Nonwoven composites and related products and methods
A filtering catalytic substrate including a non-woven fibrous refractory body, a plurality of channels formed in the body, a washcoat layer at least partially coating the channels, and a catalyst material at least partially coating the washcoat. The body is substantially composed of interlocking fibers fabricated using methods of forming a rigid matrix of ceramic fibers to provide a porous substrate for filtration applications.
1. A process for preparing a catalytic filtering substrate, comprising:
mixing a plurality of ceramic fibers of at least one predetermined length with a liquid;
blending the fibers into a flowable mixture;
forming the flowable mixture into a body;
forming a plurality of honeycomb channels in the body;
drying the body; and
firing the body to provide a fired body;
wherein the fired body comprises bonded ceramic fibers forming a rigid non-woven matrix having a porosity of at least 60%.
2. The process of claim 1 wherein the fired body is used in a diesel engine.
3. The process of claim 1 wherein the fired body is used in a gasoline engine.
4. The process of claim 1 wherein the ceramic fibers comprise alumina and silica.
5. The process of claim 1 wherein the fired body further comprises from about 5% to about 50% of alumina.
6. The process of claim 1 wherein the fired body further comprises from about 50% to about 90% of silica.
7. The process of claim 1 wherein the ceramic fibers comprise amorphous aluminosilicate fiber.
8. The process of claim 1 wherein the step of firing the body to provide a fired body comprises sintering the ceramic fibers.
9. The process of claim 1 wherein the ceramic fibers comprise at least a plurality of material compositions.
10. The process of claim 1 further comprising adapting the fired body into a wall-flow configuration.
11. The process of claim 1 further comprising coating the fired body with a catalyst.
12. The process of claim 11 wherein the catalyst is selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof.
13. The process of claim 11 wherein the catalyst is present in an amount of between about 1 g/ft3 to about 50 g/ft3.
14. The process of claim 11 wherein the catalyst is at least partially coating the channels.