Flame retardant and an epoxy resin composition comprising the same for encapsulating semiconductor devices
A flame retardant featuring: an inorganic porous fine particle, a phosphazene compound represented by the following average compositional formula (1) (X is a single bond, CH 2 , C(CH 3 ) 2 , SO 2 , S, 0, or O(CO)O; n is an integer of from 3 to 1000; d and e are numbers with 2d+e=2n), and a resin layer. The phosphazene compound is supported on the inorganic porous fine particle, and the resin layer coats the inorganic porous fine particle with the phosphazene compound supported thereon. The resin layer thermally decomposes to lose weight by 10% at a temperature of from 300° C. to 500° C., as measured by thermogravimetry in the air at a heating rate of 10° C./min.
1. A flame retardant comprising
an inorganic porous fine particle selected from the group consisting of silicon dioxide, calcium silicate, apatite, alumina, and zeolite, each having a mean particle size of from 0.5 to 20 μm and a specific surface area of from 100 to 600 m 2 /g,
a phosphazene compound represented by the following average compositional formula (1)
wherein X is selected from the group consisting of a single bond, CH 2 , C(CH 3 ) 2 , SO 2 , S, O, and O(CO)O, n is an integer of from 3 to 1000, d and e are numbers with 2d+e=2n,
said phosphazene compound being supported on said inorganic porous fine particle, and
a resin layer coating said inorganic porous fine particle with the phosphazene compound supported thereon, said resin thermally decomposing to lose weight by 10% at a temperature of from 300° C. to 500° C. as measured by thermogravimetry in the air at a heating rate of 10° C./min.
2. The flame retardant according to claim 1 , wherein said resin layer comprises an epoxy resin or a bismaleimide resin.
3. The flame retardant according to claim 1 , wherein said phosphazene compound is contained in an amount of from 10 to 60 weight % in the flame retardant.
4. An epoxy resin composition for encapsulating semiconductor devices, said composition comprising
(A) a flame retardant according to any one of claims 1 , 2 , or 3 ,
(B) an epoxy resin,
(C) a curing agent, and
(D) an inorganic filler,
wherein said flame retardant (A) is contained in an amount of from 5 to 50 parts by weight per total 100 parts by weight of the epoxy resin (B) and the hardener (C), and said composition comprises neither brominated compounds nor antimony compounds.
5. A semiconductor device encapsulated with a cured product of an epoxy resin composition comprising
(A) a flame retardant according to any one of claims 1 , 2 , or 3 ,
(B) an epoxy resin,
(C) a curing agent, and
(D) an inorganic filler,
wherein said flame retardant (A) is contained in an amount of from 5 to 50 parts by weight per total 100 parts by weight of the epoxy resin (B) and the hardener (C), and said composition comprises neither brominated compounds nor antimony compounds.