Topsheet for absorbent article
A topsheet for absorbent articles is disclosed. The topsheet is used on the side of an absorbent article to be brought into contact with a wearer's body. The topsheet has an air permeability of 10 ml/cm 2 ·sec or more in the horizontal direction under a pressure of 10 cN/cm 2 . The topsheet also has an air permeability of 10 to 500 ml/cm 2 ·sec in the horizontal direction under a pressure of 50 cN/cm 2 .
1. A topsheet for absorbent articles used on the side of an absorbent article to be brought into contact with a wearer's body, which has an air permeability of 100 to 500 ml/cm 2 ·sec or more in the horizontal direction under a pressure of 10 cN/cm 2 , with a ratio of the air permeability under 10 cN/cm 2 in the machine direction to that in the cross direction being 0.6 to 1.7, and which has a first fiber layer and a second fiber layer both comprising a fiber aggregate, said second fiber layer comprising thermally shrinkable fiber, said first fiber layer and said second fiber layer being partially thermally fusion-bonded together to form fusion-bonded joints in a prescribed pattern and a large number of the fusion-bonded joints are almost equally spaced in a regular configuration with the fusion-bonded joints having a thickness t of 0.1 to 0.5 mm,
said first fiber layer forming protrusions in portions other than said fusion-bonded joints by the heat shrinkage of said thermally shrinkable fiber of said second fiber layer wherein each protrusion is dome-shaped and filled with the fibers making the first fiber layer, the portions of said protrusions adjoining said fusion-bonded joints being denser and stiffer than other portions of said protrusions, and the first fiber layer bulging upward in areas that are surrounded by fusion-bonded joints to form a great number of the protrusions,
said second fiber layer being substantially flat in portions other than said fusion-bonded joints, and
wherein a ratio of the substantial thickness T′ of the protrusions to the thickness t of the fusion-bonded joints (T′/t) is 5 to 50.
2. The topsheet for absorbent articles according to claim 1 , which has an air permeability of 10 to 500 ml/cm 2 ·sec in the horizontal direction under a pressure of 50 cN/cm 2 .
3. The topsheet for absorbent articles according to claim 2 , which has an air permeability of 20 to 200 ml/cm 2 ·sec in the horizontal direction under a pressure of 50 cN/cm 2 .
4. The topsheet for absorbent articles according to claim 1 , which has a great number of protrusions discontinuous in the longitudinal and width directions on the side facing a wearer's body, the topsheet under a pressure of 0.5 cN/cm 2 having a thickness of 0.5 to 10 mm, and the shortest distance between adjacent protrusions being 0.5 to 15 mm.
5. The topsheet for absorbent articles according to claim 1 , wherein the number of fusion-bonded joints after thermal shrinkage is 1 to 30 per cm 2 of the topsheet.
6. A topsheet for absorbent articles used on the side of an absorbent article to be brought into contact with a wearer's body, which has a first fiber layer and a second fiber layer both comprising a fiber aggregate, said second fiber layer comprising thermally shrinkable fiber, said first fiber layer and said second fiber layer being partially thermally fusion-bonded together to form fusion-bonded joints in a prescribed pattern, said first fiber layer forming protrusions in portions other than said fusion-bonded joints by the heat shrinkage of said thermally shrinkable fiber of said second fiber layer, said second fiber layer being substantially flat in portions other than said fusion-bonded joints, and the ratio of the substantial thickness T′ of said protrusions to the thickness t of said fusion-bonded joints (T′/t) is 5 to 50,
wherein said protrusions are discontinuous in the MD and CD and each protrusion possesses a MD length/CD length ratio of about 1/2 to 2/1 and the shortest distance between adjacent protrusions is 0.5 to 15 mm,
wherein the topsheet possesses an air permeability of 100 to 500 ml/cm 2 ·sec or more in the horizontal direction under a pressure of 10 cN/cm 2 with a ratio of the air permeability under 10 cN/cm 2 in the MD to that in the CD being 0.6 to 1.7, and
wherein the topsheet under a pressure of 0.5 cN/cm 2 has a thickness of 0.5 to 10 mm.
7. The topsheet for absorbent articles according to claim 6 , wherein the number of fusion-bonded joints after thermal shrinkage is 1 to 30 per cm 2 of the topsheet.