellent galling resistance and workability that are at least as good as the corresponding properties afforded by conversion treatment methodologies, contains water-soluble inorganic salt and smectite-type clay mineral. The lubrication performance of the coating can also be improved when said composition additionally contains a lubricating component.
1. A waterborne composition comprising;
a.) water;
b.) a water-soluble inorganic salt selected from sulfates, borates, silicates, molybdates, vanadates, and tungstates; and
c.) a smectite-type clay mineral being at least one selection from the group consisting of sauconite, beidellite, hectorite, nontronite, saponite, iron saponite, and stevensite, said clay minerals having a mean particle size of 20 to 500 nm;
wherein the mass ratio of water-soluble inorganic salt to smectite-type clay mineral is 1:1 to 1:0.01.
2. The waterborne composition of claim 1 , further comprising a lubricating component comprising at least one selection from the group consisting of oils, soaps, metal soaps, waxes, and polytetrafluoroethylene, in an amount comprising 1-70 mass % of the sum of the water-soluble inorganic salt, smectite-type clay mineral, and lubricating component.
3. The waterborne composition of claim 1 , wherein the water-soluble inorganic salt is at least one selection from the group consisting of sodium sulfate, potassium sulfate, sodium borate, potassium borate, ammonium borate, sodium silicate, potassium silicate, lithium silicate, ammonium molybdate, sodium molybdate, sodium tungstate, and sodium vanadate.
4. The waterborne composition of claim 1 , wherein the smectite-type clay mineral is at least one selection from the group consisting of beidellite, hectorite, nontronite, saponite, iron saponite, and stevensite.
5. The waterborne composition of claim 1 , wherein the smectite-type clay mineral is synthetic hectorite clay.
6. The waterborne composition of claim 1 , further comprising a lubricating component comprising at least one selection from the group consisting of oils, soaps, metal soaps, waxes, and polytetrafluoroethylene, in an amount comprising 5-45 mass % of the sum of the water-soluble inorganic salt, smectite-type clay mineral, and lubricating component.
7. A waterborne composition for forming protective coatings comprising:
a.) water;
b.) at least one water-soluble inorganic salt selected from the group consisting of sulfates, molybdates, vanadates, and tungstates;
c.) a smectite-type clay mineral; and
d.) a lubricating component comprising at least one selection from the group consisting of oils, soaps, metal soaps, waxes, and polytetrafluoroethylene, in an amount comprising 1-45 mass % of the sum of the water-soluble inorganic salt, smectite-type clay mineral, and lubricating component;
wherein the mass ratio of water-soluble inorganic salt to smectite-type clay mineral is 1:1 to 1:0.01.
8. The waterborne composition of claim 7 , wherein the lubricating component comprises at least one selection from the group consisting of oils, soaps, metal soaps, and waxes in an amount comprising 5-45 mass % of the sum of the water-soluble inorganic salt, smectite-type clay mineral, and lubricating component.
9. A metal workpiece to be formed with a tool, the workpiece comprising a protective coating produced by applying and drying a composition according to claim 1 on the metal workpiece.
10. The metal workpiece according to claim 9 , wherein the metal is iron, steel, copper, copper alloy, aluminum, aluminum alloy, titanium, titanium alloy, magnesium, magnesium alloy, tin, or tin alloy.
11. A method of forming a uniform protective coating on a metal workpiece to be formed with a tool, comprising the steps of:
a) degreasing a metal workpiece to be formed with a tool;
b) water-rinsing the metal workpiece;
c) applying a waterborne composition according to claim 1 ; and
d) drying the composition on the workpiece.
12. The method of claim 11 wherein the waterborne composition further comprises a lubricating component comprising at least one selection from the group consisting of oils, soaps, metal soaps, waxes, and polytetrafluoroethylene, in an amount comprising 1-70 mass % of the sum of the water-soluble inorganic salt, smectite-type clay mineral, and lubricating component.
13. A method of forming a lubricant coating on a metal workpiece to be formed with a tool in the plastic working of metals comprising the steps of:
a) degreasing the metal workpiece
b) water-rinsing the metal workpiece
c) applying a waterborne composition according to claim 7 ; and
d) drying the composition on the workpiece.
14. The method of claim 13 wherein the metal is iron, steel, copper, copper alloy, aluminum, aluminum alloy, titanium, titanium alloy, magnesium, magnesium alloy, tin, or tin alloy.
15. A waterborne composition comprising:
a.) water;
b.) a water-soluble inorganic salt; and
c.) a smectite-type clay mineral being at least one selection from the group consisting of sauconite, beidellite, hectorite, nontronite, saponite, iron saponite, and stevensite, said clay minerals having a mean particle size of 20 to 500 nm;
wherein the mass ratio of water-soluble inorganic salt to smectite-type clay mineral is 1:1 to 1: 0.01.