Hyperbranched polymer modified biopolymers, their biobased materials and process for the preparation thereof
View Patent ↗Compositions of biodegradable polymers and hyperbranched dendritic polymer (HBP) are described. The compositions can also include anhydride modified HBP. The resulting compositions have superior elongation at break and can be as cast or blown films for packaging, for example.
1. A composition comprising an extrusion blended mixture of:
(a) a thermoplastic biodegradable polyester polymer of a lactic acid monomer;
(b) a hyperbranched dendritic polymer comprising a hydroxyl functional group; and
(c) an anhydride;
wherein:
(i) the anhydride and the hyperbranched dendritic polymer form a reaction product as an anhydride modified hyperbranched dendritic polymer comprising an ester linkage between the anhydride and the hydroxyl group of the hyperbranched dendritic polymer; and
(ii) the anhydride modified hyperbranched dendritic polymer improves elongation at break of the biodegradable polyester polymer at least about 700% relative to the biodegradable polyester polymer alone.
2. The composition of claim 1 wherein the anhydride modified hyperbranched dendritic polymer is present in an amount between about 2 and 12% by weight of the composition.
3. The composition of claim 1 wherein the hyperbranched dendrite polymer is a hyperbranched polyester dendrite polymer.
4. The composition of claim 1 wherein the biodegradable polyester polymer further comprises a polyhydroxyalkanoate (PHA) selected from the group consisting of poly(hydroxybutyrate) (PHB), poly (hydroxybutyrate-co-valerate) (PHBV) and mixtures thereof.
5. The composition of claim 1 further comprising clay particles, talc particles and mixtures thereof.
6. The composition of claim 5 , wherein the anhydride modified hyperbranched dendritic polymer is a matrix modifier as well as dispersing agent for clay and talc particles.
7. The composition of claim 1 with en improved heat deflection temperature over the biodegradable polyester polymer alone.
8. The composition of claim 1 with an improved heat deflection temperature over the biodegradable polyester polymer alone and wherein the biodegradable polyester polymer further comprises a polyhydroxyalkanoate (PHA) selected from the group consisting of poly (hydroxybutyrate) (PHB), poly (hydroxybutyrate-co-valerate) (PHBV) mixtures thereof.
9. The composition of claim 8 further comprising nano-clay particles, clay particles or mixtures thereof.
10. The composition of claim 9 , wherein the anhydride modified hyperbranched dendritic polymer is a matrix modifier as well as compatibilizer for different biodegradable polyester polymers.
11. The composition of any one of claims 1 , 8 , or 9 as a cast or blown film.
12. A blend of neat polylactic acid with a modified polylactic acid according to the composition of claim 1 as a master batch, wherein the modified polylactic acid is present in the blend in an amount varying from 20 to 60 wt % and the blend optionally contains clay particles varying from 2 to 5 wt % and talc particles varying from 2 to 50 wt %.
13. A modified polylactic acid composition comprising an extrusion blended mixture of:
(a) a thermoplastic biodegradable polyester polymer comprising polylactic acid;
(b) an anhydride modified hyperbranched dendritic polymer in an amount ranging from about 2 wt. % to 12 wt. % of the composition, wherein the anhydride modified hyperbranched dendritic polymer comprises an ester reaction product between an anhydride and a hyperbranched dendritic polymer having hydroxyl functionality; and
(c) optionally, clay particles or talc particles to provide improved gas barrier properties.
14. The composition of claim 1 further comprising a natural fiber.
15. The composition of claim 14 , wherein the hyperbranched dendritic polymer or the anhydride modified hyperbranched dendritic polymer is matrix modifier as well as a compatibilizer for the natural fiber.
16. The composition of claim 1 wherein the biodegradable polyester polymer comprises a blend of polylactic acid and polyhydroxyalkanoate.
17. A process for preparing the composition of claim 1 which comprises reactively extruding the hyperbranched dendritic polymer with the biodegradable polyester polymer at an extruder barrel temperature below a decomposition temperature of the biodegradable polyester polymer.
18. A process for preparing the composition of claim 1 which comprises reactively extruding the hyperbranched dendritic polymer with the biodegradable polyester polymer at an extruder barrel temperature below the decomposition temperature of the biodegradable polyester polymer and wherein the extruder has single or duel rotating screws for blending.
19. The composition of claim 1 wherein the anhydride is a polyanhydride (PA) present between about 5-50% by weight with respect to the anhydride modified hyperbranched dendritic polymer.
20. The composition of claims 1 or 13 wherein the anhydride modified hyperbranched dendritic polymer is at least partially crosslinked.
21. The composition of claim 20 wherein the anhydride comprises a polymeric polyanhydride that forms crosslinks in the anhydride modified hyperbranched dendritic polymer.
22. The composition of claims 1 or 13 wherein the anhydride comprises a polymeric polyanhydride.
23. The composition of claim 13 wherein the hyperbranched dendritic polymer comprises a hyperbranched dendritic polyester polymer.
24. The composition of claim 13 further comprising a polyhydroxyalkanoate.
25. The composition of claim 24 wherein the polyhydroxyalkanoate is selected from the group consisting of poly(hydroxybutyrate) (PHB), poly(hydroxybutyrate-co-valerate) (PHBV), and mixtures thereof.