Method of removing resist, semiconductor device thereby and method of manufacturing a semiconductor device
Disclosed is a method of removing resist preventing increase of dielectric constant of low permittivity insulating films and preventing remains of resist. Using a resist mask, a protection insulating film, a MSQ film, and a silicon oxide film composing an ILD are RIE dry etched sequentially, and a via is formed on the surface of a substrate for processing reaching the diffusion layer on the substrate for processing. Subsequent process consists of; removing a modified layer formed on the substrate for processing surface because of prior etching using plasma gas by plasma excitation of NH 3 gas, and another etching for complete removal of the resist mask by irradiation of hydrogen active species created by hydrogen gas and inert gas, of which example is helium gas or argon gas.
1. A method of removing a resist used as a mask for patterning a substrate for processing, said method comprising the steps of:
Removing, by etching, the surface of said resist with a reactive species created by plasma excitation of a first processing gas including NH 3 , said surface being modified during said patterning; and
subsequently removing all remaining resist by etching with a hydrogen active species created by plasma excitation of a second processing gas, said processing gas including a hydrogen gas.
2. The method of claim 1 wherein said hydrogen species are a plurality of hydrogen radicals.
3. The method of claim 1 wherein said second processing gas is a mixture of hydrogen gas and an inert gas
4. The method of claim 1 , wherein said substrate for processing is placed in a temperature set in a range of 200° C. to 400° C. for etching by use of said hydrogen active species.
5. The method of claim 1 , wherein the first processing gas also includes at least one of a nitrogen gas, an oxygen gas, a carbon tetrafluoride (CF 4 ) gas, a hydrogen gas and a mixture of these gases onto said surface.
6. The method of claim 1 , wherein the surface of said resist, modified due to said patterning, is removed by immersion of said substrate for processing in a chemical liquid including an organic solution.
7. The method of claim 1 , wherein the surface of said resist is modified due to an etching process of a low dielectric constant insulating film, said dielectric constant is three (3) or less, said low dielectric constant insulating film being formed on the surface of said substrate for processing.
8. The method of claim 1 , wherein the surface of said resist is modified due to an etching process of a metal film on said low dielectric constant insulating film of which dielectric constant is three (3) or less, said low dielectric constant insulating film being formed on the surface of said substrate for processing.
9. A method of manufacturing a semiconductor device comprising the steps of:
forming an insulating film of low dielectric constant on a surface of a substrate for processing;
forming a resist on a surface of said low dielectric constant insulating film;
forming a pattern on said resist by lithography;
forming the pattern by etching said low dielectric constant film by use of the pattern of said resist;
removing a surface part formed on the surface of said resist with a reactive species created by plasma excitation of a first processing gas including NH 3 ; and
subsequently removing all remaining resist by etching with a hydrogen active species created by plasma excitation of a second processing gas including a hydrogen gas.
10. The method of claim 9 wherein said hydrogen active species are a plurality of hydrogen radicals.
11. The method of claim 9 wherein said second processing gas is a mixture of a hydrogen gas and an inert gas.
12. The method of claim 9 wherein said substrate for processing is placed in a temperature being set in a range of 200° C. to 400° C. for etching by use of said hydrogen active species.
13. The method of claim 9 wherein the first processing gas also includes at least one of a nitrogen gas, an oxygen gas, a carbon tetrafluoride (CF 4 ) gas, a hydrogen gas, and a mixture of said gas onto said surface.
14. The method of claim 9 wherein the surface of said resist, said surface being modified by said patterning, is removed by immersion of said substrate for processing in a chemical liquid including an organic solution.
15. The method of claim 9 wherein the surface of said resist is modified because of etching process of a low dielectric constant insulating film of which dielectric constant is three (3) or less, said low dielectric constant insulating film being formed on the surface of said substrate for processing.
16. The method of claim 9 wherein, the surface of said resist is modified because of etching process of a metal film formed on a low dielectric constant insulating film which dielectric constant is three (3) or less, said low dielectric constant insulating film being formed on the surface of said substrate for processing.
17. A semiconductor device manufactured by a method comprising the steps of:
patterning a substrate for processing, on which a low dielectric constant layer is formed by use of a resist coated onto a surface of said substrate for processing;
removing, by etching, a surface of said resist with an active species created by plasma excitation of a first processing gas including NH 3 , the surface being modified by said patterning; and
subsequently removing all remaining resist by etching with a hydrogen active species created by plasma excitation of a second processing gas including a hydrogen gas;
wherein said low dielectric constant insulating film is an inter layer dielectric (ILD) of a multilayer interconnect wiring structure for interconnection of a plurality of semiconductor elements.
18. The semiconductor device of claim 17 , wherein said inter layer dielectric(ILD) is an inter layer dielectric(ILD) of at least one of a damascene and a dual damascene wiring structure configured to interconnect the plurality of semiconductor elements.