Aluminum nitride arc discharge vessel having high total transmittance and method of making same
Aluminum nitride arc discharge vessels having a high total transmittance may be made by annealing the as-sintered AlN vessel in a nitrogen atmosphere, preferably at a temperature of at least about 1850° C. and for a time of at least about 50 hours. The annealing increases the total transmittance of the vessel to greater than 92% in the wavelength region from about 400 nm to about 700 nm. The annealed AlN discharge vessels are useful for lamp applications, such as metal halide lamps, and offer an improved durability and life over polycrystalline alumina (PCA).
1. A method of making an arc discharge vessel having a ceramic body, comprising: forming the ceramic body of a sintered aluminum nitride and annealing the ceramic body in a nitrogen atmosphere at a temperature of at least about 1850 degree C. for a time of at least 50 hours to increase the total transmittance of the ceramic body to greater than 92% in a wavelength range from about 400 nm to about 700 nm.
2. The method of claim 1 wherein the total transmittance is increased to at least about 95%.
3. The method of claim 1 wherein the total transmittance is increased to at least about 98%.
4. The method of claim 1 wherein the ceramic body of sintered aluminum nitride is formed with a calcia sintering aid.
5. The method of claim 4 wherein the amount of the calcia sintering aid in the aluminum nitride prior to forming the ceramic body is from about 0.2 percent to about 5 percent by weight.
6. The method of claim 1 wherein the ceramic body has a wall thickness of 0.3 mm to 0.8 mm.
7. A method of making an arc discharge vessel having a ceramic body, comprising: forming the ceramic body of a sintered aluminum nitride; and, annealing the ceramic body at a temperature of at least about 1850° C. for a time of at least about 50 hours in a nitrogen atmosphere.
8. The method of claim 7 wherein the ceramic body is annealed for at least about 60 hours.
9. The method of claim 7 wherein the ceramic body is annealed for at least about 100 hours.
10. The method of claim 7 where the ceramic body is annealed at a temperature of from about 1850° C. to about 1950° C.
11. The method of claim 10 wherein the ceramic body is annealed for at least about 60 hours.
12. The method of claim 10 wherein the ceramic body is annealed for at least about 100 hours.
13. The method of claim 7 wherein the ceramic body of sintered aluminum nitride is formed with a calcia sintering aid.
14. The method of claim 13 wherein the amount of the calcia sintering aid in the aluminum nitride prior to forming the ceramic body is from about 0.2 percent to about 5 percent by weight.
15. A method of making an arc discharge vessel having a ceramic body, comprising:
sintering an aluminum nitride powder containing a calcia sintering aid to form the ceramic body; and, annealing the ceramic body at a temperature of about 1850° C. for a time of at least about 60 hours in a nitrogen atmosphere.
16. The method of claim 15 wherein the ceramic body is annealed for at least about 100 hours.
17. The method of claim 15 wherein the amount of the calcia sintering aid in the aluminum nitride powder is from about 0.2 percent to about 5 percent by weight.