High temperature piezo buzzer
A piezoelectric buzzer includes a vibrating layer capable of withstanding temperatures in excess of 260° C. for at least five minutes while still maintaining its ability to vibrate and produce a buzzing sound at a level of at least 80 dB, and a high temperature piezoelectric material having a Curie temperature in excess of 260° C. and one or more of the following properties: a planar coupling coefficient (k p ) of at least about 0.5; a longitudinal coupling coefficient (k 33 ) of at least about 1500; and a mechanical quality factor (Q m ) of at least about 2000. The piezo material may have a combination of these properties such that the product (k p 2 )(k 33 )(Q m ) is at least about 1.5×10 6 . The piezoelectric material may have a base formula of Pb x Sr (1-x) (Mn 1/3 Sb 2/3 ) (1-y) (Zr z Ti 1-z ) y O 3 with x ranging from 0.95 to 0.99, y ranging from 0.92 to 0.97, and z ranging from 0.45 to 0.55, and may further include dopants in the amounts of about 0.4% CeO 2 , about 1% CuO, and about 4% Nb 2 O 5 .
1. A piezoelectric buzzer effective for use in a personal assist safety system (PASS), comprising:
a) a vibration layer;
b) a piezoelectric material at least partially overlaying said vibration layer in a manner effective for causing said vibration layer to vibrate to emit a buzzing sound when an electric current is applied to the piezoelectric material; and
c) electric contacts effective for connecting the piezoelectric layer to an electric power source;
wherein said piezoelectric material is a material having a base formula of:
Pb x Sr (1-x) (Mn 1/3 Sb 2/3 ) (1-y) (Zr Z Ti 1-z ) y O 3
wherein x may range from 0.95 to 0.99;
wherein y may range from 0.92 to 0.97; and
wherein z may range from 0.45 to 0.55
wherein said piezoelectric material includes one or more dopants added by incorporating into the pre-fired composition one or more dopant precursor materials selected from the group consisting of: CeO 2 , CuO, and Nb 2 O 5 .
2. A piezoelectric buzzer according to claim 1 wherein the dopant precursor materials are preferably added to the ceramic composition in individual amounts ranging from 0.01 wt % to up to 5.0 wt %.
3. A piezoelectric buzzer according to claim 1 wherein the piezoelectric material is a PZT ceramic made from the following relative amounts of starting materials:
PbO 0.96 SrO 0.0194 MnO 0.016 SbO 0.032 ZrO 0.466 TiO 0.456 NbO 0.038 CuO 0.010 CeO 0.004 .
4. A piezoelectric buzzer according to claim 1 wherein said vibration layer is made of a material capable of withstanding temperatures in excess of 260° C. for at least five minutes while still maintaining its ability to vibrate and produce a buzzing sound at a level of at least 95 dB (measured at 10 feet from the source; re 20 μPa) when used in a PASS unit.
5. A piezoelectric buzzer according to claim 1 wherein the vibrating material is an iron-nickel-cobalt alloy with a coefficient of linear thermal expansion of 5.15×10 −6 /° C under 260° C.
6. A piezoelectric buzzer according to claim 1 wherein the vibrating material is an iron-nickel alloy with a coefficient of linear thermal expansion of between about 1.5×10 −6 /° C and 2.0×10 −6 /° C. under 260° C.
7. A piezoelectric buzzer according to claim 1 wherein the vibrating material is an austenitic nickel-based superalloy having a coefficient of linear thermal expansion of about 7×10 −6 /° C. under 260° C.
8. A piezoelectric buzzer according to claim 1 wherein the vibrating material is a molybdenum-based material having a coefficient of linear thermal expansion of about 5.5×10 −6 /° C. under 260° C.
9. A piezoelectric buzzer according to claim 1 wherein the vibrating material is a high temperature plastic.
10. A piezoelectric buzzer according to claim 1 wherein the vibrating material is a fiber reinforced plastic.
11. A piezoelectric buzzer according to claim 1 wherein the buzzer includes at least two layers of piezoelectric material.
12. A piezoelectric buzzer according to claim 1 wherein said vibration layer is made of a material capable of withstanding temperatures in excess of 260° C. for at least five minutes while still maintaining its ability to vibrate and produce a buzzing sound at a level of at least 80 dB (measured at 10 feet from the source; re 20 μPa) when used in a PASS unit.
13. A piezoelectric buzzer according to claim 12 wherein the piezoelectric material is a PZT ceramic made from the following relative amounts of starting materials:
PbO 0.96 SrO 0.0194 MnO 0.016 SbO 0.032 ZrO 0.466 TiO 0.456 NbO 0.038 CuO 0.010 CeO 0.004 .